Colloidal InAs Quantum Dot-Based Infrared Optoelectronics Enabled by Universal Dual-Ligand Passivation

Solution-processed low-bandgap semiconductors are crucial to next-generation infrared (IR) detection for various applications, such as autonomous driving, virtual reality, recognitions, and quantum communications. In particular, III–V group colloidal quantum dots (CQDs) are interesting as nontoxic bandgap-tunable materials and suitable for IR absorbers; however, the device performance is still lower than that of Pb-based devices. Herein, a universal surface-passivation method of InAs CQDs enabled by intermediate phase transfer (IPT), a preliminary process that exchanges native ligands with aromatic ligands on the CQD surface is presented. IPT yields highly stable CQD ink. In particular, desirable surface ligands with various reactivities can be obtained by dispersing them in green solvents. Furthermore, CQD near-infrared (NIR) photodetectors are demonstrated using solution processes. Careful surface ligand control via IPT is revealed that enables the modulation of surface-mediated photomultiplication, resulting in a notable gain control up to ≈10 with a fast rise/fall response time (≈12/36 ns). Considering the figure of merit (FOM), EQE versus response time (or –3 dB bandwidth), the optimal CQD photodiode yields one of the highest FOMs among all previously reported solution-processed nontoxic semiconductors comprising organics, perovskites, and CQDs in the NIR wavelength range.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2022

Fast Near-Infrared Photodetection Using III–V Colloidal Quantum Dots

Colloidal quantum dots (CQDs) are promising materials for infrared (IR) light detection due to their tunable bandgap and their solution processing; however, to date, the time response of CQD IR photodiodes is inferior to that provided by Si and InGaAs. It is reasoned that the high permittivity of II–VI CQDs leads to slow charge extraction due to screening and capacitance, whereas III–Vs—if their surface chemistry can be mastered—offer a low permittivity and thus increase potential for high-speed operation. In initial studies, it is found that the covalent character in indium arsenide (InAs) leads to imbalanced charge transport, the result of unpassivated surfaces, and uncontrolled heavy doping. Surface management using amphoteric ligand coordination is reported, and it is found that the approach addresses simultaneously the In and As surface dangling bonds. The new InAs CQD solids combine high mobility (0.04 cm 2 V -1 s -1 ) with a 4× reduction in permittivity compared to PbS CQDs. Finally, the resulting photodiodes achieve a response time faster than 2 ns—the fastest photodiode among previously reported CQD photodiodes—combined with an external quantum efficiency (EQE) of 30% at 940 nm.

36 MATERIALS SCIENCE↗