DOE OSTI2022

Quantifying Equiaxed vs Epitaxial Solidification in Laser Melting of CMSX-4 Single Crystal Superalloy

The competition between epitaxial vs. equiaxed solidification has been investigated in CMSX-4 single crystal superalloy during laser melting as practiced in additive manufacturing. Single-track laser scans were performed on a powder-free surface of directionally solidified CMSX-4 alloy with several combinations of laser power and scanning velocity. Electron backscattered diffraction (EBSD) mapping facilitated identification of new orientations, i.e., “stray grains” that nucleated within the fusion zone along with their area fraction and spatial distribution. Using high-fidelity computational fluid dynamics simulations, both the temperature and fluid velocity fields within the melt pool were estimated. This information was combined with a nucleation model to determine locations where nucleation has the highest probability to occur in melt pools. In conformance with general experience in metals additive manufacturing, the as-solidified microstructure of the laser-melted tracks is dominated by epitaxial grain growth; nevertheless, stray grains were evident in elongated melt pools. It was found that, though a higher laser scanning velocity and lower power are generally helpful in the reduction of stray grains, the combination of a stable keyhole and minimal fluid velocity further mitigates stray grains in laser single tracks.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Time-Resolved Geometric Feature Tracking Elucidates Laser-Induced Keyhole Dynamics

In this report, during laser melting of metals, localized metal evaporation resulting in the formation of a keyhole shaped cavity can occur if processing conditions are chosen with high power density. An unstable keyhole can have deleterious effects in certain applications (e.g., laser powder bed fusion) as it increases the likelihood of producing defects such as porosity. In this work, we propose a pipeline that enables complete segmentation and extraction of various geometric features in keyholing conditions. In situ synchrotron high-speed X-ray visualization at the Advanced Photon Source provides large datasets of experimental images with a high spatio-temporal resolution across a range of laser parameters for Ti-6Al- 4 V. Computer vision image processing techniques were used to extract time-resolved quantitative geometric features (e.g., depth, width, front wall angle) throughout keyhole evolution which were subsequently analyzed to understand the relationship between the variation of local keyhole geometry and processing conditions. This analysis is the first to employ a data-driven approach to further our understanding of the keyholing process regime.

36 MATERIALS SCIENCE↗

NASA NTRS2018

Development and Flammability Testing of Magnesium Alloys for Space Applications

This project will be comparing the flammability of select lightweight Mg alloys for use in a simulated ISS environment. It will also be determining the factors that influence flammability of selected alloys in elevated oxygen, including the formation of an oxide layer. The significance of this work is that such alloys can reduce weight saving by up to 30%. This work is adding to knowledge base of lightweight Mg alloys for possible future applications, as no previous flammability testing of Mg alloys have been conducted at elevated oxygen concentrations.

International Space Station↗

NASA NTRS2017

Magnesium Alloys for Space Hardware Design

There have been advances in magnesium alloy development that NASA has not taken into consideration for space hardware because of a lack of test data. Magnesium alloys offer excellent weight reduction, specific strength, and deep space radiation mitigation. Traditionally, magnesium has been perceived as having too poor of a flammability resistance and corrosion resistance to be used for flight. Recent developments in magnesium alloying has led to the formation of two alloys, WE43 and Elektron 21, which are self-extinguishing and significantly less flammable because of their composition. Likewise, an anodizing process called Tagnite was formulated to deter any concern with galvanic and saltwater corrosion. The Materials Science Branch at Kennedy Space Center is currently researching these new alloys and treatments to better understand how they behave in the harsh environment of space. Successful completion of the proposed testing should result in a more thorough understanding of modern aerospace materials and processes, and possibly the permission to use magnesium alloys in future NASA designs.

microstructure↗