Publications and source records attributed to Banerjee, Rajarshi.

16 records

DOE OSTI2023

Microstructure and Temperature Dependent Indentation Response of Additively Manufactured Precipitation-Strengthened Al 0.3 Ti 0.2 Co 0.7 CrFeNi 1.7 High Entropy Alloy

The temperature-dependent [from room temperature (RT) to 500°C] nanoindentation behavior of a precipitation-strengthened Al 0.3 Ti 0.2 Co 0.7 CrFeNi 1.7 high-entropy alloy (HEA) processed via two different additive manufacturing (AM) techniques was investigated in the as-deposited and annealed conditions. The hierarchically heterogeneous microstructures were achieved via simple one-step annealing treatments, exploiting the residual stresses in the AM-processed HEA to partially recrystallize the microstructure, performed remarkably better than the nearly homogeneous microstructures in the as-deposited state. Further, the one-step annealed conditions revealed < 6.6% reduction in hardness values at 500°C compared to RT, while the as-deposited conditions showed a > 18% reduction in the hardness. The one-step annealed conditions also exhibited significantly higher hardness than the as-deposited conditions owing to their L1 2 -strengthened FCC microstructures. Furthermore, serrated yielding or the Portevin-Le Chatlier effect indicative of microstructural instability was observed during nanoindentation deformation (at 500°C) for the as-deposited conditions but not for the one-step annealed conditions. This, therefore, signifies the robustness of the hierarchically heterogeneous microstructures at elevated temperatures presenting a strong avenue for tuning the HEAs for future nuclear reactor applications.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Solid-state reaction mediated microstructural evolution in a spark plasma sintered in situ Ti–B 4 C composite

For this study, a novel porosity-free in situ Ti–B 4 C composite was fabricated via spark plasma sintering (SPS). Detailed analysis of the phase evolution, coupling results from XRM, XRD and SEM-EBSD-EDS, indicate that primarily TiB 2 precipitates formed due to the in-situ reactions between the boron-carbide and titanium powders. The precipitation of TiB 2 resulted in the formation of a graphitic C-rich thin layer circumscribing the partially reacted B 4 C particles. Further progression of the in-situ reaction leads to the out-diffusion of the excess carbon from the B 4 C particles, across the graphite and TiB 2 phases, forming TiC upon reacting with the titanium matrix. Therefore, the final microstructure primarily consisted of TiB 2 , TiC, and partially reacted B 4 C phases, with small amounts of TiB, α-Ti, and graphite. Furthermore, the microstructure in these SPS processed in situ composites appeared to be the product of a solid-state Ti–B 4 C diffusion couple, substantially different from their fusion-based additively manufactured counterparts. Nano-indentation tests revealed a remarkably high average hardness of ~25 GPa for this SPS-processed Ti–B 4 C composite and comparable (with literature) phase-specific hardness and modulus values for the constituent TiB 2 , TiC, and B 4 C phases.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Influence of energy density on the microstructure, growth orientation, and anisotropy of magnetic properties in additively manufactured Fe-3.8wt%Si transformer steels

Fe-3.8wt%Si transformer steels were processed using two different additive manufacturing (AM) techniques, laser powder bed fusion (LPBF) and directed energy deposition (DED). While the LPBF processed samples exhibited a strong <001> orientation of the BCC grains along the build axis, the DED processed samples exhibited a randomized texture along the build axis. DED processed samples showed substantially coarser columnar grains as compared to their LPBF counterparts. Here, the columnar grains exhibited a substantial number of low-angle sub-grain boundaries. All samples exhibited very good soft magnetic properties, with saturation magnetization (M s ) values ranging from 205 - 232 emu/gm, and coercivity (H c ) values ranging from 1.2 – 4.2 Oe. The Coercivity (H c ) values were significantly lower when the magnetic field was applied parallel to the build axis, as compared to being perpendicular, which can be rationalized based on the columnar nature of the grains, resulting in a higher number density of grain boundaries in case of the field applied perpendicular to the build axis.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Exceptional enhancement of mechanical properties in high-entropy alloys via thermodynamically guided local chemical ordering

