DOE OSTI2024

Chemo-Mechanical Instabilities in Lithium Cobalt Oxide at Higher State-Of-Charge in Li-Ion Batteries

Transition metal oxide cathodes are widely used in commercial Li-ion batteries. However, their practical charge capacity is limited due to severe chemo-mechanical instabilities at higher charge voltage, and state-of-charge condition. Here, in situ stress and strain measurements were synchronized to probe mechanical deformations in the lithium cobalt oxide (LCO) cathode via a multi-beam stress sensor and digital image correlation, respectively. In situ mechanical measurements revealed how Li removal from the electrode structure induces deformations on the LCO composite cathodes during cycling. The structure and morphology of the LCO cathodes were further investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM) studies. Two distinct electrochemical and mechanical behaviors were identified when the LCO was charged up to 4.65 V. The LCO undergoes a compressive stress generation when charged up to 4.2 V and surface fractures on the LCO particles were detected by SEM. LCO cathode experienced significantly large contractions (negative strains) when charged up to 4.65 V, where intergranular crack formation and phase transformation were detected on the LCO particles via SEM and XRD, respectively. Overall, the study bridges complicated structural deformations with in situ analysis of mechanical degradations in LCO cathodes charged at higher voltages. The correlation is vital to understanding instability mechanisms in transition metal oxides at high voltages for alkali metal ion batteries.

higher state-of-charge↗

DOE OSTI2023

The Linkage Between Electro-Chemical Mechanical Instabilities in Battery Materials

Battery chemistry must be diversified to achieve a sustainable energy landscape by effectively utilizing renewable energy sources. Alkali metal-ion, all-solid-state, metal–air batteries, and multivalent batteries offer unique cost, safety, raw material abundance, energy, and power density solutions. However, realizing these “beyond Li-ion batteries” must uncover their working principles and performance & property relationships. In this aspect, mitigating chemo-mechanical instabilities in the structure and surface of the electrodes plays a crucial role in their performance. Unfortunately, the coupling between electrochemical and mechanical interactions is often poorly understood due to a lack of operando characterization. Here, this review article explains the working principles of curvature measurement and digital image correlation for measuring stress and strain generations in battery materials. We provided specific examples of how these operando mechanical measurements shed light on instabilities in alkali metal ion electrodes, solid electrolytes, Li-O 2 batteries, and aqueous Zn-ion batteries. Operando mechanical measurements offer an effective way to map changes in the physical fingerprint of the battery materials, therefore providing crucial information to elucidate instabilities in battery materials.

25 ENERGY STORAGE↗

DOE OSTI2023

Probing the Formation of Cathode-Electrolyte Interphase on Lithium Iron Phosphate Cathodes via Operando Mechanical Measurements

Interfacial instabilities in electrodes control the performance and lifetime of Li-ion batteries. While the formation of solid-electrolyte interface (SEI) on anodes has received much attention, there is still lack of understanding about the formation of cathode-electrolyte interface (CEI) on the cathodes. To fill this gap, we report on dynamic deformations on lithium iron phosphate, LiFePO 4 cathodes during charge / discharge by utilizing in-operando digital image correlation, impedance spectroscopy and Cryo X-ray photoelectron spectroscopy. LiFePO4 cathodes were cycled in either LiPF 6 , LiClO 4 or LiTFSI- containing organic liquid electrolytes. Beyond the first cycle, Li-ion intercalation results in a nearly linear correlation between electrochemical strains and the state of (dis)-charge, regardless of the electrolyte chemistry. However, during the first charge in LiPF 6 - containing electrolyte, there is a distinct irreversible positive strain evolution at the onset of anodic current rise as well as current decay at around 4.0V. Impedance studies show the increase in surface resistance in the same potential window, suggesting the formation of CEI layers on the cathode. The chemistry of the CEI layer was characterized by X-ray photoelectron spectroscopy. LiF is detected in CEI layer starting as early as 3.4 V and Li $x$ PO $y$ F $z$ appeared at voltages higher than 4.0 V during the first charge. In conclusion, our approach offers new insights into the formation mechanism of CEI layers on the cathode electrodes, which is crucial for the development of robust cathode and electrolyte chemistries for higher performance batteries.

25 ENERGY STORAGE↗

DOE OSTI2023

The Role of Transition Metals on Chemo-Mechanical Instabilities in Prussian Blue Analogues For K-Ion Batteries: The Case Study on KNHCF Versus KMHCF

Prussian blue analogues (PBAs) cathodes can host diverse monovalent and multivalent metal ions due to their tunable structure. However, their electrochemical performance suffers from poor cycle life associated with chemo-mechanical instabilities. This study investigates the driving forces behind chemo-mechanical instabilities in Ni- and Mn-based PBAs cathodes for K-ion batteries by combining electrochemical analysis, digital image correlation, and spectroscopy techniques. Capacity retention in Ni-based PBA is 96% whereas it is 91.5% for Mn-based PBA after 100 cycles at C/5 rate. During charge, the potassium nickel hexacyanoferrate (KNHCF) electrode experiences a positive strain generation whereas the potassium manganese hexacyanoferrate (KMHCF) electrode undergoes initially positive strain generation followed by a reduction in strains at a higher state of charge. Overall, both cathodes undergo similar reversible electrochemical strains in each charge–discharge cycle. There is ~0.80% irreversible strain generation in both cathodes after 5 cycles. XPS studies indicated richer organic layer compounds in the cathode-electrolyte interface (CEI) layer formed on KMHCF cathodes compared to the KNHCF ones. Faster capacity fades in Mn-based PBA, compared to Ni-based ones, is attributed to the formation of richer organic compounds in CEI layers, rather than mechanical deformations. In conclusion, understanding the driving forces behind instabilities provides a guideline to develop material-based strategies for better electrochemical performance.

25 ENERGY STORAGE↗

DOE OSTI2021

In Situ Probing Potassium-ion Intercalation-induced Amorphization in Crystalline Iron Phosphate Cathode Materials

Na-ion and K-ion batteries are promising alternatives for large-scale energy storage applications due to their abundance and low cost. Intercalation of these large ions could cause irreversible structural deformation and partial to complete amorphization in the crystalline electrodes. The designing of new amorphous electrodes is another route to develop electrodes to store these ions reversibly. Lack of understanding of dynamic changes in the amorphous nanostructures during battery operation is the bottleneck for further developments. Here, we report the utilization of in situ digital image correlation and in-operando X-ray diffraction (XRD) techniques to probe dynamic changes in the amorphous phase of iron phosphate during potassium intercalation. In-operando XRD demonstrates amorphization in the electrode’s nanostructure during the first charge/discharge cycle. Additionally, the ex-situ high-resolution transmission electron microscopy further confirms the amorphization after potassium insertion. In situ strain analysis detects the reversible deformation associated with redox reactions in the amorphous phases. Our approach offers new insights on the mechanisms of ion intercalation in the amorphous nanostructures which are highly potent for development of next-generation batteries.

Ozdogru, Bertan↗