Engineering topics
Publications and source records attributed to Abraham, Daniel.
This invention relates to an electrolyte composition for a lithium ion battery comprising a lithium salt in a non-aqueous solvent containing an additive comprising a compound of formula R 3 SiOP(O) n F 2 ; wherein each R independently is a hydrocarbyl group; and n is 0 or 1; and wherein the additive is substantially free from (R 3 SiO) 3 P(O) n and (R 3 SiO) 2 P(O) n F. Electrochemical cells and batteries also are described.
In our initial study on the high-voltage 5 V cobalt-free spinel LiNi 0.5 Mn 1.5 O 4 (LNMO) cathode, we discovered a severe delamination issue in the laminates when cycled at a high upper cut-off voltage (UCV) of 4.95 V, especially when a large cell format was used. This delamination problem prompted us to investigate further by studying the transition metal (TM) dissolution mechanism of cobalt-free LNMO cathodes, and as a comparison, some cobalt-containing lithium nickel manganese cobalt oxides (NMC) cathodes, as the leachates from the soaking experiment might be the culprit for the delamination. Unlike other previous reports, we are interested in the intrinsic stability of the cathode in the presence of a baseline Gen2 electrolyte consisting of 1.2 M of LiPF 6 in ethylene carbonate/ethyl methyl carbonate (EC/EMC), similar to a storage condition. The electrode laminates (transition metal oxides, transition metal oxides, TMOs, coated on an Al current collector with a loading level of around 2.5 mAh/cm 2 ) or the TMO powders (pure commercial quality spinel LNMO, NMC, etc.) were stored in the baseline solution, and the transition metal dissolution was studied through nuclear magnetic resonance, such as 1 H NMR, 19 F NMR, scanning electron microscope (SEM), X-ray photoelectron spectroscopy (XPS) and inductively coupled plasma mass spectrometry (ICP-MS). Significant electrolyte decomposition was observed and could be the cause that leads to the TM dissolution of LNMO. To address this TM dissolution, additives were introduced into the baseline electrolyte, effectively alleviating the issue of TM dissolution. The results suggest that the observed delamination is caused by electrolyte decompositions that lead to etching, and additives such as lithium difluorooxalato borate and p-toluenesulfonyl isocyanate can alleviate this issue by forming a firm cathode electrolyte interface. This study provides a new perspective on cell degradation induced by electrode/electrolyte interactions under storage conditions.
Lithium tetrafluoro(malonato)phosphate compounds are useful as additives in lithium ion battery applications. The compounds are represented by Formula (I): MPF 4 [—O(C═O)—(CX′X″)—(C═O)O—]; wherein M is Li or Na; each X′ and X″ independently is selected from the group consisting of H, alkyl, fluoro-substituted alkyl, and F; or wherein the X′ and X″ together are —CR 2 —(CR′ 2 ) m —CR″ 2 —; each R, R′ and R″ independently is selected from the group consisting of H methyl, trifluoromethyl, and F; and in is 0 or 1. These compounds can be prepared in high purity and a high yield by reaction of a metal hexafluorophosphate with a bis-silyl malonate compound. A similar oxalato compound, lithium tetrafluoro(oxalato)phosphate), can be made in the same manner, but using a bis-silyl oxalate in place of the bis-silyl malonate. Advantageously, the compounds can be formed, in situ, in a LiPF 6 -containing electrolyte solution.