DOE OSTI2024

Electrostatic Dissipation in 3D-Printable Silicone

Here, in this report, we describe the incorporation of single-walled carbon nanotubes (CNTs) into 3D printable siloxane elastomers for electrostatic dissipation. The composite was characterized, focusing on how rheological and mechanical properties of the siloxane are affected at various CNT loading levels. Electrical properties were also characterized to develop materials with effective electrostatic dissipation. We demonstrate that low loadings (<1 wt %) of CNTs can be sufficiently dispersed into silicone resins that can be 3D printed, and the resulting material shows a significant improvement in electrostatic dissipation through the reduction in electrical resistivity with minimal effect on its mechanical properties.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Controlled In Situ Foaming for Mechanical Responsiveness of Architected Foams

Addition of chemical blowing agents to polysiloxane resins produces foams with closed–cell morphology. Combining this chemistry with the 3D–printing technique direct ink writing (DIW) permits the creation of architected foams with controllable, hierarchical tiers of porosity. Here, using a two–component foaming ink, the extent of foaming can be controlled by incorporating an active mixing printhead as part of the fabrication process. Changes in the mixing speed allows for in situ control of the foaming reaction where the mixing speed is directly correlated with the resulting foaming that occurs upon extrusion. These architected foams display tunable mechanical responses, porosities, and open–to–closed cell ratios. While chemically blown polysiloxane foam is a well–established material, utilizing DIW as fabrication technique presents a novel approach for creating tailored, architected foams that require minimal post–processing.

36 MATERIALS SCIENCE↗