Probing the fatigue enhancement in a thermally aged cast duplex stainless steel by in situ neutron diffraction

After long-term thermal aging at 400 °C for 3000 h and 10,000 h, a cast duplex stainless steel exhibits promoted fatigue performance, including enhanced three-stage cyclic hardening and prolonged fatigue life. Utilizing in situ neutron diffraction, the phase-specific stresses are resolved, and their evolutions over entire fatigue cycling reveal the underlying mechanisms of the fatigue enhancement. It is found that the ferrite phase bears a much higher stress than the austenite matrix under both as-received and aged conditions. The enhanced cyclic hardening in Stage I is attributed to the strengthening of both phases due to thermal aging, while the enhancement in Stage III results from the martensitic transformation induced strengthening. The fatigue life is prolonged thanks to the cyclic hardening and the delay of martensitic transformation in the austenite phase after thermal aging.

Yu, Dunji↗
DOE OSTI2024

Significantly Promoting the Thermal Conductivity and Machinability of Negative Thermal Expansion Alloy via In Situ Precipitation of Copper Networks

Rapid advancements in electronic devices yield an urgent demand for high-performance electronic packaging materials with high thermal conductivity, low thermal expansion, and great mechanical properties. However, it is a great challenge for current design philosophies to fulfill all the requirements simultaneously. Here, an effective strategy is proposed for significantly promoting the thermal conductivity and machinability of negative thermal expansion alloy (Zr,Nb)Fe 2 through eutectic precipitation of copper networks. The eutectic dual-phase alloy exhibits an isotropic chips-matched thermal expansion coefficient and a thermal conductivity enhancement exceeding 200% compared with (Zr,Nb)Fe 2 , along with an ultimate compressive strength of 550 MPa. The addition of copper reorganizes the composition of (Zr,Nb)Fe 2 , which smooths the magnetic transition and shifts it toward higher temperature, resulting in linear low thermal expansion in a wide temperature range. The highly fine eutectic copper lamellae construct high thermal conductivity networks within (Zr,Nb)Fe 2 , serving as highways for heat transfer electrons and phonons. The in situ forming of eutectic copper lamellae also facilitates the mechanical properties by enhancing interfacial bonding and bearing additional stress after yielding of (Zr,Nb)Fe 2 . This work provides a novel strategy for promoting thermal conductivity and mechanical properties of negative thermal expansion alloys via eutectic precipitation of copper networks.

36 MATERIALS SCIENCE↗
DOE OSTI2024

A Portable Miniature Cryogenic Environment for In Situ Neutron Diffraction

Neutron diffraction instruments offer a platform for materials science and engineering studies at extended temperature ranges far from ambient. As one of the widely used neutron sample environment types, cryogenic furnaces are usually bulky and complex, and they may need hours of beamtime overhead for installation, configuration, cooling, and sample change, etc. To reduce the overhead time and expedite experiments at the state-of-the-art high-flux neutron source, we developed a low-cost, miniature, and easy-to-use cryogenic environment (77–473 K) for in situ neutron diffraction. A travel-size mug serves for the environment where the samples sit inside. Immediate cooling and an isothermal dwell at 77 K are realized on the sample by direct contact with liquid N 2 in the mug. The designed Al inserts serve as the holder of samples and heating elements, alleviate the thermal gradient, and clear neutron pathways. Both a single-sample continuous measurement and multi-sample high-throughput measurements are demonstrated in this environment. High-quality and refinable in situ neutron diffraction patterns are acquired on model materials. The results quantify the orthorhombic-to-cubic phase transformation process in LiMn 2 O 4 and differentiate the anisotropic lattice thermal expansions and bond length evolutions between rhombohedral perovskite oxides with composition variation.

