Engineering topics

Agrawal, Priyanka

Publications and source records attributed to Agrawal, Priyanka.

14 records

DOE OSTI2026

Experimental determination of critical resolved shear stress for strain-induced phase transformation

The current investigation reports the first attempt to measure the critical resolved shear stress to initiates strain-induced phase transformation in a three-dimensional polycrystalline aggregate using high-energy diffraction microscopy (HEDM). In situ tensile testing was performed on a Fe38.5Mn20Co20Cr15Si5Cu1.5 metastable alloy exhibiting transformation-induced plasticity (TRIP). Grains with a higher propensity for strain-induced phase transformation were tracked using HEDM. A sharp drop in grain specific stress, coinciding with the appearance of a new ε-hcp grain oriented relative to the parent γ-fcc phase, was taken as evidence of grain-specific stress required to trigger phase transformation. The highest resolved shear stress on the potential transformation systems was identified as the critical resolved shear stress (CRSS) for strain-induced phase transformation. For the studied metastable alloy, CRSS for transformation was determined to be 86±3 MPa which was very close to theoretical CRSS value determined using Schmid factor (89±12 MPa) compared to the value determined using Taylor factor (62±7 MPa).

Jain, Roopam↗

DOE OSTI2024

Irradiation-induced shift in the thermodynamic stability of phases and the self-healing effect in transformative high entropy alloys

Here, this work investigated Fe 40 Mn 20 Cr 15 Co 20 Si 5 high entropy alloy (CS-HEA), which exhibits transformation induced plasticity (TRIP) from γ-fcc → ε-hcp, as a probable candidate for nuclear applications. CS-HEA is an extensively-explored, low stacking fault energy alloy with superior strength, ductility, fatigue resistance, and corrosion resistance. This study delved into the effect of irradiation on the shift in thermodynamic stability of the phases and thus radiation tolerance. The evolution of phases, lattice parameters, and transformation volume, V γ→ε , were evaluated from X-ray diffraction experiments along with the mechanical response from nanoindentation. The alloy exhibited a recently-proposed novel self-healing mechanism possible due to the TRIP effect to minimize irradiation damage by restraining the γ-fcc → ε-hcp transformation via thermal aid; this self-healing mechanism was confirmed by transmission electron microscopy. The results were corroborated by a negative change in V γ→ε and a low |V γ→ε |, which is an important criterion for recovery of parent γ-fcc phase. Thus, this alloy was deemed a good radiation-tolerant candidate for nuclear application.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Multimodal and multiscale strengthening mechanisms in Al-Ni-Zr-Ti-Mn alloy processed by laser powder bed fusion additive manufacturing

The unique thermokinetics of laser-powder bed fusion additive manufacturing (L-PBFAM) has been exploited for development of a novel high-strength Al-Ni-Ti-Zr-Mn alloy. The addition of 0.5 wt% Mn leads to extraordinary improvement in ultimate tensile strength (502 MPa) and work hardening due to the activation of two Mn-induced strengthening mechanisms. First, by a bimodal particle strengthening effect due to Al 31 Mn 6 Ni 12 nano-quasi-crystal particles rejected in inter-dendritic spaces and fibrous Al 3 Ni eutectic dendritic channels, which predominately contributes to the strength improvement, and second by solid solution strengthening from remaining Mn entrapped in Al. These mechanisms supplement the particle strengthening effect imparted by coherent and incoherent Al 3 (Ti,Zr) co-precipitates present at melt pool boundaries, dislocation strengthening due to solidification induced strain, and Hall-Petch and backstress strengthening effect due to heterogenous grain size distribution occurring at various length scales. In conclusion, the solidification dynamics and hierarchical heat distribution that are associated with L-PBFAM resulted in complex spatial variations in these strengthening phenomena and were investigated via a high-throughput multiscale structure–property correlation that involved thermokinetic simulation, X-ray diffraction, high-resolution nanoindentation mapping, and site-specific transmission electron microscopy of the alloy.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Strength-conductivity synergy via lean alloy design: A study on novel solid stir extrusion of an Al-2Cu-0.1 Nb-0.15Zr (~wt.%) alloy

