NASA NTRS1985

Heavily doped polysilicon-contact solar cells

The first use of a (silicon)/heavily doped polysilicon)/(metal) structure to replace the conventional high-low junction or back-surface-field (BSF) structure of silicon solar cells is reported. Compared with BSF and back-ohmic-contact (BOC) control samples, the polysilicon-back solar cells show improvements in red spectral response (RSR) and open-circuit voltage. Measurement reveals that a decrease in effective surface recombination velocity S is responsible for this improvement. Decreased S results for n-type (Si:As) polysilicon, consistent with past findings for bipolar transistors, and for p-type (Si:B) polysilicon, reported here for the first time. Though the present polysilicon-back solar cells are far from optimal, the results suggest a new class of designs for high efficiency silicon solar cells. Detailed technical reasons are advanced to support this view.

Lindholm, F. A.↗

NASA NTRS1985

Experimental study of the minority-carrier transport at the polysilicon-monosilicon interface

This paper presents the results of an experimental study designed to explore both qualitatively and quantitatively the mechanism of the improved current gain in bipolar transistors with polysilicon emitter contacts. Polysilicon contacts were deposited and heat treated at different conditions. The electrical properties were measured using p-n junction test structures that are much more sensitive to the contact properties than are bipolar transistors. A simple phenomenological model was used to correlate the structural properties with electrical measurements. Possible transport mechanisms are examined and estimates are made about upper bounds on transport parameters in the principal regions of the devices. The main conclusion of this study is that the minority-carrier transport in the polycrystalline silicon is dominated by a highly disordered layer at the polysilicon-monosilicon interface characterized by very low minority-carrier mobility. The effective recombination velocity at the n(+) polysilicon-n(+) monosilicon interface was found to be a strong function of fabrication conditions. The results indicate that the recombination velocity can be much smaller than 10,000 cm/s.

Neugroschel, A.↗

NASA NTRS1985

Front and back polysilicon-contacted silicon solar cells

The first use of a (silicon)/ (heavily doped polysilicon)/ (metal) structure to replace the conventional high-low junction (or back-surface-field, BSF) structure of silicon solar cells is reported. Compared with BSF and back-ohmic-contact control samples, the polysilicon-back solar cells show improvements in red spectral response and open-circuit voltage. Measurement reveals that a decrease in effective surface recombination velocity S is responsible for this improvement. Decreased S results for n-type (Si:As) polysilicon, consistent with past findings for bipolar transistors, and for p-type (Si:B) polysilicon, reported here for the first time. Though the present polysilicon-back solar cells are far from optimal, the results suggest a new class of designs for high efficiency silicon solar cells. Detailed technical reasons are advanced to support this view.

Lindholm, F. A.↗