When and Where Lithium Plating Occurs, Its Correlation with Microstructure Heterogeneity, and the Mechanisms That Initiate and Self-Regulate Electrochemical Heterogeneity (A02-0444)

A microstructure scale electrochemical LIB model was used to investigate lithium plating onset, material non-uniform utilization, and in-plane heterogeneities for an NMC-graphite full cell. Model predicts active material particle surface roughness and size distribution (respectively, non-uniform curvature within and between particles) initiate in-plane heterogeneity, and that particle size heterogeneity at the separator interface controls the lithium plating preferential deposition ("Where"). These in-plane heterogeneities are then exacerbated by through-plane heterogeneities induced at fast charge as electrolyte depletion occurs and concentrates intercalation reaction near the anode-separator interface. Also, magnitude and occurrence of lithium plating is controlled by effective, or macroscale, microstructure parameters ("When"). As local states of charge start to diverge between nearby active material regions, overpotential differences induced by OCP difference kick in and contribute to reduce these SOC local heterogeneities. However, for staged materials such as graphite, with OCP profile alternating between plateaus and varying regions, this balancing mechanism is, respectively, inactive and active. This leads to a dynamic, non-monotonic, in-plane heterogeneity time evolution for state of charge and Faraday current density, for which their respective in-plane heterogeneity magnitude alternates. Such behavior has been modeled both for the whole electrode at the microstructure scale and at the particle scale. In-plane heterogeneities are usually considered to be detrimental, as they result in material non-uniform utilization (i.e., under and over stressed regions) and earlier degradations. However, this work provides a more granular approach as it discriminates between a harmful in-plane heterogeneity (non-uniform curvature) that triggers SOC in-plane heterogeneity, and a beneficial in-plane heterogeneity (Faraday current density) that contributes to reduce SOC in-plane heterogeneity. This work comprehensively explains the mechanisms that initiate, exacerbate, and regulate heterogeneity at the microstructure scale, while providing some design suggestions to reduce both in-plane and through-plane heterogeneities, as summarized in the graphical abstract.

ADVANCED PROPULSION SYSTEMS↗

Handling Iterative Solvers in an Algorithmic Differentiation Framework Using Implicit Methods

Differentiable programming is a powerful concept as it enables the seemly propagation of gradients through functions, algorithms, and/or whole physics simulations. These gradients are useful for a wide variety of applications, including sensitivity studies and machine learning, but one of particular interest is optimization. Gradient-based optimization, enabled through automatic/algorithmic differentiation (AD), can be used on predictive physical models to efficiently optimize a set of design variables. AD methods are a particularly promising approach to complex physics simulations because they can be shown to scale well with an increasing number of design variables; however, care must be taken when coupling between different models or different states of a single model.

algorithmic differentiation↗

Cohesive phase-field chemo-mechanical simulations of inter- and trans- granular fractures in polycrystalline NMC cathodes via image-based 3D reconstruction

The optimal design and durable utilization of lithium-ion batteries necessitates an objective modeling approach to understand fracture and failure mechanisms. This paper presents a comprehensive chemo-mechanical modeling study focused on elucidating fracture-induced damage and degradation phenomena in the polycrystalline Li $\mathcal{x}$ Ni 0.5 Mn 0.3 Co 0.2 O 2 (NMC532) cathode. An innovative approach that utilizes image-based reconstructed 3D geometry as finite element (FE) mesh input is employed to enhance the precision in capturing the convoluted architecture and morphological features. For accurately representing the intricate crack configurations within the polycrystalline system, we adopted the cohesive phase-field fracture (CPF) model. Through the integration of advanced image-based geometry reconstruction technique and the promising CPF modeling approach, lithium (de)intercalation induced crack evolution (e.g., nucleation, propagation, branching and diverse modes including inter-/trans-(intra-) granular patterns) and the resulting chemical degradation can be precisely captured, which is also compared and validated with numerical predictions using a continuum damage model. In particular, this model predicts fracture induced degradation under varying fracture properties of grain boundaries and charging rates; the conclusion that NMC particles comprised of larger grains are predicted to have less degradation than those with smaller grains can also be drawn. This comprehensive analysis provides valuable insights into the fracture and degradation within polycrystalline NMC cathodes.

