DOE OSTI2023

Contributions to the mechanistic understanding of the microstructural evolution in irradiated U-Mo dispersion fuel

Here, advanced microstructural characterization techniques, such as scanning electron microscopy (SEM) and scanning transmission electron microscopy - energy dispersive x-ray spectroscopy (STEM-EDS), were used to interpret the fuel microstructure evolution and fission products behavior in U-Mo dispersion fuel irradiated in the Advanced Test Reactor (ATR) as part of the European Mini-Plate Irradiation Experiment (EMPIrE) test. The larger as-fabricated fuel grain size achieved by heat-treating the U-Mo powder resulted in slower high burnup structure (HBS) development and reduced fission gas porosity. Slower HBS kinetics was observed at the fuel kernels’ periphery, which contained smaller and less fission gas bubbles at all fission densities (FDs) investigated and was attributed to a locally reduced damage density and fission products concentration, as corroborated with Monte Carlo simulations. The non-refined grains at the fuel kernel periphery hosted a perfectly ordered fission Gas Bubble Superlattice (GBS) up to 6.3 × 10 21 fissions/cm 3 . Nano-scale STEM-EDS analysis presented in this study provided useful information on the GBS characteristic morphology and evolution in U-Mo fuel. The concentration of fission gas in the GBS progressively increased with FD, pointing to an evolution of the nanobubble pressure status with irradiation. A possible connection between the GBS collapse and HBS onset is proposed for which there exists a threshold in the misorientation of the refined sub-grains above which the GBS stability during irradiation is no longer preserved, resulting in the GBS collapse.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2023

The effect of phosphorus on precipitation in irradiated reactor pressure vessel (RPV) steels

Embrittlement of light water reactor pressure vessels (RPV) steels by fast neutron irradiation may limit extended nuclear plant life. Embrittlement, which is manifested as increases in various indexes of a ductile to brittle transition temperatures (ΔT), is primarily due to hardening by nanoscale precipitates containing Cu, Ni, Mn, and Si, which form under irradiation. In addition to these elements, P has also been found to play a role in embrittlement. While only slightly enriched in the precipitates, hardening and embrittlement increase with trace P concentrations in low-Cu steels. Here, we characterize the individual and synergistic irradiation precipitation and hardening mechanisms in a series of RPV steels containing no to low-Cu and with systematic variations in Ni and P. In this study, the steels were irradiated to a fluence of ~ 1.38 x 10 20 n/cm 2 at ~ 292 °C in the UCSB ATR-2 experiment. In Cu-free medium and high-Ni RPV steels, atom probe tomography shows that P and Ni promotes precipitation of P-Mn-Si-Ni and Mn-Si-Ni precipitates, respectively. The precipitate microstructure correlates with the observed irradiation hardening.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Layer dissolution in accumulative roll bonded bulk Zr/Nb multilayers under heavy-ion irradiation

In this work, the heavy-ion irradiation behavior of bulk zirconium-niobium multilayered composites was investigated up to large doses. Multilayers with an average individual layer thicknesses ranging between 15 and 80 nm were synthesized by accumulative roll bonding technique. The irradiation was performed with a defocused 7 MeV Zr 2+ ion beam at 500 °C. The maximum dose achieved was ~145 dpa at the depth of ~1.5 μm from the irradiated surface. Sub-surface microstructural damage and the chemical redistribution were characterized by transmission electron microscopy and energy dispersive spectroscopy, respectively. Irrespective of the layer thicknesses, the irradiation condition caused layer instability and the extent of damage varied with the dose levels. Doses lesser than ~60 dpa caused layer fragmentation and greater than ~60 dpa resulted in layer dissolution. The chemical mixing of layers occur to a depth of ~1 μm, consuming multiple bi-layer periods. Despite the elevated irradiation temperature (500 °C) and a slightly positive heat of mixing (+6 kJ/mol), no phase separation was observed and single-phase was retained in the mixed region. The results demonstrate that chemical mixing was facilitated by the liquid phase miscibility of Zr and Nb, which propelled the interdiffusion within the thermal spikes towards mixing.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Helium-bubble-enhanced disordering of intermetallic phase under irradiation

Understanding and controlling phase transformations in metals and alloys under irradiation is vital to the design of irradiation-tolerant materials. The L1 2 -ordered intermetallic phase in nickel-based superalloys provides superior high-temperature mechanical properties and corrosion resistance. Here, we studied the order-disorder transformation kinetics of an L1 2 -structured gamma-prime phase in nickel-based superalloy Rene N4 under krypton ion irradiation and the effect of pre-implanted helium gas bubbles on the kinetics of phase transformation. Furthermore, the presence of pre-implanted helium gas bubbles significantly enhances the order-disorder transformation of L1 2 -structured gamma-prime phase under irradiation at 300 °C. The evolution of pre-implanted helium gas bubbles under irradiation implies that helium gas bubbles could effectively trap irradiation-induced vacancies and impede the reordering process of anti-site defects in gamma-prime phase.

36 MATERIALS SCIENCE↗