DOE OSTI2022

Reduced Recombination and Improved Performance of CdSe/CdTe Solar Cells due to Cu Migration Induced by Light Soaking

The performance of CdTe solar cells has advanced impressively in recent years with the incorporation of Se. Instabilities associated with light soaking and copper reorganization have been extensively examined for the previous generation of CdS/CdTe solar cells, but instabilities in Cu-doped Se-alloyed CdTe devices remain relatively unexplored. In this work, we fabricated a range of CdSe/CdTe solar cells by sputtering CdSe layers with thicknesses of 100, 120, 150, 180, and 200 nm on transparent oxide-coated glass and then depositing CdTe by close-spaced sublimation. After CdCl 2 annealing, Cu-doping, and back metal deposition, a variety of analyses were performed both before and after light soaking to understand the changes in device performance. The device efficiency was degraded with light soaking in most cases, but devices fabricated with a CdSe layer thickness of 120 nm showed reasonably good efficiency initially (13.5%) and a dramatic improvement with light soaking (16.5%). Here, the efficiency improvement is examined within the context of Cu ion reorganization that is well known for CdS/CdTe devices. Low-temperature photoluminescence data and V oc versus temperature measurements indicate a reduction in nonradiative recombination due to the passivation of defects and defect complexes in the graded CdSe x Te 1–x layer.

CdSexTe1−x↗

DOE OSTI2021

Enabling bifacial thin film devices by developing a back surface field using Cu x AlO y

Bifacial solar cells have the potential to increase the energy yield per unit area over traditional monofacial devices without significant added cost, driving $/kWh costs lower and accelerating the adoption of solar photovoltaics. However, the performance of bifacial thin film solar cells significantly lags that achieved by crystalline silicon cells. Here we incorporate wide bandgap Cu x AlO y as a back buffer layer for CdTe devices and achieve a backside illuminated device with high current density and high fill factor. Moreover, these values remain nearly constant even as the absorber layer thickness changes, indicating that a fully-depleted device is not required for efficient charge collection. We show that this response is indicative of a back surface field, albeit with a persistent high back surface recombination velocity. By managing electron reflection, we achieved a backside illumination conversion efficiency of 7.1% and bifaciality of 0.55 for a 3.3 µm CdTe device and 8.0% and 0.62 for a 2 µm device. Future improvements can be made by identifying and incorporating a passivation material that reduces the back surface recombination velocity.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Back-Surface Passivation of CdTe Solar Cells Using Solution-Processed Oxidized Aluminum

Although back-surface passivation plays an important role in high-efficiency photovoltaics, it has not yet been definitively demonstrated for CdTe. Here, we present a solution-based process, which achieves passivation and improved electrical performance when very small amounts of oxidized Al 3+ species are deposited at the back surface of CdTe devices. The open circuit voltage (V oc ) is increased and the fill factor (FF) and photoconversion efficiency (PCE) are optimized when the total amount added corresponds to ~1 monolayer, suggesting that the passivation is surface specific. Addition of further Al 3+ species, present in a sparse alumina-like layer, causes the FF and PCE to drop as the interface layer becomes blocking to current flow. The optimized deposit increases the average baseline PCE for both Cu-free devices and devices where Cu is present as a dopant. The greatest improvement is found when the Al 3+ species are deposited prior to the CdCl 2 activation step and Cu is employed. In this case, the best-cell efficiency was improved from 12.6 to 14.4%. Furthermore, time-resolved photoluminescence measurements at the back surface and quantum efficiency measurements performed at the maximum power point indicate that the performance enhancement is due to a reduction in the interface recombination current at the back surface.

14 SOLAR ENERGY↗

DOE OSTI2020

Understanding and Advancing Bifacial Thin Film Solar Cells

Because bifacial solar cells increase the power generated per area, their market share is projected to increase over the next decade. While silicon technologies have implemented bifacial technology, little progress has occurred in bifacial thin film (BTF) solar cells. Understanding the factors that limit performance is critical to advancing BTF cells. We show that recombination at the back interface has limited device performance of fabricated BTF devices. Improved BTF performance will require decreasing recombination at the back interface, through passivation or by reducing downward band-bending at this interface. Increasing carrier lifetimes improves performance, but increasing hole density has little effect.

14 SOLAR ENERGY↗