Evaporated CdSe for Efficient Polycrystalline CdSeTe Thin-Film Solar Cells

Recent progress has shown that alloying cadmium telluride (CdTe) with cadmium selenide (CdSe) to create a CdSexTe1-x (CdSeTe) gradient region can significantly boost the performance of polycrystalline CdSeTe thin-film solar cells. However, improper CdSeTe alloying might introduce problematic band alignment and deleterious voids at the front interface, limiting the benefit maximization of this technique. Here, we show that the CdSe layers deposited by thermal evaporation result in CdSeTe cells with a higher performance than the sputtered CdSe. This is because evaporated CdSe can avoid the formation of voids at the front interface, producing improved front junction quality with suppressed front junction nonradiative recombination. The champion cell using evaporated CdSe demonstrated a power conversion efficiency (PCE) of 19.7%, much higher than 18.1% in the cell using sputtered CdSe.

cadmium selenide↗

DOE OSTI2024

Four–Terminal Perovskite–CdSeTe Tandem Solar Cells: From 25% toward 30% Power Conversion Efficiency and Beyond

Thin-film tandem photovoltaic (PV) technology has emerged as a promising avenue to enhance power conversion efficiency beyond the radiative efficiency limit of single-junction devices. Combining a tunable wide-bandgap perovskite cell with a commercially established narrow-bandgap cadmium selenium telluride (CdSeTe) cell in a comparatively easy-to-fabricate four-terminal (4-T) arrangement is a great step in that direction. Herein, the impact of the transparent back contact and the perovskite absorber bandgap on the performance of 4-T perovskite–CdSeTe tandem solar cells is investigated. 4-T perovskite–CdSeTe tandem device architecture with ≈25% efficiency is demonstrated and a feasible pathway is shown to improve the tandem efficiency to more than 30%. Furthermore, the results show that the integration of CdSeTe with perovskite in 4-T tandem PV configurations represents a significant advancement toward achieving higher efficiency and low-cost tandem PVs.

14 SOLAR ENERGY↗

DOE OSTI2022

Post‐Annealing Treatment on Hydrothermally Grown Antimony Sulfoselenide Thin Films for Efficient Solar Cells

Herein, antimony sulfoselenide (Sb 2 (S, Se) 3 ) thin‐film solar cells are fabricated by a hydrothermal method followed by a post‐deposition annealing process at different temperatures and the impact of the annealing temperature on the morphological, structural, optoelectronic, and defect properties of the hydrothermally grown Sb 2 (S, Se) 3 films is investigated. It is found that a proper annealing temperature leads to high‐quality Sb 2 (S, Se) 3 films with large crystal grains, high crystallinity, preferred crystal orientation, smooth and uniform morphology, and reduced defect density. These results show that suppressing deep‐level defects is crucial to enhance solar cell performance. After optimizing the annealing process, Sb 2 (S, Se) 3 solar cells with an improved power conversion efficiency 2.04 to 8.48% are obtained.

14 SOLAR ENERGY↗