DOE OSTI2020

Evaporated Se x Te 1-x Thin Films with Tunable Bandgaps for Short-Wave Infrared Photodetectors

Semiconducting absorbers in high-performance short-wave infrared (SWIR) photodetectors and imaging sensor arrays are dominated by single-crystalline germanium and III-V semiconductors. However, these materials require complex growth and device fabrication procedures. In this work, thermally evaporated Se x Te 1- x alloy thin films with tunable bandgaps for the fabrication of high-performance SWIR photodetectors are reported. From absorption measurements, it is shown that the bandgaps of Se x Te 1- x films can be tuned continuously from 0.31 eV (Te) to 1.87 eV (Se). Owing to their tunable bandgaps, the peak responsivity position and photoresponse edge of Se x Te 1- x film-based photoconductors can be tuned in the SWIR regime. By using an optical cavity substrate consisting of Au/Al 2 O 3 to enhance its absorption near the bandgap edge, the Se 0.32 Te 0.68 film (an optical bandgap of ≈0.8 eV)-based photoconductor exhibits a cut-off wavelength at ≈1.7 μm and gives a responsivity of 1.5 AW -1 and implied detectivity of 6.5 × 10 10 cm Hz 1/2 W -1 at 1.55 μm at room temperature. Importantly, the nature of the thermal evaporation process enables the fabrication of Se 0.32 Te 0.68 -based 42 × 42 focal plane arrays with good pixel uniformity, demonstrating the potential of this unique material system used for infrared imaging sensor systems.

36 MATERIALS SCIENCE↗

DOE OSTI2019

Evaporated tellurium thin films for p-type field-effect transistors and circuits

There is an emerging need for semiconductors that can be processed at near ambient temperature with high mobility and device performance. Although multiple n-type options have been identified, the development of their p-type counterparts remains limited. In this paper, we report the realization of tellurium thin films through thermal evaporation at cryogenic temperatures for fabrication of high-performance wafer-scale p-type field-effect transistors. We achieve an effective hole mobility of ~35 cm 2 V –1 s –1 , on/off current ratio of ~10 4 and subthreshold swing of 108 mV dec –1 on an 8-nm-thick film. High-performance tellurium p-type field-effect transistors are fabricated on a wide range of substrates including glass and plastic, further demonstrating the broad applicability of this material. Significantly, three-dimensional circuits are demonstrated by integrating multi-layered transistors on a single chip using sequential lithography, deposition and lift-off processes. Finally, various functional logic gates and circuits are demonstrated.

42 ENGINEERING↗

DOE OSTI2019

Strong optical response and light emission from a monolayer molecular crystal

Excitons in two-dimensional (2D) materials are tightly bound and exhibit rich physics. So far, the optical excitations in 2D semiconductors are dominated by Wannier-Mott excitons, but molecular systems can host Frenkel excitons (FE) with unique properties. Here, we report a strong optical response in a class of monolayer molecular J-aggregates. The exciton exhibits giant oscillator strength and absorption (over 30% for monolayer) at resonance, as well as photoluminescence quantum yield in the range of 60-100%. We observe evidence of superradiance (including increased oscillator strength, bathochromic shift, reduced linewidth and lifetime) at room-temperature and more progressively towards low temperature. These unique properties only exist in monolayer owing to the large unscreened dipole interactions and suppression of charge-transfer processes. Finally, we demonstrate light-emitting devices with the monolayer J-aggregate. The intrinsic device speed could be beyond 30 GHz, which is promising for next-generation ultrafast on-chip optical communications.

36 MATERIALS SCIENCE↗

DOE OSTI2019

Centimeter-Scale and Visible Wavelength Monolayer Light-Emitting Devices

Monolayer 2D transition metal dichalcogenides (TMDCs) have shown great promise for optoelectronic applications due to their direct bandgaps and unique physical properties. In particular, they can possess photoluminescence quantum yields (PL QY) approaching unity at the ultimate thickness limit, making their application in light-emitting devices highly promising. In this research, large-area WS 2 grown via chemical vapor deposition is synthesized and characterized for visible (red) light-emitting devices. Detail optical characterization of the synthesized films is performed, which show peak PL QY as high as 12%. Electrically pumped emission from the synthetic WS 2 is achieved utilizing a transient-mode electroluminescence device structure, which consists of a single metal–semiconductor contact and alternating gate fields to achieve bipolar emission. Utilizing this aforementioned structure, a centimeter-scale ( ≈ 0.5 cm 2 ) visible (640 nm) display is demonstrated, fabricated using TMDCs to showcase the potential of this material system for display applications.

36 MATERIALS SCIENCE↗