47 OTHER INSTRUMENTATION↗
DOE OSTI2024

Utilizing integrated neutron diffraction and elastoplastic self-consistent crystal plasticity model to quantitatively assess the strengthening mechanism in Al–12.5Ce and Al–12.5Ce–0.4Mg alloys

An integrated in-situ neutron diffraction and elastic plastic self-consistent crystal plasticity (EPSC-CP) modeling scheme is performed on a binary Al–12Ce alloy and a ternary Al–12Ce–0.4Mg alloys. Using this scheme, the constitutive parameters, i.e. elastic constants and slip system parameters of individual phases can be calibrated which can be used in microstructure-based CP models to predict materials performance. From this study, it is shown that the elastic constants of Al 11 Ce 3 intermetallics calculated from density function theory calculation in the literature are rather accurate. When applied to the EPSC-CP model, the lattice strains of both the binary and ternary alloys are correctly predicted as compared with experiments, and large lattice strain differences between Al (100) plane and Al 11 Ce 3 (010) plane are demonstrated. The slip system parameters calibrated by the scheme shows that the addition of 0.4 wt% Mg in the alloy has little influence on the critical resolved shear stress of initial dislocation glide in the Al matrix which caused plastic yield in the material. This can be explained by the very dilute Mg solute content in the Al solid solution, causing large spacing of Al–Mg lattice misfit sites and little impact on resistance of dislocation glide at initial yield. The 0.4 wt% Mg addition, on the other hand, has a large influence on the hardening term in the slip system parameters, indicating those Al–Mg misfit sites do help dislocation accumulation during the deformation. The impact of dilute Mg addition on the Al slip system parameters is also reflected in the flow behavior of the ternary alloy: little impact on the yield stress, but a large impact on working hardening and tensile strength of the materials which is consistent with the literature.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Effect of Collimation on Diffraction Signal-to-Background Ratios at a Neutron Diffractometer

High diffraction signal-to-background ratios (SBRs), the ratios of diffraction peak integrated intensity over its background intensity, are desired for a neutron diffractometer to acquire good statistics for diffraction pattern measurements and subsequent data analysis. For a given detector, while the diffraction peak signals primarily depend on the characteristics of neutron beam and sample coherent scattering, the background largely originates from the sample incoherent scattering and the scattering from the instrument space. In this work, we investigated the effect of collimation on neutron diffraction SBRs of Si powder measurements using one high-angle area detector bank coupled with six different collimation configurations in a large and complex instrument space at the engineering materials diffractometer VULCAN, SNS, ORNL. The results revealed that the diffraction SBRs can be significantly improved by a proper coarse collimator that leaves no gap between the detector and the collimator, and the improvement of SBRs by a fine radial collimator was remarkable with a proper coarse collimator in place but not distinguishable without one. It was also found that the diffraction SBRs were not effectively improved by adding neutron absorbing element boron to the fine radial collimator body, which indicates that either the absorption of secondary scattered neutrons by the added boron is insignificant or the collimator base material (resin and ABS) alone attenuates background scattering sufficiently. These findings could serve as a useful reference for diffractometer developers and/or operators to optimize their collimation to achieve higher diffraction SBRs.

Yu, Dunji↗
DOE OSTI2024

Real-time evolution of texture and temperature during friction stir processing of a magnesium alloy: An operando neutron diffraction study

The real-time development of texture and the evolution of temperature during friction stir processing (FSP) of a Mg alloy were investigated using an operando neutron diffraction measurement. A novel approach was applied in this study where the real-time, quasi-steady state measurements performed as a function of position during FSP are converted to a Lagrangian dataset that reveals the transient behavior as a function of time. The in-situ FSP was carried out under two different thermo-mechanical processing conditions represented by the Zener-Hollomon parameter, Z. Further, the results show that: (i) a shear texture develops from the initial strong basal texture with the peak temperature reaching about 774 K during a low-Z processing and (ii) a strong off-normal texture develops with a peak temperature of 616 K during a high-Z processing. Moreover, time-temperature-texture diagrams were established to reveal the real-time development of the texture during the processing for both the low Z and high Z processing conditions. The changes in texture will be discussed in terms of plastic deformation mechanisms active during various stages of the FSP under the two different processing conditions.

