NASA NTRS1997

Electron Paramagnetic Resonance Imaging of the Spatial Distribution of Free Radicals in PMR-15 Polyimide Resins

Prior studies have shown that free radicals generated by heating polyimides above 300 C are stable at room temperature and are involved in thermo-oxidative degradation in the presence of oxygen gas. Electron Paramagnetic Resonance Imaging (EPRI) is a technique to determine the spatial distribution of free radicals. X-band (9.5 GHz) EPR images of PMR-15 polyimide were obtained with a spatial resolution of about 0.18 mm along a 2 mm dimension of the sample. In a polyimide sample that was not thermocycled, the radical distribution was uniform along the 2 mm dimension of the sample. For a polyimide sample that was exposed to thermocycling in air for 300 one-hour cycles at 335 C, one-dimensional EPRI showed a higher concentration of free radicals in the surface layers than in the bulk sample. A spectral-spatial two-dimensional image showed that the EPR lineshape of the surface layer remained the same as that of the bulk. These EPRI results suggest that the thermo-oxidative degradation of PMR-15 resin involves free radicals present in the oxygen-rich surface layer.

Ahn, Myong K.↗

NASA NTRS1997

Electron Paramagnetic Resonance Imaging of the Spatial Distribution of Free Radicals in PMR-15 Polyimide Resins

Prior studies have shown that free radicals generated by heating polyimides above 300 C are stable at room temperature and are involved in thermo-oxidative degradation in the presence of oxygen gas. Electron paramagnetic resonance imaging (EPRI) is a technique to determine the spatial distribution of free radicals. X-band (9.5 GHz) EPR images of PMR-15 polyimide were obtained with a spatial resolution of approximately 0.18 mm along a 2-mm dimension of the sample. In a polyimide sample that was not thermocycled, the radical distribution was uniform along the 2-mm dimension of the sample. For a polyimide sample that was exposed to thermocycling in air for 300 1-h cycles at 335 C, one-dimensional EPRI showed a higher concentration of free radicals in the surface layers than in the bulk sample. A spectral-spatial two-dimensional image showed that the EPR lineshape of the surface layer remained the same as that of the bulk. These EPRI results suggest that the thermo-oxidative degradation of PMR-15 resin involves free radicals present in the oxygen-rich surface layer.

Ahn, Myong K.↗

NASA NTRS1992

Lower temperature curing thermoset polyimides utilizing a substituted norbornene endcap

Methoxycarbonyl bridgehead substituted nadic diacid monomethyl ester, when used as an endcapping monomer, lowered the cure temperature of thermoset PMR polyimides without seriously affecting other desirable properties, such as glass transition temperature and thermal oxidative stability. The C-13 CP/MAS NMR of model compounds was used to follow the cure of resin systems using both the unmodified nadic endcap and the methoxycarbonyl-substituted endcap. Rheological analysis and differential scanning calorimetry DSC also provided evidence for the lower curing nature of the substituted endcap. Two regioisomers of the bridgehead-substituted endcap were isolated, and their chemical structures were elucidated by X-ray crystallography. The model compound and molecular modeling studies conducted ruled out the possibility of regioisomeric imide formation in the substituted endcaps.