Understanding the local chemical ordering propensity in random solid solutions, and tailoring its strength, can guide the design and discovery of complex, paradigm-shifting multicomponent alloys. First, we present a simple thermodynamic framework, based solely on binary enthalpies of mixing, to select optimal alloying elements to control the nature and extent of chemical ordering in high-entropy alloys (HEAs). Next, we couple high-resolution electron microscopy, atom probe tomography, hybrid Monte-Carlo, special quasirandom structures, and density functional theory calculations to demonstrate how controlled additions of Al and Ti and subsequent annealing drive chemical ordering in nearly random equiatomic face-centered cubic CoFeNi solid solution. We establish that short-range ordered domains, the precursors of long-range ordered precipitates, inform mechanical properties. Specifically, a progressively increasing local order boosts the tensile yield strengths of the parent CoFeNi alloy by a factor of four while also substantially improving ductility, which breaks the so-called strength–ductility paradox. Finally, we validate the generality of our approach by predicting and demonstrating that controlled additions of Al, which has large negative enthalpies of mixing with the constituent elements of another nearly random body-centered cubic refractory NbTaTi HEA, also introduces chemical ordering and enhances mechanical properties.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2022

High-temperature deformation mechanisms in a BCC+B2 refractory complex concentrated alloy

The current study reports the analysis of the deformation mechanisms at 600 °C in a two-phase, BCC+B2, refractory complex concentrated alloy (RCCA) Al 0.5 NbTa 0.8 Ti 1.5 V 0.2 Zr. At this temperature, the alloy microstructure is unstable and dynamic coarsening of B2 precipitates is evidenced during the mechanical testing. After true plastic strain of 0.030 at strain rate of 10 -4 s -1 , the deformation becomes highly localized in wavy bands reflecting the profusion of cross-slip. Scanning transmission electron microscopy (STEM) observations highlight the presence of paired a/2$\langle$111$\rangle$ dislocations that shear the B2 precipitates in a cooperative process. Additionally, some chemical segregation effect is observed along the narrow dislocation bands likely induced to decrease the antiphase boundary (APB) energy of the system.

ordering↗

DOE OSTI2021

High Density of Strong yet Deformable Intermetallic Nanorods Leads to an Excellent Room Temperature Strength-Ductility Combination in a High Entropy Alloy

This paper introduces a new microstructural template for high entropy alloys (HEAs), where the face centered cubic (FCC) complex concentrated solid solution is reinforced with a high density of strong, yet deformable, nanorods of an ordered multi-component intermetallic L12 compound. Thermodynamic modeling has been employed to design this HEA with a large L12 volume fraction. Thermo-mechanical processing by isothermal annealing of the conventionally processed bulk cold-rolled alloy directly at precipitation temperatures, has been applied to produce a high density of uniformly distributed L12 nanorods within refined FCC grains, resulting from concomitant recrystallization and discontinuous precipitation processes. The nanorod morphology of the discontinuous L12 product has been established from three-dimensional atom probe tomography. The refined grains result in a complete coverage of the microstructure with discontinuously precipitated intermetallic nanorods. This nanorod strengthened HEA exhibits an exceptionally high room temperature yield strength of ~1630 MPa, good tensile ductility of ~15%, and an ultimate tensile strength of ~1720 MPa. Furthermore, a single L12 phase alloy, melted based on the precipitate composition in the two-phase FCC + L12 HEA, exhibits very high compressive deformability and strain hardenability, unusual for ordered intermetallic compounds. These results open a new strategy for design of fine-grained microstructures strengthened via ordered intermetallic phases, exploiting the beneficial effects of discontinuous precipitation, for achieving very high room temperature tensile strengths while maintaining good ductility.