36 MATERIALS SCIENCE↗
DOE OSTI2024

An isotropic zero thermal expansion alloy with super-high toughness

Zero thermal expansion (ZTE) alloys with high mechanical response are crucial for their practical usage. Yet, unifying the ZTE behavior and mechanical response in one material is a grand obstacle, especially in multicomponent ZTE alloys. Herein, we report a near isotropic zero thermal expansion (α l = 1.10 × 10 -6 K -1 , 260–310 K) in the natural heterogeneous LaFe 54 Co 3.5 Si 3.35 alloy, which exhibits a super-high toughness of 277.8 ± 14.7 J cm -3 . Chemical partition, in the dual-phase structure, assumes the role of not only modulating thermal expansion through magnetic interaction but also enhancing mechanical properties via interface bonding. The comprehensive analysis reveals that the hierarchically synergistic enhancement among lattice, phase interface, and heterogeneous structure is significant for strong toughness. Our findings pave the way to tailor thermal expansion and obtain prominent mechanical properties in multicomponent alloys, which is essential to ultra-stable functional materials.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Tensile Deformation of DED Graded IN718-René41 Superalloy at 650°C by in-situ Neutron Diffraction and Digital Image Correlation

A compositionally graded material comprised IN718 (718, γ'/γ" strengthened superalloy) and René41 (R41, a medium γ' strengthened superalloy) was fabricated using laser blown-powder directed energy deposition (DED/LB-M). Hot gas path components that require high and low temperature capabilities at different locations may benefit from such graded superalloy, potentially eliminating the use of welded or mechanically joined components and reducing cost. In the present work, microstructure and 650°C tensile behavior of 718-R41 graded superalloy in as-built and heat-treated states are investigated by Digital Image Correlation (DIC), in-situ neutron diffraction, coupled with conventional characterization techniques. The applied heat treatment generates static recrystallization and equiaxed grains in 718 rich compositions, while R41 rich compositions remain partially or un-recrystallized. Yield strengths of 718 and R41 sections in heat-treated state are comparable to wrought forms but the graded compositions show weakness. From neutron experiment, diffraction elastic constants and single crystal elastic constants are calculated, which show small difference between the as-built and heat-treated states and between the γ and γ' phases. Grain-level load transfer from the (220) grains to (200) grains is found to be composition dependent, and qualitatively agrees with DIC measured macroscopic yield strength. Within the (200) grains, the γ/γ' phases deform elastically until the γ phase yields and afterwards the γ' phase takes load from γ phase.

digital image correlation↗
DOE OSTI2024

An additively manufactured near-eutectic Al-Ce-Ni-Mn-Zr alloy with high creep resistance

A new additively manufactured (AM) Al-7.5Ce-4.5Ni-0.4Mn-0.7Zr (wt.%) near-eutectic alloy is reported, which shows unprecedented creep resistance up to 400 °C (a homologous temperature of 0.72). The eutectic solidification microstructure comprises ~ 27 vol% of coarsening-resistant second phase network with an ultrafine (<100 nm) inter-phase spacing. Both Mn and Zr contribute to creep resistance of the alloy. Small amount of Mn addition promotes selection of coarsening resistant phases without compromising the alloy processability. Zr not only improves hot-tearing resistance, but further enhances the second phase coarsening resistance resulting in improved creep resistance. Neutron diffraction performed during creep deformation reveals that the underlying mechanism for creep resistance in this alloy is impedance to dislocation motion stemming from the ultrafine eutectic solidification microstructure, whereas load transfer strengthening becomes less effective as the creep temperature increases. The second phase forms a continuous network in the as-fabricated condition, which is maintained during long-term creep at 300 °C. However, this network is fragmented into fine dispersoids at higher temperatures. It is proposed that the rate-limiting deformation mechanism at 300–400 °C is (i) dislocation climb for the alloy with fragmented second phase dispersoids and (ii) Orowan looping for the alloy with a continuous second phase network. In conclusion, the present design of an AM-processable multicomponent eutectic alloy with high creep resistance can be applied to other metallic systems exhibiting eutectic reactions, with expected extreme creep resistance.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Additive manufacturing of defect-free TiZrNbTa refractory high-entropy alloy with enhanced elastic isotropy via in-situ alloying of elemental powders

