EXPLORE THE ARCHIVE

Anita Garg

Publications and source records attributed to Anita Garg.

5 records

NASA NTRS2026

Thermochemical Stability of Ca2Yb8(SiO4)6O2 Apatite in Presence of Molten Calcium-Magnesium-Aluminosilicate (CMAS)

Thermochemical stability of ytterbium silicon oxyapatite Ca 2 Yb 8 (SiO 4 ) 6 O 2 (CYbS) in the presence of molten calcium-magnesium aluminosilicate (CMAS) has been investigated at elevated temperatures for consideration as a thermal and environmental barrier coating (T/EBC) material. CYbS apatite powder was synthesized from the constituent oxides via a solid-state reaction method. Hot-pressed apatite substrates were exposed to molten CMAS at 1200, 1300, and 1400 °C for 1, 10, and 50 h. Development of phases in the interaction region of the heat-treated specimens was monitored using scanning electron microscopy, transmission electron microscopy, high-angle annular dark-field imaging, selected area electron diffraction, and energy dispersive x-ray spectroscopy. Monoclinic cyclosilicate Ca 3 Yb 2 (Si 3 O 9 ) 2 formed from interaction of CYbS apatite with CaO in the CMAS melt at the apatite-CMAS reaction front and continued to nucleate and grow within the residual CMAS in diffusion couples annealed for 1 to 50 h at 1200 °C as well as in those heat treated at 1300 °C for 1 h. Residual CMAS was depleted of Ca when cyclosilicate was present. Dendritic wollastonite (CaSiO3) was observed within the residual CMAS in couples annealed at 1200 and 1300 °C. Ingress of molten CMAS, because of its exponential decrease in viscosity, occurred through open pores and along the grain boundaries of the apatite substrates without any detectable chemical reaction at 1300 and 1400 °C. Results of this study indicate that Ca 2 Yb 8 (SiO 4 ) 6 O 2 apatite has the potential to mitigate the CMAS corrosion up to about 1200 °C but not at higher temperatures.

Narottam P Bansal↗

NASA NTRS2006

Effect of Thermomechanical Processing on the Microstructure, Properties, and Work Behavior of a Ti50.5 Ni29.5 Pt20 High-Temperature Shape Memory Alloy

TiNiPt shape memory alloys are particularly promising for use as solid state actuators in environments up to 300 °C, due to a reasonable balance of proper ties, including acceptable work output. However, one of the challenges to commercializing a viable high-temperature shape memory alloy (HTSMA) is to establish the appropriate primary and secondary processing techniques for fabrication of the material in a required product form such as rod and wire. Consequently, a Ti 50.5 Ni 29.5 Pt 20 alloy was processed using several techniques including single- pass high-temperature extrusion, multiple-pass high-temperature extrusion, and cold drawing to produce bar stock, thin rod, and fine wire, respectively. The effects of heat treatment on the hardness, grain size, room temperature tensile properties, and transformation temperatures of hot- and cold-worked material were examined. Basic tensile properties as a function of temperature and the strain-temperature response of the alloy under constant load, for the determination of work output, were also investigated for various forms of the Ti 50.5 Ni 29.5 Pt 20 alloy, including fine wire.

Grain Size↗

NASA NTRS2006

Properties of a Ni19.5Pd30Ti50.5 High-Temperature Shape Memory Alloy in Tension and Compression

Potential applications involving high-temperature shape memory alloys have been growing in recent years. Even in those cases where promising new alloys have been identified, the knowledge base for such materials contains gaps crucial to their maturation and implementation in actuator and other applications. We begin to address this issue by characterizing the mechanical behavior of a Ni 19.5 Pd 30 Ti 50.5 high-temperature shape memory alloy in both uniaxial tension and compression at various temperatures. Differences in the isothermal uniaxial deformation behavior were most notable at test temperatures below the martensite finish temperature. The elastic modulus of the material was very dependent on strain level; therefore, dynamic Young’s Modulus was determined as a function of temperature by an impulse excitation technique. More importantly, the performance of a thermally activated actuator material is dependent on the work output of the alloy. Consequently, the strain-temperature response of the Ni 19.5 Pd 30 Ti 50.5 alloy under various loads was determined in both tension and compression and the specific work output calculated and compared in both loading conditions. It was found that the transformation strain and thus, the specific work output were similar regardless of the loading condition. Also, in both tension and compression, the strain-temperature loops determined under constant load conditions did not close due to the fact that the transformation strain during cooling was always larger than the transformation strain during heating. This was apparently the result of permanent plastic deformation of the martensite phase with each cycle. Consequently, before this alloy can be used under cyclic actuation conditions, modification of the microstructure or composition would be required to increase the resistance of the alloy to plastic deformation by slip.

