Temperature dependent interfacial microstructure in HIP-bonded Al6061/Zr joints

Pressing (HIP) at 450 °C and 560 °C under 103 MPa for 90 minutes to evaluate interfacial diffusion and microstructural evolution. Sound metallurgical bonding was achieved at both temperatures, with Zr serving as an effective diffusion barrier. Microstructural analysis revealed the the formation of a (Al,Si)3Zr intermetallic layer at the Al/Zr interface, whose thickness increased from ~100 nm at 450 °C to ~2100 nm at 560 °C, consistent with temperature-driven diffusion kinetics. The thin and continuous reaction layer observed at 450 °C indicates controlled interdiffusion and minimal reaction zone growth, favorable for maintaining interface stability and ductility. At 560 °C, enhanced atomic mobility led to pronounced intermetallic development, confirming diffusion-controlled growth behavior. These results provide valuable insights for optimizing Al/Zr interface design and diffusion barrier performance in advanced structural and energy systems.

Al/Zr interface↗

DOE OSTI2026

Effect of Specimen Thickness on Fracture Toughness and Plane Stress to Plane Strain Transition in Medium-Density Polyethylene

This study investigates the effect of specimen thickness on fracture toughness and the transition from plane stress to plane strain conditions in Medium-Density Polyethylene (MDPE) using Single Edge Notched Bend (SENB) specimens. Three thickness groups (7.5 mm, 9.0 mm, and 12.1 mm) were tested following ASTM D5045 protocol. Conditional stress intensity factors (KQ) increased from 2.2 MPavm to 2.8 MPavm with increasing thickness, demonstrating significant size dependency. Confocal microscopy revealed a 34% reduction in maximum crack tip opening displacement (CTOD) from 0.478 mm to 0.314 mm as thickness increased, with plastic zone lateral extent decreasing by 32%. This quantitative evidence validates Irwin's theoretical prediction of plastic zone size transition from plane stress r_y˜ (1/2p) (K_I/s_y )^2 to plane strain conditions r_y˜ (1/6p) (K_I/s_y )^2.Scanning electron microscopy confirmed progressive suppression of shear lips and evolution from ductile tearing with extensive polymer chain drawing in thin specimens to localized crazing in thick specimens. Despite all specimens satisfying the ASTM D5045 criterion (B = 2.5(KQ/s_y )^2 ) ,residual shear lips persisted even in the thickest specimens, demonstrating that nominal size requirements alone are insufficient for achieving complete plane strain conditions in highly ductile polymers. The findings emphasize the necessity of integrated analytical and morphological assessment for valid fracture toughness characterization, with critical implications for life assessment and integrity prediction in thick-section polymer components such as natural gas distribution pipelines.

Medium-Density Polyethylene↗

DOE OSTI2024

Preliminary Characterization and Evaluation on ShAPE Manufactured 316H and ODS Steels

This study provides the first- of- a- kind results of direct tube formation through shear assisted processing and extrusion (ShAPE) for oxide dispersion strengthened (ODS) steel material; previously only bar was successfully made. The Advanced Materials and Manufacturing Technology (AMMT) program develops cross-cutting technologies in support of a broad range of nuclear reactor technologies and maintains U.S. leadership in materials and manufacturing technologies for nuclear energy applications. The overarching vision of AMMT is to accelerate the development, qualification, demonstration, and deployment of advanced materials and manufacturing technologies to enable reliable and economical nuclear energy. Solid-state advanced manufacturing techniques can overcome some of the challenges in liquid-based additive manufacturing processes and should therefore be considered in material design and manufacturing as well. The work presented in this report forms part of a study on solid-state additive manufacturing techniques of 316 stainless steels and ODS steel components and supports the vision and goals of the AMMT program relevant to accelerate the development and deployment of advanced manufacturing processes. Achieving this can provide a safety improvement through larger safety margins, economic benefit for higher efficiency during operation, and a cost reduction through more effective manufacturing processes and less waste.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Breaking Boundaries: Deformation Processing Techniques for the Next Generation of Lightweight and High-Strength Materials

This chapter emphasizes the importance of solid phase processing (SPP) techniques in developing advanced materials for lightweight and high-strength applications. SPP methods like friction stir welding, and shear-assisted processing can create new microstructures and process materials in novel ways. SPP can enhance mechanical performance via various strengthening mechanisms like solid solution supersaturation, Hall-Petch and Orowan effects, and misorientation angle grain boundaries. The potential for in situ alloying or joining of components with near-net shape and low energy inputs, even for immiscible systems with high enthalpies of mixing, is also discussed. The chapter explores the concept of metastability through microstructural manipulation and the role of advanced characterization for atomistic understanding. The formation of metastable grain, shear-driven chemical mixing, and transformation pathways are also discussed. Finally, the emerging trends for SPP and the challenges that need to be addressed before realizing the full potential of these techniques are presented.

