DOE OSTI2023

Microstructural Insights into Performance Loss of High-Voltage Spinel Cathodes for Lithium-ion Batteries

Spinel-structured LiNi x Mn 2-x O 4 (LNMO), with low-cost earth-abundant constituents, is a promising high-voltage cathode material for lithium-ion batteries. Even though extensive electrochemical investigations have been conducted on these materials, few studies have explored correlations between their loss in performance and associated changes in microstructure. Here, down to the atomic scale, the structural evolution of these materials is investigated upon the progressive cycling of lithium-ion cells. Transgranular cracking is revealed to be a key feature during cycling; this cracking is initiated at the particle surface and leads to the penetration of electrolytes along the crack path, thereby increasing particle exposure to the electrolyte. The lattice structure on the crack surface shows spatial variances, featuring a top layer of rock-salt, a sublayer of a Mn 3 O 4 -like arrangement, and then a mixed-cation region adjacent to the bulk lattice. The transgranular cracking, along with the emergence of local lattice distortion, becomes more evident with extended cycling. Further, phase transformation at primary particle surfaces and void formation through vacancy condensation is found in the cycled samples. All these features collectively contribute to the performance degradation of the battery cells during electrochemical cycling.

25 ENERGY STORAGE↗

DOE OSTI2023

Understanding and Mitigating the Dissolution and Delamination Issues Encountered with High-Voltage LiNi 0.5 Mn 1.5 O 4

In our initial study on the high-voltage 5 V cobalt-free spinel LiNi 0.5 Mn 1.5 O 4 (LNMO) cathode, we discovered a severe delamination issue in the laminates when cycled at a high upper cut-off voltage (UCV) of 4.95 V, especially when a large cell format was used. This delamination problem prompted us to investigate further by studying the transition metal (TM) dissolution mechanism of cobalt-free LNMO cathodes, and as a comparison, some cobalt-containing lithium nickel manganese cobalt oxides (NMC) cathodes, as the leachates from the soaking experiment might be the culprit for the delamination. Unlike other previous reports, we are interested in the intrinsic stability of the cathode in the presence of a baseline Gen2 electrolyte consisting of 1.2 M of LiPF 6 in ethylene carbonate/ethyl methyl carbonate (EC/EMC), similar to a storage condition. The electrode laminates (transition metal oxides, transition metal oxides, TMOs, coated on an Al current collector with a loading level of around 2.5 mAh/cm 2 ) or the TMO powders (pure commercial quality spinel LNMO, NMC, etc.) were stored in the baseline solution, and the transition metal dissolution was studied through nuclear magnetic resonance, such as 1 H NMR, 19 F NMR, scanning electron microscope (SEM), X-ray photoelectron spectroscopy (XPS) and inductively coupled plasma mass spectrometry (ICP-MS). Significant electrolyte decomposition was observed and could be the cause that leads to the TM dissolution of LNMO. To address this TM dissolution, additives were introduced into the baseline electrolyte, effectively alleviating the issue of TM dissolution. The results suggest that the observed delamination is caused by electrolyte decompositions that lead to etching, and additives such as lithium difluorooxalato borate and p-toluenesulfonyl isocyanate can alleviate this issue by forming a firm cathode electrolyte interface. This study provides a new perspective on cell degradation induced by electrode/electrolyte interactions under storage conditions.

25 ENERGY STORAGE↗

DOE OSTI2022

Visualizing electrode assembly movement and lithiation heterogeneity in lithium-metal batteries using operando energy dispersive X-ray diffraction

There is renewed interest in Li-metal anodes in order to increase the energy density of battery cells. Here, we demonstrate an operando X-ray crystallography method to visualize lithiation gradients and electrode assembly movement during electrochemical cycling of a Li-metal cell containing a Ni-Mn-Co layered oxide cathode (NMC811). During charge, deposition of Li + ions from the cathode increases the Li foil thickness; during discharge, the thickness decreases as Li + ions are stripped off the foil. Additionally, the resulting periodic movement is observed through tracking of Bragg peaks from the ordered phases of the cathode and separator. In addition to this 3.6 μm/mAh displacement, continuous mossy Li build-up on the anode causes an irreversible drift of the assembly, which is similar to 11.3 μm/cycle. Furthermore, our data indicate significant lithiation gradients in the NMC811 cathode during the oxide relithiation, which is not observed during the delithiation.

25 ENERGY STORAGE↗