Engineering topics
Publications and source records attributed to Adeyemi, Adedoyin N..
Transition metal silicon arsenide with Ir–Si and Ir–As covalent bonding exhibits remarkable non-linear optical properties: high second harmonic generation activity and a large laser damage threshold.
Here, the intermetallic compound LiMnBi was synthesized by the two-step solid-state reaction from the elements. The synthesis temperature of 850 K was selected based on in-situ high-temperature powder X-ray diffraction data. LiMnBi crystalizes in the layered-like PbClF structure type (a = 4.3131(7) Å, c = 7.096(1) Å at 100 K, P4/nmm space group, Z = 2). LiMnBi structure is built of the alternating [MnBi] and Li layers, as determined from single-crystal X-ray diffraction data. Magnetic properties measurements and solid-state 7 Li Nuclear Magnetic Resonance data collected for polycrystalline LiMnBi samples indicate the long-range antiferromagnetic ordering of Mn sublattice at ~340 K, with no superconductivity down to 5 K detected. LiMnBi is air- and water-sensitive. In aerobic conditions, Li can be extracted from LiMnBi structure to form Li 2 O/LiOH and MnBi (NiAs structure type, P6 3 /mmc). The obtained MnBi polymorph was previously reported to be one of the strongest rare-earth-free ferromagnets, yet its bulk synthesis in powder form is cumbersome. The proposed magneto-structural transformation from ternary LiMnBi to ferromagnetic MnBi involves condensation of the MnBi4 tetrahedra upon Li deintercalation and is exclusive to LiMnBi. In contrast, ferromagnetic MnBi cannot be obtained from either isostructural NaMnBi and KMnBi, or from the structurally related CaMn 2 Bi 2 . Such a distinctive transformation in the case of LiMnBi is presumed to be due to its fitting reactivity to yield MnBi and favorable interlayer distance between [MnBi] layers, while the interlayer distance in NaMnBi and KMnBi structural analogs is unfavorably long. The studies of delithiation from the layered-like LiMnBi under different chemical environments indicate that the yield of the MnBi depends on the type of solvent used and the kinetics of the reaction. A slow rate and mild reaction media lead to a high fraction of the MnBi product. The saturation magnetization of the “as-prepared” MnBi is ~50 % of the expected value of 81.3 emu/g. Overall, this study adds a missing member to the family of ternary pnictides and illustrates how soft-chemistry methods can be used to obtain “difficult-to-synthesize” compounds.
The synthesis, formation mechanism, crystal structure, and transport properties of the bismuth chalcohalide Bi 13 S 17 Br 3 are reported.
SrTiO 3 and aluminum-doped SrTiO 3 are synthesized by calcination of metal salts dissolved in a deep eutectic solvent (DES) without any post-synthesis treatment.
The intergrowth of stable and metastable AgInS2 polymorphs was synthesized using a microwave-assisted synthesis. The samples were synthesized in water and in a deep eutectic solvent (DES) consisting of choline chloride and thiourea. An increase in the metal precursor concentration improved the crystallinity of the synthesized samples and affected the particle size. AgInS2 cannot be synthesized from crystalline binary Ag2S or In2S3 via this route. The solution synthesis reported here results in the intergrowth of the thermodynamically stable polymorph (space group I4¯2d, chalcopyrite structure) and the high-temperature polymorph (space group Pna21, wurtzite-like structure) that is metastable at room temperature. A scanning transmission microscopy (STEM) study revealed the intergrowth of tetragonal and orthorhombic polymorphs in a single particle and unambiguously established that the long-thought hexagonal wurtzite polymorph has pseudo-hexagonal symmetry and is best described with the orthorhombic unit cell. The solution-synthesized AgInS2 polymorphs intergrowth has slightly lower bandgap values in the range of 1.73 eV–1.91 eV compared to the previously reported values for tetragonal I4¯2d (1.86 eV) and orthorhombic Pna21 (1.98 eV) polymorphs.
A precipitation method involving a deep eutectic solvent (DES)–a mixture of hydrogen bond donor and acceptor–is used to synthesize a ternary metal oxide. Without toxic reagents, precipitates consisting of Zn 3 (OH) 2 V 2 O 7 ·nH 2 O and Zn 5 (OH) 6 (CO 3 ) 2 are obtained by simply introducing deionized H 2 O to the DES solution containing dissolved ZnO and V 2 O 5 . Manipulation of the synthetic conditions demonstrates high tunability in the size/morphology of the two-dimensional nanosheets precipitated during the dynamic equilibrium process. According to differential scanning calorimetry and high-temperature powder X-ray diffraction, Zn 3 V 2 O 8 and ZnO obtained by the annealing of the precipitate are intermediates in the reaction pathway toward metastable Zn 4 V 2 O 9 . Intimate mixing of the metal precursors achieved by the precipitation method allows access to the metastable zinc-rich vanadate with unusually rapid heat treatment. Furthermore, the UV–vis and surface photovoltage spectra reveal the presence of sub-band gap states, stemming from the reduced vanadium (V 4+ ) center. Photoelectrochemical measurements confirm weak photoanodic currents for water and methanol oxidation. For the first time, this work shows the synthesis of a metastable oxide with the DES-precipitation route and provides insight into the structure–property relationship of the zinc-rich vanadate.
Two new ternary tetrel pnictide phases, Li 1.08 Ge 4.92 As 7 and Cs 0.11 Zn 0.05 Si 0.95 As, have been synthesized. Both compounds crystallize in new structure types, which demonstrate the flexibility of Ge(Si)–As layers when accommodating electropositive cations of various sizes. Li 1.08 Ge 4.92 As 7 displays a Ge-As layer motif that has not been observed in ternary Ge-As systems, while Cs 0.11 Zn 0.05 Si 0.95 As exhibits a 3D framework composed of fragments of the 2D parent-phase SiAs. For Li 1.08 Ge 4.92 As 7 , a combination of computational modeling and solid-state 7 Li MAS NMR was used to establish the correct crystal structure with one mixed occupied Ge/Li site. The compositions of the phases were confirmed through energy-dispersive X-ray spectroscopy. Transport properties and UV–Vis spectroscopy reveal both reported compounds to be semiconductors. Cs 0.11 Zn 0.05 Si 0.95 As shows high thermal stability with congruent melting at 1300 K and an exceptionally low thermal conductivity of 0.5 W m –1 K –1 at 300 K. Temperature-dependent Li-ion hopping dynamics in Li 1.08 Ge 4.92 As 7 was characterized using 7 Li solid-state NMR.
Complex polymorphic relationships in the Ln SiP 3 ( Ln = La and Ce) family of compounds are reported.
Explore the source record for details and available documents.