Gwalani, Bharat↗

DOE OSTI2021

Insights into Defect-Mediated Nucleation of the Equilibrium B2 Phase in Face-Centered Cubic High-Entropy Alloys

A fine scale second phase distribution is important for strengthening metallic materials. High precipitate density is often difficult to achieve due to sluggish precipitation kinetics and limited nucleation sites. Based on the CALPHAD predictions, transition element-based complex concentrated alloys (CCAs)/ High Entropy Alloys (HEAs), have a highly stable face-centered cubic (FCC) phase and intermetallic B2 phase. The precipitation of the strengthening B2 phase is often limited to low fractions in these alloys due to a high nucleation barrier in the FCC matrix. Here, by illustrating in three different alloys, we present a defect mediated nucleation of a high fraction equilibrium B2 phase. The degree of cold work is used to manipulate the phase fraction, morphology, and distribution of B2 precipitates. Our approach synergistically improves the strength and ductility of these alloys and is widely applicable to many other complex alloys.

Sharma, Abhishek↗

DOE OSTI2021

Ordering effects on deformation substructures and strain hardening behavior of a CrCoNi based medium entropy alloy

Here, a CrCoNi based medium entropy alloy with small additions of Ti, Al and Nb (denoted as (CrCoNi) 93 Al 4 Ti 2 Nb) in the as-quenched condition, exhibits tensile properties comparable to those of the equiatomic CrCoNi alloy at room temperature. Dark field transmission electron microscopy (TEM), atomic resolution high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) together with atom probe tomography (APT) show that spatially-localized long range ordering (LRO) L1 2 domains exist in this alloy. The evolution of deformation substructure with plastic deformation in this alloy was characterized using electron backscatter diffraction (EBSD), electron channeling contrast imaging (ECCI) and STEM based techniques including the recently developed weak beam dark field STEM imaging. Plastic deformation occurs by the slip of a/2<110>dislocations, which are narrowly dissociated into Shockley partial dislocations on {111} slip planes. Their dissociation distances in the (CrCoNi) 93 Al 4 Ti 2 Nb alloy are much smaller than the widths of the corresponding partials in the equiatomic CrCoNi alloy due to one or more of the minor alloying elements (Al, Ti, Nb). Dislocation slip in this alloy has a pronounced planar character. The leading dislocations in slip bands glide as pairs due to the existence of LRO domains. Multipoles were formed through the slip of dislocations with opposite signs on adjacent {111} slip planes. Those multipoles serve as building blocks for the formation of subgrain structures consisting of fine slip bands. The distances between slip bands were continuously refined during plastic deformation and dynamic refinement of slip bands plays a crucial role in strain hardening. The effects of LRO domains on planar dislocation slip, the deactivation of deformation twinning and strain hardening of this alloy are discussed.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Influence of fine-scale B2 precipitation on dynamic compression and wear properties in hypo-eutectic Al0.5CoCrFeNi high-entropy alloy

The near equiatomic high-entropy alloys based on Al, Co, Cr, Fe, Ni have provided a novel microstructural template for alloy design. The face-centered cubic (FCC) matrix strengthened by body-centered cubic (BCC) based ordered B2 precipitates can be used to develop a new generation of precipitation strengthened alloys. The present study focuses on an Al0.5CoCrFeNi hypo-eutectic alloy consisting of an as-solidified FCC+B2 microstructure. Guided by solution thermodynamic modeling, this alloy has been isothermally aged for solid-state precipitation of a high fraction of fine-scale intragranular B2 particles. The dynamic compressive strength, hardness, and sliding wear response of the alloy as a function of B2 phase fraction is examined. The flow stress at 0.02% true strain increased from ~ 670 MPa to ~1350 (102%) MPa, the ultimate compressive strength increased from ~1160 MPa to 1500 MPa (20%), and the wear resistance increased more than 5 times with progressively increasing phase fraction of B2 precipitates.