Aluminum alloys find wide applications in power and transmission cables, and electrical conductors due to their advantageous properties of high electrical conductivity, and lower cost per unit. However, the lower tensile strength compared to copper poses a challenge for the mechanical stability of aluminum-based cables. In this study, we addressed this issue by adopting a process-based alloy design approach, creating a lean alloy with a dilute composition of Al-2Cu-0.1 Nb-0.15Zr (~wt.%). Here, the alloy was processed using a friction stir based novel SolidStir® (SSE) technique, followed by low-temperature aging. The resulting aluminum wire exhibited improved strength (240 MPa) while simultaneously enhancing electrical conductivity (64%IACS). The study employed computational simulations (Thermocalc) and experimental techniques (differential scanning calorimetry and transmission electron microscopy) to thoroughly investigate the microstructure. Microstructural examinations revealed that the precipitation kinetics in SSE and SSE+aged conditions played a significant role in enhancing strength and electrical conductivity. These findings demonstrate the successful achievement of high strength and high electrical conductivity in aluminum wire through a lean alloy design approach.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Additive manufacturing of a metastable high entropy alloy: Metastability engineered microstructural control via process variable driven elemental segregation

Compositional paradigm shift in high entropy alloys (HEAs) provided new opportunities for microstructural engineering, whereas process control during laser powder bed fusion (LPBF) additive manufacturing (AM) enable fine microstructure tailoring. Metastability engineering in transformation induced plasticity (TRIP) HEAs by addition of minor alloying elements is an attractive strategy for fine microstructural tuning. This study explored in detail the microstructural evolution during LPBF AM of a metastable Fe 40 Mn 20 Co 20 Cr 15 Si 5 (at.%) dual phase HEA (CS-HEA). LPBF processing window for CS-HEA was established based on quantitative analysis and experiments. Based on melt pool overlap lack of fusion pores were observed at lower energy densities (J) of $\textit{J}$ ≤ 31.25 J/mm 3 and key-hole formation by melt pool destabilization in case of $\textit{J}$ ≥ 75 J/mm 3 . The microstructure of CS-HEA consists of metastable FCC-γ and HCP-ε phases; LPBF process parameters governed the final phase fraction in the alloy which has been correlated to metastability alteration of the high temperature γ phase. Final microstructural engineering was devised by LPBF process control which enabled cooling rate manipulation to guide Mn and Si segregation at the cell boundaries, thereby controlling the matrix metastability and final phase fraction. Additionally, high resolution transmission electron microscopy (TEM) revealed disparity in stacking fault morphology in CS-HEA with LPBF process variable alterations associated with local variations in chemical composition and stacking fault energy. Further, the phase evolution with process parameters also affected the nanomechanical behavior of the alloy.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Synergy of tensile strength and high cycle fatigue properties in a novel additively manufactured Al-Ni-Ti-Zr alloy with a heterogeneous microstructure

Alloy design strategies in additive manufacturing (AM) to achieve grain refinement and terminal eutectic solidification have been introduced to engineer Al alloys having microstructural hierarchy and heterogeneity. Such alloy design strategies enable crack-free builds with an expanded AM processing window and pushed the strength limit in Al alloys. However, fatigue performance of Al alloys made by AM is restricted by the presence of process induced defects and its stochasticity. In this work, tensile and high cycle fatigue (HCF) behavior of a novel Al-Ni-Ti-Zr alloy with a heterogeneous microstructure is studied in the as-built condition, supplemented by detailed microstructural and mechanical characterization. Excellent strength-ductility synergy of 342 MPa and 16% failure strain achieved in the alloy was associated with the microstructural attributes that pertain to the novel alloy. Additionally, the alloy showed excellent HCF performance with a fatigue endurance limit to ultimate tensile strength ratio of 0.29 in flexural fatigue mode. The study revealed the existence of multiple crack retardation mechanisms and favorable crack propagation pathways through the fine-grained regions which enabled good fatigue performance to the alloy. Further, a probabilistic model has been used to estimate the fatigue life of the alloy as a function of the stochastic microstructure by utilizing the statistical distribution of pores, solid-state inclusions, and grains in the AM Al alloy. Finally, the model parametric trends are consistent with the experimental observations.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Irradiation response of innovatively engineered metastable TRIP high entropy alloy

For this work, properties and radiation responses of a metastable high alloy (HEA) exhibiting the transformation induced plasticity (TRIP) effect were studied. Innovative engineering used to manufacture this HEA has shown superior mechanical and corrosion properties in 3.5% NaCl than most advanced stainless steels. The microstructural evolution and corresponding mechanical response after irradiation have been evaluated using detailed transmission electron microscopy, and nanoindentation. The study shows a change in metastability of the alloy with irradiation via a recovery mechanism, where the irradiation-induced transformation is reversed by the temperature-induced transformation, thereby introducing the concept of self-healing, made possible due to the TRIP behavior of HEA.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Multiscale hierarchical and heterogeneous mechanical response of additively manufactured novel Al alloy investigated by high-resolution nanoindentation mapping