25 ENERGY STORAGE↗

Capturing Time-Varying Wake Dynamics Using Hybridized Actuator Disks in Steady-State Simulations for Improved Optimization Efficiency

When optimizing turbine blade properties, using a time varying, unsteady simulation allows for high-fidelity representations of the wake dynamics. Unfortunately these types of optimizations are prohibitively expensive in terms of computation time and memory requirements. This presentation aims to show a method of transferring the wake dynamics of an unsteady simulation to a much more computationally tractable steady state simulation using hybrid actuator disks informed by unsteady, actuator line model dynamics.

actuator disk model↗

Cell-Format-Dependent Mechanical Damage in Silicon Anodes

Strong binders can be counterproductive for silicon anodes. Here, we show that stresses from cycling Si-based electrodes can cause permanent stretching and wrinkling of the current collector. Furthermore, this deformation damages the electrode coating and accelerates cell aging due to the inactivation of Si domains and facilitation of Li plating. Interestingly, we demonstrate that the formation of wrinkles is size-dependent, being present in pouch cells but absent from coin cells. This size-dependent performance decay indicates that, in extreme cases, testing outcomes are highly dependent on scale and that the validation of battery materials may require testing at larger cell formats.

25 ENERGY STORAGE↗

Enhancing Lithium-Ion Battery Aging Simulations: Coupling a High-Resolution, 3D, Grain-Scale Electromechanical Model to a Single-Particle Model

One of the main goals in modeling lithium-ion batteries is to improve/predict longevity and resilience of new chemistries. Unfortunately, this requires simulation of thousands of charge/discharge cycles, which can be rather time consuming depending on the fidelity of the simulation. The purpose of this talk is to discuss a new modeling framework that couples a high-resolution, continuous damage model (CDM) to a single particle model (SPM) resulting in a good combination of speed and fidelity. In previous work, a 3D, continuum-level chemo-mechanical model was developed to investigate cracking within a single cathode particle comprised of hundreds to thousands of randomly oriented grains. The CDM predicted that particle fracture is primarily due to non-ideal grain interactions with slight dependence on high-rate charge demands. Essentially, when neighboring grains were misaligned, they expanded different rates relative to one another leading to high stresses and ultimately the formation of intraparticle cracks. The model predicted that small particles with large grains develop significantly less damage than larger particles with small grains. Finally, the model predicted most of the chemo-mechanical damage accumulates in the first charge after formation. This chemo-mechanical "damage saturation" effect indicated that initial particle fracture occurs within the first few cycles, while long-term cathode degradation is not solely chemo-mechanically induced. This led to a need for simulating fatigue-like mechanism that degrade the battery over longer time scales. In order to reach the time scales, need to resolve fatigue-like degradation, the CDM needs to be complemented by a faster model. Therefore, recent efforts have been focused on using results from the CDM to inform parameters within the SPM. These parameters are homogenization factors that are associated with diffusion, particle radius, and/or exchange current density. By coupling the CDM to the SPM, the aging simulation is broken up into two domains: short-term and long-term degradation. The short-term degradation occurs over a single cycle and is handled by the CDM due of its high fidelity, but relatively expensive computational cost. Such mechanism include break-in crack caused by mismatches in grain orientation. The long-term degradation occurs over tens of cycles and is handled by the SPM due it's computational efficiency. Most of the fatigue-like mechanism fall into this category. The eventual goal of this modeling framework is to upscale to a psudo-2D model allowing for full electrode simulation, which are informed by high-fidelity grain-scale simulations.

electrochemistry↗

Enabling Extreme Fast-Charging: Challenges at the Cathode and Mitigation Strategies