Laser powder-bed fusion (L-PBF) additive manufacturing presents ample opportunities to produce net-shape parts. The complex laser-powder interactions result in high cooling rates that often lead to unique microstructures and excellent mechanical properties. Refractory high-entropy alloys show great potential for high-temperature applications but are notoriously difficult to process by additive processes due to their sensitivity to cracking and defects, such as un-melted powders and keyholes. Here, we present a method based on a normalized model-based processing diagram to achieve a nearly defect-free TiZrNbTa alloy via in-situ alloying of elemental powders during L-PBF. Compared to its as-cast counterpart, the as-printed TiZrNbTa exhibits comparable mechanical properties but with enhanced elastic isotropy. This method has good potential for other refractory alloy systems based on in-situ alloying of elemental powders, thereby creating new opportunities to rapidly expand the collection of processable refractory materials via L-PBF.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Variations in γ′ formers and refractory elements for enhanced creep resistance and phase stability of an advanced Ni-based superalloy

The strong demands on increasing fuel efficiency have continuously driven the optimization of superalloys for high-performance applications. In this study, modifications to the chemistry and heat treatment of HAYNES® 282® alloy (H282) were performed by varying γ′ formers and refractory elements. It was found that increasing Ti and substituting W for some of the Mo in the newly designed alloy (Q) resulted in a significant improvement of creep resistance, up to 130% increase in creep life, compared to standard H282. It was found that Orowan loops and dislocation climb were the dominant creep deformation mechanisms in alloy Q, while extensive dislocation tangling as an additional configuration was observed in the baseline alloy. Moreover, phase stability investigations for up to 5000 h at 800 °C and 900 °C revealed a reduced formation of detrimental σ and μ phases in alloy Q when compared to H282. Atom-probe tomography (APT) revealed that the formation and growth of those phases were responsible for a decrease in Mo content in the matrix, thereby leading to a decrease in solid-solution strengthening in H282 over time. Furthermore, the coarsening of γ′ precipitates was retarded by the substitution of W for Mo, particularly under creep stress. The theoretical and experimental understanding of precipitation strengthening unraveled that higher optimal strengthening occurs at larger particle size for alloy Q, compared to the commercial formulation, further explaining the origin of enhanced creep resistance in the modified alloy.

36 MATERIALS SCIENCE↗
DOE OSTI2023

The Neutronic Engine: A Platform for Operando Neutron Diffraction in Internal Combustion Engines

Neutron diffraction is a powerful tool for noninvasive and nondestructive characterization of materials and can be applied even in large devices such as internal combustion engines thanks to neutrons’ exceptional ability to penetrate many materials. While proof-of-concept experiments have shown the ability to measure spatially and temporally resolved lattice strains in a small aluminum engine on a timescale of minutes over a limited spatial region, extending this capability to timescales on the order of a crank angle degree over the full volume of the combustion chamber requires careful design and optimization of the engine structure to minimize attenuation of the incident and diffracted neutrons to maximize count rates. Here, we present the design of a “neutronic engine,” which is analogous to an optical engine in that the materials and external geometry of a typical automotive engine have been optimized to maximize access of the diagnostic while maintaining the internal combustion chamber geometry and operability of the engine. The high transparency of aluminum to neutrons makes it the ideal window material for neutron diagnostics, which allows the neutronic engine to be a truly all-metal engine with the same load and boundary condition capabilities of a modern downsized passenger car engine. The neutronic engine will enable 3D and time-resolved measurements of strain, stress, and temperature fields as well as phase transformation, texture, and microstructure throughout the metal components of the combustion chamber.

