NASA NTRS1982

NDE of simulated Space Shuttle tile disbonds

A technique which involves the use of ultrasonic Lamb waves for assaying the structural integrity of adhesive bonds between layered materials on thin metal plates, particularly with regard to the Shuttle TPS, is presented. The Lamb waves are generated by a pulse impact, resulting in surface waves propagating radially at 2.4 mm/microsec. Trials were performed with the sound waves applied to samples, of aluminum similar to the Orbiter external skin, which were coated with Teflon and a RTV silicone screed. The goal was to detect localized debonded areas or potentially debonded areas, which, during reentry, could result in blistering of the aluminum skin. The ultrasonic probes are described, noting the usage of broadband ultrasonic harmonics and a minicomputer processor. The testing system was found to accurately identify weakened bonds by the ratio of high and low frequency component areas of the received signal of the Lamb waves sent across the surface.

Ahlberg, L.↗

NASA NTRS1978

Laboratory measurements of p-wave seismic Q on lunar and analog rocks

The longitudinal-wave, internal friction quality factor (Qp) of out-gassed rock subjected to hydrostatic confining pressure was measured by a technique of aerodynamically shaping the sample ends to remove most of the air drag. Q values of about 1000 and 100 were obtained at 100 MPa and in laboratory air, respectively. The temperature dependence of Q in lunar rock 70215.85 and an analog of lunar basalt was investigated over the range -100 to 450 deg C. A systematic increase in Q was observed at 50 Hz, 5 kHz and 50 kHz. When the temperature was lowered to -100 deg C moderate decreases in Q were observed from 100 to 250 deg C, and high Q values were obtained at 450 deg C. The temperature and pressure dependences of Q suggest that high lunar seismic Q values imply a very dry crust to depths of at least 50 km. These results further indicate that elastic waves are damped in volatile-rich rock by an absorption mechanism which involves changes in the bonding, structure and coverage of the molecular, physisorbed and chemisorbed H2O at crack and grain boundaries.

Tittmann, B. R.↗

NASA NTRS1977

Internal friction quality-factor Q under confining pressure

It has been found in previous studies that small amounts of adsorbed volatiles can have a profound effect on the internal friction quality-factor Q of rocks and other porous media. Pandit and Tozer (1970) have suggested that the laboratory-measured Q of volatile-free rocks should be similar to the in situ seismic Q values of near-surface lunar rocks which according to Latham et al. (1970) are in the range of 3000-5000. Observations of dramatic increases in Q with outgassing up to values approaching 2000 in the seismic frequency range confirm this supposition. Measurements under confining pressures with the sample encapsulated under hard vacuum are reported to aid in the interpretation of seismic data obtained below the lunar surface. It has been possible to achieve in the experiments Q values just under 2000 at about 1 kbar for a terrestrial analog of lunar basalt. It was found that a well-outgassed sample maintains a high Q whereas one exposed to moisture maintains a low Q as the confining pressure is raised to 2.5 kbar. This result suggests that volatiles can indeed affect Q when cracks are partially closed and the high lunar seismic Q values reported are concomitant with very dry rock down to depths of at least 50 km.

Tittmann, B. R.↗

NASA NTRS1976

Internal friction and velocity measurements

The Q of a lunar basalt sample was measured under varying vacuum conditions, and it was found that even at pressures as low as 10 to the -7th to 10 to the -10th torr, substantial increases in Q with decreasing pressure are observed, while the resonant frequency increases only slightly. This suggests that only small amounts of volatiles are sufficient to increase the internal friction (lower the Q) dramatically. The technique of vibrating encapsulated samples in the torsional mode was used to measure Q of terrestrial rocks as a function of hydrostatic pressure under lunar vacuum conditions. Young's modulus measurements in the temperature range 25-600 C under a variety of conditions including high vacuum show no evidence of any irreversibility upon temperature cycling and no indication that the high Q-values obtained are associated with any permanent structure changes such as the formation of lossless 'welded' contacts.

Tittmann, B. R.↗