High-Temperature Shape Memory Alloy↗

NASA NTRS2005

Characterization of Ternary NiTiPt High-Temperature Shape Memory Alloys

Pt additions substituted for Ni in NiTi alloys are known to increase the transformation temperature of the alloy but only at fairly high Pt levels. However, until now only ternary compositions with a very specific stoichiometry, Ni 50-x Pt x Ti 50 , have been investigated and then only to very limited extent. In order to learn more about this potential high-temperature shape memory alloy system, a series of over twenty alloys along and on either side of a line of constant stoichiometry between NiTi and TiPt were arc melted, homogenized, and characterized in terms of their microstructure, transformation temperatures, and hardness. The resulting microstructures were examined by scanning electron microscopy and the phase compositions quantified by energy dispersive spectroscopy. "Stoichiometric" compositions along a line of constant stoichiometry between NiTi to TiPt were essentially single phase but any deviations from a stoichiometry of (Ni,Pt) 50 Ti 50 resulted in the presence of at least two different intermetallic phases, depending on the overall composition of the alloy. Essentially all alloys, whether single or two-phase, still under went a martensitic transformation. It was found that the transformation temperatures were depressed with initial Pt additions but at levels greater than 10 at.% the transformation temperature increased linearly with Pt content. Also, the transformation temperatures were relatively insensitive to alloy stoichiometry within the range of alloys examined. Finally, the dependence of hardness on Pt content for a series of Ni 50-x Pt x Ti 50 alloys showed solution softening at low Pt levels, while hardening was observed in ternary alloys containing more than about 10 at.% Pt. On either side of these "stoichiometric" compositions, hardness was also found to increase significantly.

Transformation Temperatures↗

NASA NTRS2005

Properties and Potential of Two (Ni,Pt)Ti Alloys for Use as High-Temperature Actuator Materials

The microstructure, transformation temperatures, basic tensile properties, shape memory behavior, and work output for two (Ni,Ti)Pt high-temperature shape memory alloys have been characterized. One was a Ni 30 Pt 20 Ti 50 alloy (referred to as 20Pt) with transformation temperatures above 230 °C and the other was a Ni 20 Pt 30 Ti 50 alloy (30Pt) with transformation temperatures above 530 °C. Both materials displayed shape memory behavior and were capable of 100% (no-load) strain recovery for strain levels up to their fracture limit (3-4%) when deformed at room temperature. For the 20Pt alloy, the tensile strength, modulus, and ductility dramatically increased when the material was tested just above the austenite finish (A f ) temperature. For the 30Pt alloy, a similar change in yield behavior at temperatures above the A f was not observed. In this case the strength of the austenite phase was at best comparable and generally much weaker than the martensite phase. A ductility minimum was also observed just below the A s temperature in this alloy. As a result of these differences in tensile behavior, the two alloys performed completely different when thermally cycled under constant load. The 20Pt alloy behaved similar to conventional binary NiTi alloys with work output due to the martensite-to-austenite transformation initially increasing with applied stress. The maximum work output measured in the 20Pt alloy was nearly 9 J/cm 3 and was limited by the tensile ductility of the material. In contrast, the martensite-to-austenite transformation in the 30Pt alloy was not capable of performing work against any bias load. The reason for this behavior was traced back to its basic mechanical properties, where the yield strength of the austenite phase was similar to or lower than that of the martensite phase, depending on temperature. Hence, the recovery or transformation strain for the 30Pt alloy under load was essentially zero, resulting in zero work output.

High-Temperature Shape Memory Alloy↗