On electron beam-induced degradation of vinyl ester thermosets
We have demonstrated that electron beam radiolysis induces scissions of the C-O-C bonds along the backbone of the chains of unsaturated polyester thermosets of different compositions based on dicyclopentadiene, isophthalic acid, epoxy vinyl ester, and terephthalic acid. The radiolysis is imminent irrespective of the degree of crosslinking in the thermosets both in neat resins and in the presence of solvents. Electron Paramagnetic Resonance (EPR) results show the formation of the alkoxyl radicals and C-centered radicals as the primary intermediate products of the C-O-C scissions. While the alkoxyl radicals of these resins exhibit very good stability even six months after the irradiation, the C-centered radicals decay very rapidly via their reactions with oxygen that is available either as adsorbed in the resins, dissolved in solvents or from the environment. The radiolytically produced •OH radicals in the unsaturated-ester aqueous solutions play a major role in inducing scissions on the backbone of the polymer chains. The solvated electrons (e s ) from organic solvents, such as dimethyl sulfoxide and isopropyl alcohol, also induce direct scission of the C-O-C bonds, giving rise to the formation of alkoxyl radicals and C-centered radicals. However, a considerable fraction of es is scavenged by the dissolved O 2 to produce O 2 - . Despite the radiation-induced scissions, irradiation of the resins at a dose level of 1000 kGy results in an increase of the glass transition temperature, Tg. This is due to the simultaneous radiation-induced polymerization of the vinyl monomers, toluene, and styrene that are present in the resins. The increase in Tg is observed in all the resins except for the terephthalic polyester resin in aqueous solution, in which the absence of these monomers results in Tg decreasing sharply with irradiation. This work demonstrates that ionizing radiation triggers continuous free radical-chain reactions that lead to the formation of recyclable oligomers.
On the mechanism of radiation and thermal-induced degradation of the insulation cables in nuclear power plants-the presence of long-lived polyenyl C-centered radicals
Radiolytically and thermally produced long-lived polyenyl C-centered radicals in the nuclear power plants’ insulation cables are detected and measured after more than 45 months of aging since the irradiation and the thermal treatment. Electron Paramagnetic Resonance (EPR) results of the irradiated Cross-linked Polyethylene (XLPE) and Ethylene Propylene Rubber (EthProRu), used as primary insulation materials at Nuclear Power Plants (NPP), clearly demonstrate the presence of polyenyl radicals along with allyl and peroxyl radicals. The yields of these free radicals are dose-rate dependent. EPR results also show the presence of the long-lived polyenyl along with allyl and peroxyl free radicals in the thermally treated XLPE, and EthProRu. These free radicals can cause a major failure in the performance of these cables in NPPs. Besides, the results showed the enhancement in the oxidation reactions due to the migration of copper ions from the conductor to the bulk of the insulation. Further, this study also shows that the oxidation index (OI) and Elongation at Break (EAB) increases and decreases respectively at higher doses and temperatures.
On the Mechanism of the Steady-State Gamma Radiolysis-Induced Scissions of the Phenyl-Vinyl Polyester-Based Resins
The major societal problem of polymeric waste necessitates new approaches to break down especially challenging discarded waste streams. Gamma radiation was utilized in conjunction with varying solvent environments in an attempt to discern the efficacy of radiolysis as a tool for the deliberate degradation of model network polyesters. Our EPR results demonstrated that gamma radiolysis of neat resin and in the presence of four widely used solvents induces glycosidic scissions on the backbone of the polyester chains. EPR results clearly show the formation of alkoxy radicals and C-centered radicals as primary intermediate radiolytic products. Despite the protective role of the phenyl groups on the backbone of the radiation-induced polyester chains, the radiolytic-glycosidic scissions predominate. Among the following three solvents used in this study (water, isopropyl alcohol, and dichloromethane), the highest radiolytic yield of glycosidic scission was achieved using water. The •OH radicals produced in the radiolysis of phenyl unsaturated polyester aqueous suspensions very rapidly abstract H atoms from the methylene group, which is followed by a very rapid glycosidic scission. The lowest glycosidic yield was found in the dichloromethane solutions of these polyester resins due to scavenging by the fast electron capture reactions.
Tensile properties and microstructure of additively manufactured Grade 91 steel for nuclear applications
Explore the source record for details and available documents.
H 2 production in the 10 B(n,α) 7 Li reaction in water
Herein we demonstrate a method for measuring the H2 produced in water from the 10 B(n,α) 7 Li fission reaction. Low energy neutrons from the NIST Center for Neutron Research interact with borate-containing water in a temperature-controlled high pressure cell made from titanium. After exposure for one to several hours, the water is extracted and sparged with argon. H 2 entrained in the sparging gas is sampled with a small mass spectrometer. To determine the neutron exposure, a small amount of sodium is included in the borate solution. The water is collected and 24 Na activation is measured in a counting apparatus on the following day. The G-value for H 2 at room temperature is found to be (1.18 ± 0.10) molecules H 2 /100eV, in good agreement with previous estimates and recent modeling calculations.
On the nature of macroradicals formed upon radiolysis of aqueous poly(N-vinylpyrrolidone) solutions
Herein we have explored the nature of macroradicals formed upon radiolysis of aqueous poly(N-vinylpyrrolidone) (PVP) solutions using pulse radiolysis, density functional theory (DFT) and literature data. On the basis of literature data on site-specific kinetics of hydrogen abstraction from simple amides and spectra corresponding to specific radical sites on the same amides we have assessed the distribution of H-atom abstraction by • OH radicals from different positions on the pyrrolidone ring and the polymer backbone. Pulse radiolysis experiments performed at different doses per pulse and different PVP concentrations demonstrate that the H-abstracting radiolysis products are not quantitatively scavenged by the polymer when the dose per pulse exceeds ≈40 Gy. The implications of this are discussed in the context of radical-initiated crosslinking reactions. At a mass fraction of 0.1% PVP and doses per pulse ranging from 7 Gy to 117 Gy, the overall radical decay observed at 390 nm follows second order kinetics with rate constants on the order of 10 9 dm 3 mol -1 s -1 .