NASA NTRS1988

Supercooling effects in faceted eutectic Nb-Si alloys

The effect of melt supercooling on the microstructure of an Nb-58 at. pct Si alloy is investigated experimentally using an electromagnetic levitation apparatus. It is found that, starting with an alloy nominally of eutectic composition, nucleation of Nb5Si3 occurs in the supercooled liquid first. Upon further cooling, the remaining liquid continues to supercool until the second phase, NbSi2 is nucleated, which is commonly accompanied by rapid recalescence. The primary phase exibits a eutectoid-type decomposition. The observations are discussed with reference to the results of quantitative microstructural measurements, compositional and thermal analysis, and preliminary thermodynamic modeling of the phase diagram.

Gokhale, A. B.↗

NASA NTRS1988

Rapid solidification of Nb-base alloys

New Nb-base alloys are of interest for aerospace structural applications at high temperatures, viz, 800 to 1650 C. Fundamental information regarding the effects of rapid solidification in achieving greatly refined microstructures, extended solid solubility, suppression of embrittling equilibrium phases, and formation of new phases is desired in a number of Nb-X alloys. The microstructures and selected properties of Nb-Si and other Nb-base alloys are presented for materials both rapidly quenched from the equilibrium liquidus and rapidly solidified following deep supercooling. Electromagnetic levitation was used to achieve melting and supercooling in a containerless inert gas environment. A variety of solidification conditions were employed including splatting or drop casting of supercooled samples. The morphology and composition of phases formed are discussed in terms of both solidification history and bulk composition.

Gokhale, A. B.↗

NASA NTRS1984

Technique for the efficient and reproducible fabrication of electromagnetic levitation coils

A technique has been developed for fabricating electromagnetic induction coils in a reproducible manner. The process utilizes a split mandrel that can be disassembled to remove the mandrel from the coil. The technique has increased coil production rates by a factor of 8 over the freehand winding method. The success rate for producing a functional levitation coil has been increased from 50 percent to 95 percent. The levitation coil designed during this work has successfully levitated and melted a variety of alloys including Cu, Ag, Ag-Ni, Cu-Fe, Fe-C, and Nb-Ge. W was also levitated but not melted at temperatures as high as 2700 C. The highest sample melt temperature achieved was 2400 C for the Nb-Ge samples.

Ethridge, E. C.↗

NASA NTRS1983

Electromagnetic levitation coil fabrication technique for MSFC containerless processing facilities

A technique is described for more reproducible fabrication of electromagnetic levitation coils. A split mandrel was developed upon which the coil is wound. After fabrication the mandrel can be disassembled to remove it from the coil. Previously, a full day was required to fabricate a levitation coil and the success rate for a functional coil was only 50 percent. About eight coils may be completed in one day using the technique developed and 95 percent of them are good levitation coils.

Ethridge, E. C.↗

NASA NTRS1983

Containerless electromagnetic levitation melting of Cu-Fe and Ag-Ni alloys

The feasibility of producing silver or copper alloys containing finely dispersed nickel or iron particles, respectively, by utilizing containerless electromagnetic levitation casting techniques was investigated. A levitation coil was designed to successfully levitate and melt a variety of alloys including Nb-Ge, Cu-Fe, Fe-C, and Ag-Ni. Samples of 70 Cu-30 Fe and 80 Ag-20 Ni (atomic %), prepared by mechanical pressing of the constituent powders, were levitated and heated either to the solid plus liquid range of the alloys or to the fully liquid region. The samples were then solidified by passing helium gas into the bell jar or they were dropped into a quenching oil. The structure of the samples which were heated to the solid plus liquid range consists of uniform distribution of Fe or Ni particle in their respective matrices. A considerable amount of entrapped gas bubbles were contained. Upon heating for longer periods or to higher temperatures, the bubbles coalesced and burst, causing the samples to become fragmented and usually fall out of the coil.

Abbaschian, G. J.↗

NASA NTRS1983

Supercooling and structure of levitation melted Fe-Ni alloys

A study has been made of the effect of supercooling, quenching rate, growth inhibitors, and grain refiners on the structure of levitation-melted Fe- 25 pct Ni alloys. A combination of three morphologies, dendritic, spherical, and mixed dendritic and spherical, is observed in samples superheated or supercooled by less than 175 K. At larger supercooling, however, only the spherical morphology is observed. The grain size and the grain boundary shape are found to be strongly dependent on the subgrain morphology but not on the quenching temperature. Considerable grain growth is evident in samples with spherical and mixed morphologies but not in the dendriitic samples. The average cooling rates during solidification and the heat transfer coefficients at the metal-quenching medium boundary are calculated. For samples solidified in water, molten lead, and ceramic molds, the heat transfer coefficients are 0.41, 0.52, and 0.15 w/sq cm, respectively.

Abbaschian, G. J.↗