Gwalani, Bharat↗

DOE OSTI2021

Ordering-mediated local nano-clustering results in unusually large Hall-Petch strengthening coefficients in high entropy alloys

This paper reports a dramatic increase in the grain boundary strengthening or Hall-Petch coefficient, K, by systematically investigating the effect of Al addition on tensile yield strength in CoFeNi and CoCrFeNi high entropy alloys (HEAs) or complex concentrated alloys (CCAs). Additionally, detailed atom probe tomography (APT) revealed a high number density of Ni-Al rich nano-clusters in the Al 0.3 CoFeNi and Al 0.3 CoCrFeNi HEAs/CCAs, which can be rationalized based on the strong chemical ordering tendency between these elements. Consequently, the huge increase in K value can be attributed to the additional stress required for overcoming coherency strain fields arising from these nano-clusters.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Engineering Multi-scale B2 Precipitation in a Heterogeneous FCC Based Microstructure to Enhance the Mechanical Properties of a Al0.5Co1.5CrFeNi1.5 High Entropy Alloy

While ordered L12 or gamma prime precipitates in face centered cubic (FCC) based microstructures have been extensively used for strengthening Nickel or Cobalt base superalloys, and more recently in high entropy alloys (HEAs) or complex concentrated alloys (CCAs), the possibility of exploiting ordered B2 precipitates in FCC-based systems has been relatively less investigated. The present study shows the propensity of developing a heterogeneous microstructure, consisting of two different distributions of FCC grain sizes, and two different size scales of B2 precipitates, within an FCC-based Al0.5Co1.5CrFeNi1.5 HEA/CCA. This alloy composition has been designed using solution thermodynamics-based modeling such that it has a high phase fraction and solvus temperature of the B2 phase. The resulting heterogenous microstructure exhibited an approximately 400% increase in yield strength with respect to the single-phase FCC solid solution condition of the same alloy while maintaining very good tensile ductility ~20 %.

Dasari, Sriswaroop↗

DOE OSTI2020

Engineering transformation pathways in an Al 0.3 CoFeNi complex concentrated alloy leads to excellent strength–ductility combination

Guided by thermodynamic modeling, engineering phase transformation pathways via thermo-mechanical processing, in a complex concentrated alloy/high entropy alloy (HEA) of composition Al 0.3 CoFeNi, lead to a novel multi-scale microstructure consisting of fine-scale FCC + L1 2 grains mixed with B2 + BCC grains. The two-step pathway comprises initial decomposition of the parent single-phase FCC to form a fine-grained FCC + B2 microstructure, which further decomposes in the second step into the complex four-phase mixture, exhibiting an excellent combination of tensile yield stress of ~1490 MPa, ultimate tensile strength of ~1663 MPa, with a good ductility of ~12% at room temperature. This paper reports a novel multi-phase microstructure in a HEA/CCA similar to the microstructure observed in dual-phase stainless steel. This report exemplifies the novelty of HEA/CCA compositional space.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Influence of non-magnetic Cu on enhancing the low temperature magnetic properties and Curie temperature of FeCoNiCrCu(x) high entropy alloys

The microstructure and magnetic properties of three face-centered cubic (FCC) FeCoNiCrCu(x) high entropy alloys (HEAs) (x=0, 0.5, 1) are investigated. Interestingly, addition of the nonmagnetic element Cu to FeCoNiCr HEA is found to enhance exchange interactions and low temperature saturation magnetization. The paramagnetic to ferromagnetic Curie transition temperature increases from 85 K for FeCoNiCr to 118 K for FeCoNiCrCu. This is counterintuitive since Cu is nonmagnetic; however, atom probe tomography revealed Cu rich clusters containing 5 at% Ni and 1 at% each of Fe, Co, Cr, within FCC matrix, these clusters altered the matrix composition and consequently its magnetic properties.

