Reduction kinetics of hematite powder using argon/hydrogen plasma with prospects for near net shaping of sustainable iron

Direct reduction of iron ore using hydrogen plasma is being explored as a potential solution to decarbonize the iron and steel sector. The current state-of-the-art demonstrated reduction of hematite pellets via hydrogen plasma using Ar + 10% H 2 but had slow reduction kinetics, requiring 30 minutes of plasma exposure for complete reduction. Here we show that using hematite in a powder form, easily obtainable from beneficiated ore, results in 10× faster kinetics using plasma generated from Ar + 2% H 2 shielding gas compared to the current state-of-the art. Additionally, the increased kinetics using powders and a dilute hydrogen concentration can enable the use of advanced manufacturing techniques like blown powder directed energy deposition using a plasma tungsten arc welding torch to manufacture near net shape components directly from the ore concentrates. This ore to part approach will also reduce the emissions associated with downstream processes like rolling, forging, and machining, thereby further aiding in the sectorial decarbonization efforts.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Additive manufacturing methods using aluminum-rare earth alloys and products made using such methods

Described herein are additive manufacturing methods and products made using such methods. The alloy compositions described herein are specifically selected for the additive manufacturing methods and provide products that exhibit superior mechanical properties as compared to their cast counterparts. Using the compositions and methods described herein, products that do not exhibit substantial coarsening, such as at elevated temperatures, can be obtained. The products further exhibit uniform microstructures along the print axis, thus contributing to improved strength and performance. Additives also can be used in the alloys described herein.

Plotkowski, Alex J.↗
DOE OSTI2021

Heterogeneous creep deformation behavior of functionally graded transition joints (GTJs)

Dissimilar metal welds (DMWs) made between ferritic steels and austenitic alloys are used extensively in high-temperature power plant components. These DMWs experience premature creep failure in the ferritic steel’s heat affected zone (HAZ), close to the weld interface. Steep variations in microstructure and chemical composition across the dissimilar weld interface have been the contributing factors for the failure. Graded transition joints (GTJs), developed by functionally grading the chemical composition in layers, have been proposed as potential candidates to replace DMWs. In this research, GTJ coupons were fabricated between 2.25Cr-1Mo steel and Alloy 800H base material using two filler materials: (i) Inconel 82 and (ii) P87. These samples were aged at 600°C for 2000h to accelerate high-temperature microstructural evolution seen in service conditions, before subjecting them to short-term (~1 month) creep tests. Surface strains were measured using digital image correlation (DIC) technique to extract creep strain rates at different locations within GTJs. Both the GTJs exhibited heterogeneous creep strain distribution. Creep strain accumulated in the FGHAZ of 2.25Cr-1Mo steel, similar to type IV failure associated with Cr-Mo steel weldments. Microstructure based creep model framework was developed to describe the discrete creep strain rates observed in various 2.25Cr-1Mo steel regions of GTJs.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Interdiffusion of Elements During Ultrasonic Additive Manufacturing

In this paper, we report evidence for enhanced elemental interdiffusion during ultrasonic additive manufacturing (UAM) across metal boundaries of copper-aluminum, nickel-gold, and nickel-gold-aluminum. The high solute interdiffusion measured by energy dispersive X-ray spectroscopy line scans is rationalized with calculated vacancy concentrations orders of magnitude larger than thermal equilibrium values. The above estimates are supported by existing knowledge related to defect physics and UAM thermal cycles. The observation of pronounced elemental mixing are evidence for the presence of enhanced non-equilibrium immiscible metal interdiffusion during UAM processing.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Investigating the Linear Thermal Expansion of Additively Manufactured Multi-Material Joining between Invar and Steel

This work investigated the linear thermal expansion properties of a multi-material specimen fabricated with Invar M93 and A36 steel. A sequence of tests was performed to investigate the viability of additively manufactured Invar M93 for lowering the coefficient of thermal expansion (CTE) in multi-material part tooling. Invar beads were additively manufactured on a steel base plate using a fiber laser system, and samples were taken from the steel, Invar, and the interface between the two materials. The CTE of the samples was measured between 40 °C and 150 °C using a thermomechanical analyzer, and the elemental composition was studied with energy dispersive X-ray spectroscopy. The CTE of samples taken from the steel and the interface remained comparable to that of A36 steel; however, deviations between the thermal expansion values were prevalent due to element diffusion in and around the heat-affected zone. The CTEs measured from the Invar bead were lower than those from the other sections with the largest and smallest thermal expansion values being 10.40 μm/m-K and 2.09 μm/m-K. In each of the sections, the largest CTE was measured from samples taken from the end of the weld beads. An additional test was performed to measure the aggregate expansion of multi-material tools. Invar beads were welded on an A36 steel plate. The invar was machined, and the sample was heated in an oven from 40 °C and 160 °C. Strain gauges were placed on the surface of the part and were used to analyze how the combined thermal expansions of the invar and steel would affect the thermal expansion on the surface of a tool. There were small deviations between the expansion values measured by gauges placed in different orientations, and the elongation of the sample was greatest along the dimension containing a larger percentage of steel. On average, the expansion of the machined Invar surface was 42% less than the expansion of the steel surface. The results of this work demonstrate that additively manufactured Invar can be utilized to decrease the CTE for multi-material part tooling.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Additive manufacturing methods using aluminum-rare earth alloys and products made using such methods

Described herein are additive manufacturing methods and products made using such methods. The alloy compositions described herein are specifically selected for the additive manufacturing methods and provide products that exhibit superior mechanical properties as compared to their cast counterparts. Using the compositions and methods described herein, products that do not exhibit substantial coarsening, such as at elevated temperatures, can be obtained. The products further exhibit uniform microstructures along the print axis, thus contributing to improved strength and performance. Additives also can be used in the alloys described herein.

36 MATERIALS SCIENCE↗