Lastovich, Michael↗

DOE OSTI2023

Evaluation of printability methodologies and feasibility to down select LBPF steel and other materials for nuclear applications

In this work, new research is underway to produce alloys beyond well-known alloys with modified compositions that are better suited to be produced with additive manufacturing. These alloys can only possess improved radiation tolerance but also improved high temperature strength, creep resistance while also using elements that reduce the amount of activation after irradiation. This work package supports the vision and goals of the Advanced Materials and Manufacturing Technology (AMMT) program relevant to accelerate the development and deployment of advanced manufacturing processes. This work focuses on evaluating the methodology for designing alloys best suited for AM processes based on “printability”, literature research to evaluate and down select steel alloy systems. In this work, microstructural characterization and testing activities have been performed on certain steel alloys to support the efforts from collaborating laboratories during the evaluation and printing of the test articles. The final recommendation will be performed by all four participating laboratories.

316L↗

DOE OSTI2023

Shear deformation of pure-Cu and Cu/Nb nano-laminates using micromechanical testing

Solid phase processing by introducing shear deformation into materials can result in unique microstructure evolution and enhanced mechanical properties, especially for immiscible systems such as Cu/Nb. To better understand the correlation between microstructure and deformation behavior during shear, a dedicated testing design of stress localization at predicted sites is necessary. In this study, a specialized S-shaped specimen geometry is implemented to apply localized simple-shear loading in pure-Cu and Cu/Nb accumulative roll-bonded nanolaminates. The nanoscale microstructure and proximity of interfaces in Cu/Nb offer a ~2.8-fold increase in shear stresses than pure-Cu. In pure-Cu, the plastic instability causes shear banding and an in-plane lattice rotation. In Cu/Nb, a partial bending of the interfaces occurred, resulting in a localized lattice rotation. The adapted geometry for micro-scale specimens thus successfully captures the shear deformation at predicted sites in two distinct material systems and could potentially be a powerful technique to study the deformation mechanisms.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Modes of strain accommodation in Cu-Nb multilayered thin film on indentation and cyclic shear

Two-phase layered thin films with a high density of semi-coherent interfaces exhibit excellent mechanical properties and thermal stability. Here, in this study, a magnetron-sputtered Cu-Nb dual-layered thin film (~500 nm for Cu and ~150 nm for Nb) having an amorphous interface between Cu and Nb with a high density of aligned growth twins in Cu is subjected to severe surface deformation. The material is loaded using indentation and cyclic shear under tribological testing. The strain accommodation in the subsurface microstructure after deformation varies based on the local structure and deformation mode. Grain refinement and crack formations in the stressed region of the Nb layer and localized crystallization of the amorphous interface are observed after indentation and scratch testing. Pronounced detwinning of growth twins in the Cu layer under the cyclic shear strain leaves large dislocations sites and loops which are observed both by high-resolution transmission electron microscopy and experiment-guided molecular dynamic (MD) simulations. Our simulations provided insights into understanding the pathway for the detwinning process under cyclic shear loading.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Heterogenous activation of dynamic recrystallization and twinning during friction stir processing of a Cu-4Nb alloy

An interplay between high degree of shear deformation and deformation-induced heating occurs during friction stir processing (FSP) of metals. In medium-to-low stacking fault energy Cu alloys, this can lead to a complex spatially heterogenous activation of dynamic recrystallization (DRX) and twinning mechanisms. Within the Cu-Nb system, the presence of Nb is further expected to influence the DRX mechanism of the Cu matrix. However, the microstructural changes induced by the co-deformation of Nb during FSP are still not well understood. So, this study uses a combination of multimodal microstructural characterization, solution thermodynamics-based predictions, and computational crystal plasticity simulation to reveal the various microstructural evolution mechanisms that can occur during FSP of a Cu-4at.%Nb binary model alloy. The formation of softer DRX zones, and harder shear localization regions are revealed using electron backscatter diffraction, transmission electron microscopy, atom probe tomography, and crystal plasticity modeling.