DOE OSTI2022

A multimodal approach to revisiting oxidation defects in Cr 2 O 3

The oxidation of chromium in air at 700 °C was investigated with a focus on point defect behavior and transport during oxide layer growth. A comprehensive set of characterization techniques targeted characteristics of chromium oxide microstructure and chemical composition analysis. TEM showed that the oxide was thicker with longer oxidation times and that, for the thicker oxides, voids formed at the metal/oxide interface. PAS revealed that the longer the oxidation time, there was an overall reduction in vacancy-type defects, though chromium monovacancies were not found in either case. EIS found that the longer oxidized material was more electrochemically stable and that, while all oxides displayed p-type character, the thicker oxide had an overall lower charge carrier density. Together, the results suggest anion oxygen interstitials and chromium vacancy cluster complexes drive transport in an oxidizing environment at this temperature, providing invaluable insight into the mechanisms that regulate corrosion.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Defect Characterization Using Positron Annihilation Spectroscopy on Laser-Ablated Surfaces

In recent years, short, pulsed laser ablation has been gaining popularity for machining small-scale test geometries from bulk samples and for efficient serial sectioning. These laser-based techniques are being added to the toolbox in material science, which makes it necessary to understand the changes in the material that occur from the laser–material interaction. Positron annihilation spectroscopy is a unique, nondestructive technique to investigate small defects in materials difficult to investigate by other tools. In this work, Doppler broadening and positron lifetime annihilation spectroscopy are utilized to help quantify the damage in materials treated with short, pulsed lasers. Using a femtosecond laser on single crystal silicon, this manuscript shows that clusters of vacancy-like defects and small voids increase systematically with laser power. Lastly, the damage induced by the laser can also reach to micrometer depths.

36 MATERIALS SCIENCE↗