Smart alloying and microstructural engineering mitigate challenges associated with laser-powder bed fusion additive manufacturing (L-PBFAM). A novel Al–Ni–Ti–Zr alloy utilized grain refinement by heterogeneous nucleation and eutectic solidification to achieve superior performance-printability synergy. Conventional mechanical testing cannot delineate complex micromechanics of such alloys. This study combined multiscale nanomechanical and microstructural mapping to illustrate mechanical signatures associated with hierarchical heat distribution and rapid solidification of L-PBFAM. The disproportionate hardening effect imparted by Al 3 (Ti,Zr) precipitates in the pool boundaries and the semi-solid zone was successfully demonstrated. Nanomechanical response associated with heterogeneity in particle volume fraction and coherency across melt pool was interpreted from nanoindentation force–displacement curves. The hardness map effectively delineated the weakest and strongest sections in the pool with microscopic accuracy. The presented approach serves as a high throughput methodology to establish the chemistry-processing-microstructure-properties correlation of newly designed alloys for L-PBFAM.

36 MATERIALS SCIENCE↗

DOE OSTI2021

High Density of Strong yet Deformable Intermetallic Nanorods Leads to an Excellent Room Temperature Strength-Ductility Combination in a High Entropy Alloy

This paper introduces a new microstructural template for high entropy alloys (HEAs), where the face centered cubic (FCC) complex concentrated solid solution is reinforced with a high density of strong, yet deformable, nanorods of an ordered multi-component intermetallic L12 compound. Thermodynamic modeling has been employed to design this HEA with a large L12 volume fraction. Thermo-mechanical processing by isothermal annealing of the conventionally processed bulk cold-rolled alloy directly at precipitation temperatures, has been applied to produce a high density of uniformly distributed L12 nanorods within refined FCC grains, resulting from concomitant recrystallization and discontinuous precipitation processes. The nanorod morphology of the discontinuous L12 product has been established from three-dimensional atom probe tomography. The refined grains result in a complete coverage of the microstructure with discontinuously precipitated intermetallic nanorods. This nanorod strengthened HEA exhibits an exceptionally high room temperature yield strength of ~1630 MPa, good tensile ductility of ~15%, and an ultimate tensile strength of ~1720 MPa. Furthermore, a single L12 phase alloy, melted based on the precipitate composition in the two-phase FCC + L12 HEA, exhibits very high compressive deformability and strain hardenability, unusual for ordered intermetallic compounds. These results open a new strategy for design of fine-grained microstructures strengthened via ordered intermetallic phases, exploiting the beneficial effects of discontinuous precipitation, for achieving very high room temperature tensile strengths while maintaining good ductility.

Gwalani, Bharat↗

DOE OSTI2021

Design of heterogeneous structured Al alloys with wide processing window for laser-powder bed fusion additive manufacturing

Required microstructural attributes of an alloy vary with structural applications. The microstructural fine-tuning capability of laser-powder bed fusion (L-PBF) additive manufacturing (AM) enables application specific manufacture of the components. Such manufacture with L-PBF AM requires alloys that exhibit wide processing window and are amenable to multiple deformation mechanisms. However, high hot cracking susceptibility of Al alloys poses a barrier to such printability-performance synergy. In this work we show that an integration of, a) grain refinement through heterogeneous nucleation, and b) eutectic solidification, leads to crack-free parts at wide range of process parameters, microstructural heterogeneity, and hierarchy in the Al-Ni-Ti-Zr alloy. Such an integration targets hot cracking at multiple stages of solidification in L-PBF as opposed to the contemporary alloy design strategies that target hot-cracking at only specific stages of solidification. The Al-Ni-Ti-Zr alloy exhibits excellent printability and a high as-built tensile performance. Due to the wide processing window and amenability to multiple deformation mechanisms, the alloy microstructure and subsequently the performance, can be fine-tuned. Here, such strategy opens the gateway for application-specific manufacture of Al alloys with L-PBF AM and establishes a fundamental shift in current methodologies for design of these alloys for L-PBF AM.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Friction stir gradient alloying: A high-throughput method to explore the influence of V in enabling HCP to BCC transformation in a γ-FCC dominated high entropy alloy

