DOE OSTI2022

Performance of stainless steel interconnects with (Mn,Co) 3 O 4 -Based coating for solid oxide electrolysis

Mixed transition-metal oxide coatings are commonly applied to stainless steel interconnects for solid oxide cell stacks. Such coatings reduce oxidation and Cr evaporation rates, leading to improved degradation rate and stack lifetime. Here, the ChromLok™ MCO-based composition (Mn,Co) 3 O 4 is applied to Crofer 22 APU stainless steel and evaluated specifically for application in solid oxide electrolyzer stacks operating around 800 °C and utilizing oxygen-ion-conducting solid oxide cells. The MCO coating is found to decrease the stainless steel oxidation rate by about one order of magnitude, and decrease the Cr evaporation rate by fourfold. Furthermore, the coating also dramatically lowers the rate of area-specific resistance increase for stainless steel coupons oxidized for 500 h with constant current applied, from 33 mΩ*cm 2 kh -1 for an uncoated coupon to less than 4 mΩ*cm2 kh -1 for coated coupons. The coating is demonstrated on full-scale interconnects for single-cells, where the coating dramatically reduces degradation rate, and for a stack, which displays stable operation for 700 h.

08 HYDROGEN↗

DOE OSTI2021

Hydroxide melt induced corrosion of Ni at elevated temperatures under steam electrolysis conditions

Molten alkali electrolyte based high temperature water electrolysis (HTWE) process offers an efficient pathway to integrate renewable energy resources for large scale and economic hydrogen production. Long term and stable operation of these systems require an in-depth understanding of materials stability under anodic and cathodic exposure conditions of the cell and cell stacks. In the present study, we report our findings on the corrosion of Ni in the presence and absence of (LieNa) hydroxide melt at 600 °C under oxidizing and reducing conditions representative of HTWE. While the Ni electrode was found to remain thermodynamically stable in metallic form under cathodic (reducing) exposure conditions, the corrosion rate in molten hydroxide under oxidizing conditions was found to be nonparabolic in nature. A cyclic voltammetry study provides the breakdown of the passive metal-oxide surface layer at the anodic overpotential region between 0.45 V and 2 V in molten hydroxide under oxidizing conditions. As a result, a thermochemical process for accelerated corrosion based on the oxide scale fluxing in hydroxide melt has been developed.

08 HYDROGEN↗

DOE OSTI2020

High-Temperature Alkaline Water Electrolysis

Hydrogen production for mobile and energy storage applications from water electrolysis is attractive due to its high efficiency, fast ramp rates, and potential for the clean energy economy. However, current hydrogen production from electrolysis comprises only a small fraction of the global hydrogen market due to the high cost associated with expensive stack materials (membrane, catalyst, and bipolar plates) and electricity consumption of the commercial electrolysis systems. In this project, we aimed to develop a high temperature alkaline water electrolyzer (HTAWE) that can simultaneously reduce the electrolyzer cost (by adopting cheap material) and improve energy efficiency (by enabling high-temperature operation).

08 HYDROGEN↗

DOE OSTI2020

Stability of ceramic matrix materials in molten hydroxide under oxidizing and reducing conditions

The degradation mechanism of ceramic matrix materials used as molten hydroxide electrolyte support for steam electrolysis cells, is not well documented. In this study, we have investigated the structural and chemical stability of non-oxide and oxide ceramics (SiC, YSZ, Li 2 ZrO 3, LiAlO 2 , and SrZrO 3 ) in the presence of molten hydroxide under oxidizing and reducing conditions with humidity levels of 3 and 85% at 550 °C. SiC, YSZ, Li 2 ZrO 3 and LiAlO 2 showed structural and chemical changes due to dissolution of the ceramic particles in the hydroxide melt followed by precipitation. The SrZrO 3 powder, on the other hand, remained both chemically and structurally stable during 500 h test under both oxidizing and reducing atmospheres. The findings of a stable ceramic matrix in molten hydroxide contribute to the enhancement of the durability and performance of intermediate temperature water electrolysis system.

08 HYDROGEN↗

DOE OSTI2020

Oxidation of porous stainless steel supports for metal-supported solid oxide fuel cells

Here, oxidation behavior of porous P434L ferritic stainless steel, used for the fabrication of metal-supported solid oxide fuel cells (MS-SOFC), is studied under anodic and cathodic atmospheres. Temperature- and atmosphere-dependence is determined for as-sintered and pre-oxidized stainless steel. Pre-oxidation reduced the long-term oxidation rate. For pre-oxidized samples, the oxidation rate in air exceeds that in humid hydrogen for temperatures above 700 °C. The influence of PrOx, LSCF-SDC, and Ni-SDC coatings is also examined. The coatings do not dramatically impact oxide scale growth. Oxidation in C-free and C-containing anodic atmospheres is similar. Addition of CO 2 , CH 4 , and CO to humidified hydrogen to simulate ethanol reformate does not significantly impact oxidation behavior. Cr transpiration in humid air is greatly reduced by the PrOx coating, and a PrCrO 3 reaction product is observed throughout the porous structure. A dense and protective chromia-based scale forms on steel samples during oxidation in all conditions. A thin silica enriched oxide layer also forms at the metal-scale interface. In general, the oxidation behavior at 700 °C is found to be acceptable.

25 ENERGY STORAGE↗