Chaudhary, Varun↗

DOE OSTI2020

Dynamic Shear Deformation of a Precipitation Hardened Al 0.7 CoCrFeNi Eutectic High-Entropy Alloy Using Hat-Shaped Specimen Geometry

Lamellar eutectic structure in Al 0.7 CoCrFeNi high-entropy alloy (HEA) is emerging as a promising candidate for structural applications because of its high strength-ductility combination. The alloy consists of a fine-scale lamellar fcc + B2 microstructure with high flow stresses > 1300 MPa under quasi-static tensile deformation and >10% ductility. The response to shear loading was not investigated so far. This is the first report on the shear deformation of a eutectic structured HEA and effect of precipitation on shear deformation. A split-Hopkinson pressure bar (SHPB) was used to compress the hat-shaped specimens to study the local dynamic shear response of the alloy. The change in the width of shear bands with respect to precipitation and deformation rates was studied. The precipitation of L1 2 phase did not delay the formation of adiabatic shear bands (ASB) or affect the ASB width significantly, however, the deformed region around ASB, consisting of high density of twins in fcc phase, was reduced from 80 μm to 20 μm in the stronger precipitation strengthened condition. We observe dynamic recrystallization of grains within ASBs and local mechanical response of individual eutectic lamellae before and after shear deformation and within the shear bands was examined using nano-indentation.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Hierarchical Eutectoid Nano-lamellar Decomposition in an Al 0.3 CoFeNi Complex Concentrated Alloy

This paper reports a novel eutectoid nano-lamellar (FCC + L1 2 )/(BCC + B2) microstructure that has been discovered in a relatively simple Al 0.3 CoFeNi high entropy alloy (HEA) or complex concentrated alloy (CCA). This novel eutectoid nano-lamellar microstructure presumably results from the complex interplay between Al-mediated lattice distortion (due to its larger atomic radius) in a face-centered cubic (FCC) CoFeNi solid solution, and a chemical ordering tendency leading to precipitation of ordered phases such as L1 2 and B2. This eutectoid microstructure is a result of solid-state decomposition of the FCC matrix and therefore distinct from the commonly reported eutectic microstructure in HEAs which results from solidification. This novel nano-lamellar microstructure exhibits a tensile yield strength of 1074 MPa with a reasonable ductility of 8%. The same alloy can be tuned to form a more damage-tolerant FCC + B2 microstructure, retaining high tensile yield stress (~900 MPa) with appreciable tensile ductility (>20%), via annealing at 700 °C. Such tunability of microstructures with dramatically different mechanical properties can be effectively engineered in the same CCA, by exploiting the complex interplay between ordering tendencies and lattice distortion.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Phase Inversion in a Two-phase, BCC+B2, Refractory High Entropy Alloy

A phenomenon of "phase inversion", presumably the first ever experimental evidence in metallic alloys, is shown in a refractory high entropy alloy (RHEA), Al0.5NbTa0.8Ti1.5V0.2Zr. Phase inversion in crystalline solid systems is driven by the differences in elastic modulus of the two phases. Quenching from a high-temperature single phase field, the RHEA exhibits a co-continuous mixture of a disordered BCC and an ordered B2 phase, that upon isothermal annealing at 600°C develops via spinodal decomposition into a continuous B2 matrix with discrete cuboidal BCC precipitates aligned along the <001> directions. Longer term annealing at 600°C results in the development of necking constrictions along the B2 channels, eventually pinching-off these channels and making the BCC phase continuous with discrete B2 precipitates. This inversion the process can be related to the simultaneous operation of two processes:(i) spheroidization of the initially discrete cuboidal BCC precipitates driven by a reduction in the total interface energy and (ii) an increase in the stiffness of the B2 phase, relative to the BCC phase, due to chemical composition changes during annealing, forcing the B2 regions to become discrete driven by the reduction in the total elastic strain energy.

Soni, Vishal↗