The compositional possibilities in high entropy alloys (HEAs) is very vast and effective strategies are needed to establish potential alloy chemistries. In this study, friction stir gradient alloying (FSGA), a recently-introduced high-throughput (HT) technique incorporating compositional and microstructural gradients, was used to explore the possibility of introducing a bcc transformation domain in γ-fcc dominated TRIP HEA Fe 38.5 Mn 20 Cr 15 Co 20 Si 5 Cu 1.5 (at.%) by vanadium addition. FSGA has accelerated the process of attaining the composition-microstructure library and the results suggest that vanadium addition of ~1 at.% results in nucleation of α-bcc. Additionally, this is the first observation of ε-hcp to α-bcc transformation in a TRIP HEA and supports the Olson-Cohen model of martensitic transformation (γ-fcc → ε-hcp → α-bcc). ε-hcp is nucleated with a pyramidal orientation by the formation of planar faults on the {111} close-packed planes of γ-fcc, and α-bcc is nucleated in the vicinity of ε-hcp along the {111} γ-fcc trace. There are indications for the formation of basal orientated ε-hcp from intersecting ε-hcp planes orientated for the pyramidal slip. Thus, the study shows the nucleation and growth of the α-bcc phase attributed to the dual effects of chemistry and strain and potential co-existence of all the three phases.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Additively manufactured novel Al-Cu-Sc-Zr alloy: Microstructure and mechanical properties

An in-depth understanding of microstructure and resultant properties is paramount in the design of a novel alloy system, especially for additive manufacturing (AM). The present investigation aims to characterize a prototypical AM Al alloy with great potential for structural applications. An Al-1.5Cu-0.8Sc-0.4Zr alloy designed using integrated computational material engineering was printed using the laser powder bed fusion AM process. This novel alloy shows promising combination of strength and ductility in as-built and peak-aged conditions. This improvement in the tensile properties is attributed to the presence of both coherent L1 2 Al 3 Sc/Al 3 (Sc,Zr) precipitates and Cu-rich regions. The microstructures were studied via extensive microscopy at different length scales using X-ray microscopy, scanning electron microscopy, and transmission electron microscopy. Fractography revealed that the columnar grain boundaries in as-built condition allow easy slip transfer as compared to the equiaxed grains, with the apex of the melt pool acting as the crack nucleation site. Furthermore, the peak aged condition resulted in improved strength while marginally sacrificing ductility due to precipitates decorating dislocations, grain boundaries and melt pool boundaries thus acting as obstacles to slip transfer.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Microstructure–Property Correlation in a Laser Powder Bed Fusion Processed High-Strength AF-9628 Steel

Laser powder bed fusion additive manufacturing (LPBF-AM) of a low-alloy, high-performance AF-9628 steel results in exceptionally high strength and good ductility. The reasons for such mechanical properties are investigated through detailed microscopy performed at several length scales. Thus, the characterization of melt pool, porosity, grain morphology, phases, and dislocations is performed in the as-printed material. The as-printed material consists of only 0.004 vol% of uniformly distributed porosity, single-phase martensitic laths with an average lath size of ≈2.5 μm, the absence of carbides indicating interstitial trapping of C atom, and high dislocation density in the martensitic laths. Experimental data through microscopy are then fed in analytical models for calculating strengthening contributions from various strengthening mechanisms. Calculated yield strength agrees well with experimentally determined value, and therefore, activation of various strengthening mechanisms is established in as-printed AF-9628.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Notch-tensile behavior of Al0.1CrFeCoNi high entropy alloy

Notch-tensile behavior of an Al0.1CrFeCoNi high entropy alloy (Al0.1-HEA) was studied using V-notch geometry and with local strain mapping using digital image correlation (DIC). A notch-strength ratio of 1.51 indicated notch strengthening. Further analysis of stress-strain response supplemented with microstructural analysis revealed that, while the presence of notch results in strengthening due to work hardening by twinning induced plasticity, the notch also contributes strongly to geometrical softening in the non-uniform ductility regime, and accounts for the onset of failure. The strain localization behavior of Al0.1-HEA due to the presence of V-notch was compared with three conventional alloys: Inconel 625 nickel-based superalloy, 304 stainless steel and Ti–6Al–4V titanium alloy. The study revealed that the nature of notch widening with increasing strain was dependent on material characteristics. The extent of notch widening impacted the local strain field and stress distribution, thereby influencing the propensity for crack initiation and growth. The experimental results were verified by finite element analysis.

Sinha, Subhasis↗