DOE OSTI2017

Comparative evaluation of cast aluminum alloys for automotive cylinder heads: Part II: Mechanical and thermal properties

The first part of this study documented the as-aged microstructure of five cast aluminum alloys namely, 206, 319, 356, A356, and A356+0.5Cu, that are used for manufacturing automotive cylinder heads (Roy et al. in Metall Mater Trans A, 2016). In the present part, we report the mechanical response of these alloys after they have been subjected to various levels of thermal exposure. In addition, the thermophysical properties of these alloys are also reported over a wide temperature range. The hardness variation due to extended thermal exposure is related to the evolution of the nano-scale strengthening precipitates for different alloy systems (Al-Cu, Al-Si-Cu, and Al-Si). The effect of strengthening precipitates (size and number density) on the mechanical response is most obvious in the as-aged condition, which is quantitatively demonstrated by implementing a strength model. Significant coarsening of precipitates from long-term heat treatment removes the strengthening efficiency of the nano-scale precipitates for all these alloys systems. Thermal conductivity of the alloys evolve in an inverse manner with precipitate coarsening compared to the strength, and the implications of the same for the durability of cylinder heads are noted.

36 MATERIALS SCIENCE↗
DOE OSTI2017

Comparative evaluation of cast aluminum alloys for automotive cylinder heads: Part I Microstructure evolution

The present study stages a comparative evaluation of microstructure and associated mechanical and thermal response for common cast aluminum alloys that are used for manufacturing automotive cylinder heads. The systems considered are Al-Cu (206-T6), Al-Si-Cu (319-T7), and Al-Si (356-T6, A356-T6, and A356 + 0.5Cu-T6). The focus of the present manuscript is on the evaluation of microstructure at various length scales after aging, while the second manuscript will deal with the mechanical and thermal response of these alloys due to short-term (aging) and long-term (pre-conditioning) heat treatments. At the grain-scale, the Al-Cu alloy possessed an equiaxed microstructure as opposed to the dendritic structure for the Al-Si-Cu or Al-Si alloys which is related to the individual solidification conditions for these alloy systems. The composition and morphology of intermetallic precipitates within the grain and at the grain/dendritic boundary are dictated by the alloy chemistry, solidification, and heat treatment conditions. At the nanoscale, these alloys contain various metastable strengthening precipitates (GPI and θ''θ'' in Al-Cu alloy, θ'θ' in Al-Si-Cu alloy, and β'β' in Al-Si alloys) with varying size, morphology, coherency, and thermal stability.

36 MATERIALS SCIENCE↗
DOE OSTI2016

Diphosphine-Protected Au 22 Nanoclusters on Oxide Supports Are Active for Gas-Phase Catalysis without Ligand Removal

Investigation of monodispersed and atomically-precise Au nanoclusters provides a route to understand the roles of coordination, size, and ligand effects in Au catalysis. We have explored the catalytic behavior of a newly-synthesized Au 22 (L 8 ) 6 nanocluster (L = 1,8-bis(diphenylphosphino) octane) with in situ uncoordinated Au sites supported on TiO 2 , CeO 2 and Al 2 O 3 . Stability of the supported Au 22 nanoclusters was probed structurally by EXAFS and HAADF-STEM, and their adsorption and reactivity for CO oxidation were investigated by IR absorption spectroscopy and temperature programed flow reaction. Low temperature CO oxidation activity was observed for the supported pristine Au 22 (L 8 ) 6 nanoclusters without ligand removal. Isotopically labeled O 2 was used to demonstrate that the reaction pathway occurs through a redox mechanism, consistent with the observed support-dependent activity trend: CeO 2 > TiO 2 > Al 2 O 3 . Substantiated by density functional theory (DFT) calculations, we conclude that the uncoordinated Au sites in the intact Au 22 (L 8 ) 6 nanoclusters are capable of adsorbing CO, activating O2 and promoting CO oxidation reaction. Thanks to the presence of the in situ coordination unsaturated Au atoms, this work is the first clear demonstration of a ligand-protected Au nanocluster that are active for gas phase catalysis without the need of ligand removal.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2016

High Ms Fe16N2 thin film with Ag under layer on GaAs substrate

(001) textured Fe16N2 thin film with Ag under layer is successfully grown on GaAs substrate using a facing target sputtering (FTS) system. After post annealing, chemically ordered Fe16N2 phase is formed and detected by X-ray diffraction (XRD). High saturation magnetization (Ms) is measured by a vibrating sample magnetometer (VSM). In comparison with Fe16N2 with Ag under layer on MgO substrate and Fe16N2 with Fe under layer on GaAs substrate, the current layer structure shows a higher Ms value, with a magnetically softer feature in contrast to the above cases. In addition, X-ray photoelectron spectroscopy (XPS) is performed to characterize the binding energy of N atoms. To verify the role of strain that the FeN layer experiences in the above three structures, Grazing Incidence X-ray Diffraction (GIXRD) is conducted to reveal a large in-plane lattice constant due to the in-plane biaxial tensile strain. INTRODUCTION

Allard, Jr, Lawrence Frederick↗
DOE OSTI2015

Oxidation-induced structural changes in sub-nanometer platinum supported on alumina

Platinum supported on alumina is an essential component of emission treatment catalysts used in transportation. Theoretical, experimental, and mechanistic aspects of platinum particles supported on a variety of supports have been extensively studied; however, available experimental information on the behavior of single vs. sub-nanometer platinum is extremely limited. To bridge the knowledge gap between single supported platinum and well-formed supported platinum nanoparticles, we have carried out synthesis, characterization, and CO and NO oxidation studies of sub-nanometer platinum supported on α, θ, and γ-Al 2 O 3 and monitored changes in structure upon exposure to CO and NO oxidation conditions. Furthermore, we find that sub-nanometer Pt is highly effective for CO oxidation due to high platinum dispersion but is not very efficient as NO oxidation catalyst. Lastly, sub-nanometer platinum agglomerates rapidly under CO or NO oxidation conditions to form nanoparticles.

36 MATERIALS SCIENCE↗