DOE OSTI2022

Dispersing Agents Impact Performance of Protonated Phosphonic Acid High-Temperature Polymer Electrolyte Membrane Fuel Cells

The microstructure of ionomers plays a significant role in the performance of high-temperature polymer electrolyte membrane fuel cells (HT-PEMFCs). Here, we establish direct correlations between the properties of dispersing agents and the microstructure of a protonated phosphonic acid ionomer. Most importantly, the formation of the porous structure of a protonated phosphonic acid ionomer depends on the pK a of the liquid media. Namely, the acid–base interaction between the charged polymer and dispersing agents determines the porosity in the ionomer thin films. The HT-PEMFC performance increases with the level of porosity of the ionomer, as the pores enable fast reactant gas accessibility. Overall, this study concludes the importance of the pK a of ionomers’ dispersing media for the HT-PEMFC performance.

25 ENERGY STORAGE↗

DOE OSTI2022

Protonated phosphonic acid electrodes for high power heavy-duty vehicle fuel cells

We report that state-of-the-art automotive fuel cells that operate at about 80 °C require large radiators and air intakes to avoid overheating. High-temperature fuel cells that operate above 100 °C under anhydrous conditions provide an ideal solution for heat rejection in heavy-duty vehicle applications. Here we report protonated phosphonic acid electrodes that remarkably improve the performance of high-temperature polymer electrolyte membrane fuel cells. The protonated phosphonic acids comprise tetrafluorostyrene-phosphonic acid and perfluorosulfonic acid polymers, where a perfluorosulfonic acid proton is transferred to the phosphonic acid to enhance the anhydrous proton conduction of fuel cell electrodes. By using this material in fuel cell electrodes, we obtained a fuel cell exhibiting a rated power density of 780 mW cm -2 at 160 °C, with minimal degradation during 2,500 h of operation and 700 thermal cycles from 40 to 160 °C under load.

25 ENERGY STORAGE↗

DOE OSTI2020

Synergistically integrated phosphonated poly(pentafluorostyrene) for fuel cells

Modern electrochemical energy conversion devices require more advanced proton conductors for their broad applications. Phosphonated polymers have been proposed as anhydrous proton conductors for fuel cells. However, the anhydride formation of phosphonic acid functional groups lowers proton conductivity and this prevents the use of phosphonated polymers in fuel cell applications. Here, we report a poly(2,3,5,6-tetrafluorostyrene-4-phosphonic acid) that does not undergo anhydride formation and thus maintains protonic conductivity above 200 °C. We use the phosphonated polymer in fuel cell electrodes with an ion-pair coordinated membrane in a membrane electrode assembly. We find that this synergistically integrated fuel cell reached peak power densities of 1,130 mW cm -2 at 160 °C and 1,740 mW cm -2 at 240 °C under H2/O2 conditions, substantially outperforming polybenzimidazole- and metal phosphate-based fuel cells. Our result indicates a pathway towards using phosphonated polymers in high-performance fuel cells under hot and dry operating conditions.

25 ENERGY STORAGE↗

DOE OSTI2020

Role of phosphate source in improving the proton conductivity of tin pyrophosphate and its composite electrolytes

Metal pyrophosphates (MPPs) in general, and tin pyrophosphate (TPP) in particular, have received significant interest in the last decade due to their potential as proton conductors for electrolyte application in intermediate temperature (IT)-fuel cells. However, for MPP based electrolytes, despite high reported proton conductivities, achieving good fuel cell performance and high open circuit voltage (OCV) remains a challenge with synthesis methods playing a crucial role in determining the final proton conductivity. Here we report the role of phosphate precursor in determining the TPP proton conductivity by examining five different precursors: (1) phosphoric acid (TPP-PA), (2) ammonium hydroxide + phosphoric acid (TPP-NH 4 OH), (3) diammonium phosphate (TPP-DAP), (4) tetramethylammonium sulphate + phosphoric acid (TPP-TMAP), and (5) tetrabutylammonium phosphate (TPP-TBAP), where a maximum conductivity of 88 mS cm -1 at 200 °C was obtained for TPP prepared from the TBAP precursor. TPP prepared from all of the different precursors formed the crystalline cubic Pa-3 with combining macron] phase after sintering at 650 °C for 2.5 hours. Furthermore, TPP-TBAP/Nafion® composite membranes prepared with a 90 : 10 ratio exhibited an OCV of 0.98 V and produced a maximum peak power density (PPD) of 630 mW cm -2 at an operating temperature of 220 °C. Our results demonstrate the significant impact of the TPP precursor on proton conductivity and fuel cell performance.

36 MATERIALS SCIENCE↗