We report charging lithium-ion batteries (LiBs) in 10 to 15 min via extreme fast-charging (XFC) is important for the widespread adoption of electric vehicles (EVs). Lately, the battery research community has focused on identifying XFC bottlenecks and determining novel design solutions. Like other LiB components, cathodes can present XFC bottlenecks, especially when considering long-term battery life. Therefore, it is necessary to develop a comprehensive understanding of how XFC conditions degrade LiB cathodes. The present article reviews relevant cathode-focused studies and summarizes the current understanding regarding cathode performance and aging issues under XFC conditions. Dominant aging modes and mechanisms are identified at different length-scales with electrochemical correlations for LiNi x Mn y Co z O 2 (NMC)-based cathodes. A range of electrochemical techniques and models provide key insights into cathode performance and life issues. A suite of multimodal and multiscale microscopy and X-ray techniques is surveyed to quantify chemical, structural, and crystallographic NMC-cathode degradation. Cathode cycle-life is scaled to equivalent EV miles to illustrate how cathode degradation translates to real-world scenarios and quantifies cathode-related bottlenecks that hinder XFC adoption. Finally, the article discusses several cathode cycle-life aging mitigation strategies with example case studies and identifies remaining challenges.

25 ENERGY STORAGE↗

A Comprehensive Understanding of the Aging Effects of Extreme Fast Charging on High Ni NMC Cathode

As the battery industry shifts toward high Ni content cathodes, such as LiNi 0.8 Mn 0.1 Co 0.1 O 2 [NMC811], a complete understanding of the degradation mechanisms of NMC811 under extreme fast charging (XFC) (XFC, ≤10–15 min charging) conditions is needed. Such comprehensive understanding would identify the most critical materials gaps that need to be addressed for enabling XFC long-life cells for electric vehicles. This study maps out the key aging mechanisms for NMC811 cycled at different XFC conditions (between 1C and 9C) for up to 1000 cycles. To acquire a fundamental understanding of utilization and degradation, cells are evaluated using a range of electrochemical techniques, and multimodal and multiscale microscopy techniques to quantify chemical, structural, and crystallographic degradation as a function of cycling conditions for the NMC cathode. When comparing NMC811 to NMC532, it is observed that NMC811 has a greater subsurface crystallographic degradation and displays a similar magnitude of subparticle cracking. However, the NMC811 maintains superior performance despite those advanced degradations. Here, the superior cycle life performance is attributed to the NMC811 particles having radially oriented grains and improved transport properties. NMC811 shows between 4.6× and 3.15× reduction in capacity fade than NMC532 for charging rates between 4C (e.g., 15-min charging) and 6C (10-min charging).

25 ENERGY STORAGE↗

Quantifying the Influence of Charge Rate and Cathode-Particle Architectures on Degradation of Li-Ion Cells Through 3D Continuum-Level Damage Models

In this article, we develop a 3D, continuum-level damage model implemented on statistically generated LiNi 0.5 Mn 0.3 Co 0.2 O (NMC 532) secondary cathode particles. The primary motivation of the particle-level model is to inform cathode-particle design through detailed exploration of the influence of secondary and primary particle sizes on the damage predicted during operation, and determine charging profiles that reduce cathode fracture. The model considers NMC 532 secondary particles containing an agglomeration of anisotropic, randomly oriented grains. These brittle, Ni-based cathodes are prone to mechanical degradation, which reduces overall battery cycle life. The model predicts that secondary-particle fracture is primarily due to non-ideal grain interactions and high-rate charge demands. The model predicts that small secondary-particles with large grains develop significantly less damage than larger secondary particles with small grains. The model predicts most of the chemo-mechanical damage accumulates in the first few cycles. The chemo-mechanical model predicts monotonically increasing capacity fade with cycling and rate. Comparing to experimental results, the model is well suited for capturing initial capacity fade mechanisms, but additional physics is required to capture long-term capacity fade effects.

25 ENERGY STORAGE↗