DOE OSTI2023

Exploring Proton Activity at the Membrane/Electrode Interface with Microelectrodes

Microelectrode measurements using a polycrystalline platinum microelectrode were used to simulate the membrane/electrode interface of a membrane-electrode-assembly (MEA) architecture. The proton activity for the hydrogen-evolution reaction (HER) was evaluated for 40, 60, and 80% relative humidity. Proton activity was calculated to be 0.5, 1.0 and 2.0 for 40, 60, and 80% relative humidity, respectively, using open circuit potential measurements between Nafion 211 and 1 molal HClO 4 . The fraction of protons which dissociate at a given relative humidity condition appears to be a distinctive factor in proton activity for Nafion 211 compared to an aqueous electrolyte. In conclusion, the microelectrode measurements exhibited a Tafel slope of ~120 mV/dec, similar to that observed for platinum in MEA systems, demonstrating that kinetic measurements made with microelectrodes can be representative of MEA kinetics.

Anderson, Grace C.↗
DOE OSTI2021

The Effect of Material Properties on Oxygen Evolution Activity and Assessing Half-Cell Screening as a Predictive Tool in Electrolysis

Iridium-based oxygen evolution catalysts are screened in this study for activity and stability with rotating disk electrode (RDE) half-cells. This study focuses on the electrochemical and materials approaches needed to characterize oxygen evolution catalysts, and include testing for activity, stability, composition, oxide content, and structure. Findings also discuss recommendations for data interpretation and detail the difficulties of comparing catalysts across materials sets with different elemental and oxide compositions, and linking RDE activity to device-level performance. The materials evaluated are a mixture of oxides and metals, and several methods are used to quantify metal content, qualitatively assess oxide content, and determine total surface area. Oxygen evolution activities and stabilities are compared, where a wide range of results are reported. In general, higher RDE performances are found for catalysts that contained larger amounts of ruthenium and metals. Higher durability, however, is found for catalysts that only contained iridium and a higher proportion of oxides. Additionally, catalysts are evaluated for performance in membrane electrode assemblies to assess RDE as a predictive tool in electrolysis. While activity trends within individual material sets generally held between ex- and in-situ testing, RDE tends to overestimate the activity of more metallic catalysts when compared to device-level performance. These results stress the need for multiple metal/oxide baselines for mixed catalysts, to better project in-situ kinetics.

36 MATERIALS SCIENCE↗
DOE OSTI2019

The Roles of Oxide Growth and Sub-Surface Facets in Oxygen Evolution Activity of Iridium and Its Impact on Electrolysis

This paper combines density functional theory calculations and electrochemical testing to study activity differences among iridium (Ir) surfaces in the oxygen evolution reaction. Ir metal/hydroxide is significantly more active than Ir oxide, which may be due to oxide skins at the surface weakening O-binding relative to pure metal or oxide surfaces. Here we report a disparity in activity between Ir and Ir oxide in half-cells not observed in single-cells. Extended operation at elevated temperature and potential were found to result in oxide growth, limiting how surface differences affect electrolyzer performance. Comparisons of half- and single-cell testing were used to assess how well rotating disk electrode testing predicts membrane electrode assembly performance and durability. Although oxygen evolution activities in half-cells can translate to single-cells, standard rotating disk electrode test procedures can exaggerate the activity benefit of a metal/hydroxide surface relative to membrane electrode assembly performance under typical operating conditions; it also appears that a half-cell test cannot reasonably accelerate activity loss from continual operation. While a variety of novel catalyst approaches, including alloying, faceting, morphology, and supports can improve oxygen evolution kinetics, these results suggest that Ir surfaces at different oxide states may struggle to improve performance at the device level.

36 MATERIALS SCIENCE↗
DOE OSTI2019

ZIF 67 Based Highly Active Electrocatalysts as Oxygen Electrodes in Water Electrolyzer

Mitigating high overpotential losses originating from the sluggish oxygen evolution reaction (OER) during water electrolysis is key to establishing a sustainable hydrogen generation technique. In this article, we report a Co-imidazolate framework (ZIF 67) as an OER catalyst that exhibits high activity in both a three electrode cell and an electrolyzer. Additionally, Fe, Ni, and Zn have been incorporated into ZIF 67 to evaluate their effects on the OER activity of ZIF 67. Due to the high charge conductivity of ZIF 67, none of the reported catalyst was carbonized at high temperature, a process that is generally accompanied by significant mass loss. Finally, in addition to being highly active, these catalysts are scalable which makes them promising candidates for application in commercial power markets.

25 ENERGY STORAGE↗