DOE OSTI2023

Microstructure development in a cold worked SRF Nb sheet undergoing 700°C-900°C/3h heat treatments.

Bulk Nb for TESLA shaped SRF cavities is a mature technology, with high gradient (>35 MV/m) and high Q cavities (>1010, ~2K) routinely fabricated. Significant advances are in order to push Q?s to 1011 (~2K), and involve modifications to the sub-surface Nb layers by impurity doping (N, O). In order to achieve the lowest surface resistance any trapped flux needs to be expelled for cavities to reach high Q?s. There is clear evidence that cavities fabricated from polycrystalline sheets meeting current specifications require higher temperatures beyond 800oC leads to better flux expulsion, and hence improves Q. Recently, cavities fabricated with a non-traditional Nb sheet with initial cold work due to cold rolling expelled flux better after 800°C/3h heat treatment than cavities fabricated using fine-grain polycrystalline Nb sheets. Here, we analyze the microstructure development in Nb from the vendor supplied cold work non-annealed sheet that was fabricated into an SRF cavity as a function of heat treatment building upon the methodology development to analyze microstructure being developed by the FSU-MSU-UT-Austin- JLAB collaboration. The results indicate correlation between full recrystallization and better flux expulsion.

Balachandran, S.↗
DOE OSTI2023

Effect of Strain on the Resistivity and Thermal Conductivity of High Purity Niobium

High purity niobium (Nb) is a technologically important material for large-scale accelerator and nano-scale quantum computing applications in microwave frequency range. The high thermal conductivity and low resistivity of Nb are critical to the high performance at temperature range of 0.01–4.0 K. The presence of interstitials such as O, N, H, and C act as scattering centers and alter the mean free path, reducing resistivity and thermal conductivity, and contributing significantly to Nb's thermal performance for temperatures of 2.0 K and above. The residual resistivity ratio (RRR), defined as the ratio of the normal state resistivity at 300 K to that at 4.2 K (Nb, T c = 9.2 K), is an accepted direct estimate of the impurity content of fully recrystallized Nb. Complete re-crystallization of Nb is challenging unless very high temperatures are employed, which is often impractical, hence, in practice, dislocation and dislocation structures impact the thermal performance of Nb due to strong phonon scattering contributions. Furthermore, this paper reports on the degradation of thermal conductivity and RRR of high purity Nb large grain, single crystal with fixed impurity, varying strain, and dislocation content levels. Experimental thermal conductivity data fits the Boltzmann transport equation incorporating dislocation density.

36 MATERIALS SCIENCE↗
DOE OSTI2022

MAGNETIC FLUX EXPULSION IN SUPERCONDUCTING RADIO-FREQUENCY NIOBIUM CAVITIES MADE FROM COLD WORKED NIOBIUM

Trapped residual magnetic field during the cool down of superconducting radio frequency (SRF) cavities is one of the primary sources of RF residual losses leading to lower quality factor. Historically, SRF cavities have been fabricated from high purity fine grain niobium with grain size ~50 to 100 µm as well as large grain with grain size of the order of few centimeters. Non-uniform recrystallization of fine-grain Nb cavities after the post fabrication heat treatment leads to higher flux trapping during the cool down, and hence the lower quality factor. We fabricated two 1.3 GHz single cell cavities from cold-worked niobium from different vendors and processed along with cavities made from SRF grade Nb. The flux expulsion and flux trapping sensitivity were measured after successive heat treatments in the range 800 to 1000°C. The flux expulsion from cold-worked fine-grain Nb cavities improves after 800°C/3h heat treatments and it becomes similar to that of standard fine-grain Nb cavities when the heat treatment temperature is higher than 900°C.

Khanal, B. D.↗
DOE OSTI2022

MAGNETIC FLUX EXPULSION IN SUPERCONDUCTING RADIO-FREQUENCY NIOBIUM CAVITIES MADE FROM COLD WORKED NIOBIUM

Trapped residual magnetic field during the cool down of superconducting radio frequency (SRF) cavities is one of the primary sources of RF residual losses leading to lower quality factor. Historically, SRF cavities have been fabricated from high purity fine grain niobium with grain size ~50 to 100 µm as well as large grain with grain size of the order of few centimeters. Non-uniform recrystallization of fine-grain Nb cavities after the post fabrication heat treatment leads to higher flux trapping during the cool down, and hence the lower quality factor. We fabricated two 1.3 GHz single cell cavities from cold-worked niobium from different vendors and processed along with cavities made from SRF grade Nb. The flux expulsion and flux trapping sensitivity were measured after successive heat treatments in the range 800 to 1000°C. The flux expulsion from cold-worked fine-grain Nb cavities improves after 800°C/3h heat treatments and it becomes similar to that of standard fine-grain Nb cavities when the heat treatment temperature is higher than 900°C.

Khanal, B. D.↗