Engineering topics
Avila, Viviana
Publications and source records attributed to Avila, Viviana.
Phase evolution during conventional and reactive flash sintering of (Mg,Ni,Co,Cu,Zn)O via in situ X-ray diffraction
Reactive flash sintering (RFS) enables the simultaneous synthesis and sintering of ceramics and has been shown to affect the reaction pathway of different materials. Herein, in situ synchrotron X-ray diffraction (XRD) is used to investigate the (Mg,Ni,Co,Cu,Zn)O entropy-stabilized oxide formation during: (i) conventional heating and (ii) RFS under current rate-controlled mode. The same reaction pathway is verified in both instances: the starting rock-salt (RS), spinel (Co 3 O 4 ), tenorite (CuO), and wurtzite (ZnO) phases transform into a single RS phase with a (1 1 1) to (2 0 0) intensity ratio of 0.67, consistent with a random distribution of the cations into the structure. Pt lattice peak shift from the XRD patterns is used as standard to monitor the sample surface temperature, revealing a strong endothermic reaction during the RS single-phase formation (Pt peaks shift toward higher angles while increasing sample temperature/current density). Furthermore, in RFS, the single-phase RS structure is formed in just 60 s at a furnace temperature of 600°C and a current rate of 220 mA mm -2 /min. Therefore, RFS greatly accelerates the synthesis of (Mg,Ni,Co,Cu,Zn)O, however, it does not play a role in the reaction pathway for this material formation.
On the Arrhenius-like behavior of conductivity during flash sintering of 3 mol% yttria stabilized zirconia ceramics
Here, we discuss the Arrhenius behavior of electrical conductivity σ during flash sintering of 3 mol% yttria stabilized zirconia (3YSZ). In situ x-ray diffraction is used to determine sample temperature. Sintering contribution to σ is excluded by investigating the flash event on a dense ceramic. We show that total conductivity follows an Arrhenius-like equation in both dense and green samples, even during Stage II of flash. The non-linearity often verified during flash sintering of 3YSZ is therefore related to the furnace temperature instead of the sample temperature when building the ln(σ) vs. 1/T plots. Furthermore, we verified a change in the activation energy for conduction prior to the ignition of the flash event and discussed the possible mechanisms. For instance, the decrease in activation energy from Stage I to II in the dense sample is attributed to a contribution from electronic carriers.
Phase evolution during reactive flash sintering of Li 6.25 Al 0.25 La 3 Zr 2 O 12 starting from a chemically prepared powder
Here, reactive flash sintering (RFS) of a chemically prepared multiphase precursor powder was performed to fabricate Li 6.25 Al 0.25 La 3 Zr 2 O 12 (Al-LLZO) ceramics. This approach allowed for obtaining single-phase dense samples in a remarkably short processing time of 30 s, at a furnace temperature of 600 °C, with an electric field of 50 V cm -1 and a current limit of 150 mA mm -2 . The ceramics display high bulk conductivity of 0.18 mS cm -1 at room temperature. Furthermore, phase evolution is studied by in-situ X-ray diffraction during: i) conventional heating and ii) RFS under current rate mode. As expected, the intermediate phases progressively dissolved into the Al-LLZO matrix by conventional heating. On the other hand, RFS promoted the growth of the intermediate La 2 Zr 2 O 7 , an effect that was overcome by the thermally driven formation of Al-LLZO at higher temperatures. The observed different reaction pathway suggests that RFS can be used for stabilizing phases that are not thermodynamically favored upon conventional heating.