NASA NTRS1973

The development and production of thermo-mechanically forged tool steel spur gears

A development program to establish the feasibility and applicability of high energy rate forging procedures to tool steel spur gears was performed. Included in the study were relatively standard forging procedures as well as a thermo-mechanical process termed ausforming. The subject gear configuration utilized was essentially a standard spur gear having 28 teeth, a pitch diameter of 3.5 inches and a diametral pitch of 8. Initially it had been planned to use a high contact ratio gear design, however, a comprehensive evaluation indicated that severe forging problems would be encountered as a result of the extremely small teeth required by this type of design. The forging studies were successful in achieving gear blanks having integrally formed teeth using both standard and thermo-mechanical forging procedures.

Bamberger, E. N.↗
NASA NTRS1973

Evaluation of load-life relation with ball bearings at 500 F

A survey of the literature suggests that a stress-life exponent of approximately 12 is typical of vacuum-processed steels for ball bearings rather than the exponent of 9 which has been generally accepted by the bearing industry and bearing users. Tests run with vacuum-degassed AISI 52100 balls in the five-ball fatigue tester at four maximum Hertz stress levels in the range from 650,000 to 875,000 psi showed good agreement with the literature. However, tests run with consumable-electrode vacuum melted AISI M-50 steel angular-contact ball bearings at 500 F at three thrust loads did not show significant deviation from the accepted ninth power stress-life relation.

Parker, R. J.↗
NASA NTRS1973

Parametric study of the lubrication of thrust loaded 120-mm bore ball bearings to 3 million DN

A parametric study was performed with 120-mm bore angular-contact ball bearings under varying thrust loads, bearing and lubricant temperatures, and cooling and lubricant flow rates. Contact angles were nominally 20 and 24 deg with bearing speeds to 3 million DN. Endurance tests were run at 3 million DN and a temperature of 492 K (425 F) with 10 bearings having a nominal 24 deg contact angle at a thrust load of 22241 N (5000 lb). Bearing operating temperature, differences in temperatures between the inner and outer races, and bearing power consumption can be tuned to any desirable operating requirement by varying 4 parameters. These parameters are outer-race cooling, inner-race cooling, lubricant flow to the inner race, and oil inlet temperature. Preliminary endurance tests at 3 million DN and 492 K (425 F) indicate that long term bearing operation can be achieved with a high degree of reliability.

Signer, H.↗
NASA NTRS1972

Advanced airbreathing engine lubricants study with a tetraester fluid and a synthetic paraffinic oil at 492 K (425 F)

Groups of 120-mm-bore angular-contact ball bearings made from AISI M-50 steel were fatigue tested with a tetraester and a synthetic paraffinic oil at a bearing temperature of 492 K (425 F) in an air environment. Bearing life exceeded AFBMA-predicted (catalog) life by factors in excess of 4 and 10 for the tetraester and synthetic paraffinic fluids, respectively. The final viscosities after 500 hours of operation were 14 and 6 times the initial values, respectively. During the same time period, when the test oil is replaced at a rate approximating the replenishment rate in actual commerical engine usage, no significant increase in lubricant viscosity with time was observed.

Zaretsky, E. V.↗