Wissink, Martin↗
DOE OSTI2023

Neutronic engine

An internal combustion engine for neutron diffraction analysis is provided. The engine includes an elongated piston chamber formed from an aluminum alloy to ensure maximum neutron visibility into the combustion chamber. An elongated piston assembly reciprocates within the elongated piston chamber, the piston assembly including an upper piston joined to a lower piston. The upper piston and the lower piston are hollow, thereby reducing the reciprocating mass and increasing neutron access to the combustion chamber. The upper piston is lubricated with a neutron-transparent fluorocarbon lubricant such as perfluoropolyether (PFPE), while the lower piston and the crankcase are lubricated with hydrocarbon lubricant. The engine enables 3D and time-resolved measurements of strain, stress, and temperature, as well as phase transformation, texture, and microstructure.

Wissink, Martin L.↗
DOE OSTI2023

Atomic faulting induced exceptional cryogenic strain hardening in gradient cell–structured alloy

Coarse-grained materials are widely accepted to display the highest strain hardening and the best tensile ductility. We experimentally report an attractive strain hardening rate throughout the deformation stage at 77 kelvin in a stable single-phase alloy with gradient dislocation cells that even surpasses its coarse-grained counterparts. Contrary to conventional understanding, the exceptional strain hardening arises from a distinctive dynamic structural refinement mechanism facilitated by the emission and motion of massive multiorientational tiny stacking faults (planar defects), which are fundamentally distinct from the traditional linear dislocation–mediated deformation. In conclusion, the dominance of atomic-scale planar deformation faulting in plastic deformation introduces a different approach for strengthening and hardening metallic materials, offering promising properties and potential applications.

Gradient dislocation structure↗
DOE OSTI2023

Deformation mechanisms in an additively manufactured dual-phase eutectic high-entropy alloy

Nanostructured metals and alloys often exhibit high strengths but at the expense of reduced ductility. Through harnessing the far-from-equilibrium processing conditions of laser powder-bed fusion (L-PBF) additive manufacturing, we develop a dual-phase nanolamellar structure comprised of FCC/L1 2 and BCC/B2 phases in a Ni 40 Co 20 Fe 10 Cr 10 Al 18 W 2 eutectic high-entropy alloy (EHEA), which exhibits a combination of ultrahigh yield strength (>1.4 GPa) and large tensile ductility (~17%). The deformation mechanisms of the additively manufactured EHEA are studied via in-situ synchrotron X-ray diffraction and high-resolution transmission electron microscopy. The high yield strength mainly results from effective blockage of dislocation motion by the high density of lamellar interfaces. The refined nanolamellar structures and low stacking fault energy (SFE) promote stacking fault (SF)-mediated deformation in FCC/L1 2 nanolamellae. The accumulation of abundant dislocations and SFs at lamellar interfaces can effectively elevate local stresses to promote dislocation multiplication and martensitic transformation in BCC/B2 nanolamellae. The cooperative deformation of the dual phases, assisted by the semi-coherent lamellar interfaces, gives rise to the large ductility of the as-printed EHEA. In addition, here we also demonstrate that post-printing heat treatment allows us to tune the non-equilibrium microstructures and deformation mechanisms. After annealing, the significantly reduced SFE and thicknesses of the FCC nanolamellae facilitate the formation of massive SFs. The dissolution of nano-precipitates in the BCC/B2 nanolamellae reduces spatial confinement and further promotes martensitic transformation to enhance work hardening. Our work provides fundamental insights into the rich variety of deformation mechanisms underlying the exceptional mechanical properties of the additively manufactured dual-phase nanolamellar EHEAs.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Mechanical responses of 316L stainless steel printed by wire arc additive manufacturing with different thermal histories

In this paper, 316L stainless steel walls were printed using single-bead pass and multiple-bead pass wire arc additive manufacturing (WAAM), which represent the internal basket wall and external wall of a spent nuclear fuel (SNF) canister; respectively. Scanning electron microscopy (SEM) microstructure characterization and tensile tests at room temperature (21 °C) and elevated temperature (250 °C) were performed on specimens extracted along the length and height directions of the printed walls. Results showed that grain morphology, grain angles, and retained ferrite are different between the two printed walls, which received different heat input in WAAM. The single-bead pass printed wall exhibited higher yield strength than the multiple-bead pass printed wall because of more retained ferrite and larger portion of random-high angle boundaries (RHAB) grains.