Arregui-Mena, Jose David

DOE OSTI2024

Comprehensive characterization of the irradiation effects of glassy carbon

Carbon materials have become increasingly diverse, finding applications in high-temperature and high-radiation environments. Glassy carbon, an allotrope known for its exceptional chemical inertness and desirable mechanical properties. However, understanding neutron irradiation effects in glassy carbon has proven challenging, primarily because of its unique nanopore structure. Here, this study presents a highly detailed microstructural characterization investigation of neutron-induced changes in glassy carbon, revealing how changes in nanopore structure and crystallinity impact the irradiation-induced shrinkage. Aberration-corrected scanning transmission electron microscopy (STEM) reveals pore closure that leads to material densification in the irradiated samples. Dimensional analysis combined with comparison to historical data suggest significant length shrinkage to occur. Neutron and in situ electron irradiation experiments suggest that glassy carbon transforms into so-called carbon onions, supporting the concept of shrinkage saturation. Investigating irradiation temperature effects using STEM, electron energy loss spectroscopy, x-ray diffraction, and Raman spectroscopy revealed partial amorphization at 210 °C–230 °C and preserved order in glassy carbon at 860 °C, coinciding with pore closure. Thermal property measurements were also conducted to assess the effects of densification and other changes in the atomic structure of glassy carbon. The results of this study have broad implications in the deployment of glassy carbon to nuclear environments, based around the observed changes in the thermal properties, and demonstrates the operational window for the onset of densification.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Development of a Reconstruction Methodology Based on X-Ray Computed Tomography to Generate Realistic 3D Concrete Microstructures in MOSAIC

Despite being passive components, concrete structures represent a major capital investment in nuclear power plants. However, some concrete components are critical for the safety and long-term operation of the reactors: the concrete containment building protects the reactors from external aggression. The concrete biological shield (CBS) contains the radiation exiting the reactor to protect equipment and personnel. Depending on the design, the CBS also has a function for supporting the reactor’s systems. This function needs to be ensured in-service and during accident scenarios. After several decades of use, the CBS is exposed to high-energy irradiation over an extended operation time, exceeding the fluence level currently considered detrimental for the concrete’s structural properties. Such conditions occur at different times depending on the reactor’s operation and design. Nevertheless, from the perspective of subsequent license application, it is mandatory to assess the potential effects of prolonged irradiation on concrete. Unlike steel components, concrete structures are built with local constituents (cement, sand, and coarse aggregates) to avoid prohibitive transportation costs. Thus, concrete performance is determined by the tolerance or the susceptibility of its constituents against any aging mechanism. The tolerance against irradiation of the CBSs may vary greatly among the 56 nuclear power plants and 93 nuclear power reactors that form the current US light-water reactor fleet. Irradiation-induced degradation is mainly a result of amorphization-induced expansions of the silicated minerals present in the aggregates. The neutron irradiation–induced expansion varies from one rock-forming mineral to another: well framework–structured silicates (e.g., quartz and feldspars) exhibit higher swelling than chained (e.g., pyroxene) or isolated silicates (e.g., garnet). Silicates make up nearly 90% of the Earth’s crust. Other common minerals present in construction aggregates are carbonates found, for example, in limestone. Irradiated carbonates exhibit only very minor expansions.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