Back-Surface Passivation of CdTe Solar Cells Using Solution-Processed Oxidized Aluminum
Although back-surface passivation plays an important role in high-efficiency photovoltaics, it has not yet been definitively demonstrated for CdTe. Here, we present a solution-based process, which achieves passivation and improved electrical performance when very small amounts of oxidized Al 3+ species are deposited at the back surface of CdTe devices. The open circuit voltage (V oc ) is increased and the fill factor (FF) and photoconversion efficiency (PCE) are optimized when the total amount added corresponds to ~1 monolayer, suggesting that the passivation is surface specific. Addition of further Al 3+ species, present in a sparse alumina-like layer, causes the FF and PCE to drop as the interface layer becomes blocking to current flow. The optimized deposit increases the average baseline PCE for both Cu-free devices and devices where Cu is present as a dopant. The greatest improvement is found when the Al 3+ species are deposited prior to the CdCl 2 activation step and Cu is employed. In this case, the best-cell efficiency was improved from 12.6 to 14.4%. Furthermore, time-resolved photoluminescence measurements at the back surface and quantum efficiency measurements performed at the maximum power point indicate that the performance enhancement is due to a reduction in the interface recombination current at the back surface.