7 records

DOE OSTI2023

Synthesis of Pt 3 Zn 1 and Pt 1 Zn 1 intermetallic nanocatalysts for dehydrogenation of ethane

Pt 3 Zn 1 and Pt 1 Zn 1 intermetallic nanoparticles supported on SiO 2 were synthesized by combining atomic layer deposition (ALD) of ZnO, incipient wetness impregnation (IWI) of Pt, and appropriate hydrogen reduction. Here, the formation of Pt 1 Zn 1 and Pt 3 Zn 1 intermetallic nanoparticles was observed by both X-ray diffraction (XRD) and synchrotron X-ray absorption spectroscopy (XAS). STEM images showed that the 2–3 nm Pt-based intermetallic nanoparticles were uniformly dispersed on a SiO 2 support. The relationships between Pt–Zn intermetallic phases and synthesis conditions were established. In situ XAS measurements at Pt L 3 and Zn K edges during hydrogen reduction provided a detailed image of surface species evolution. Owing to a combined electronic and geometric effect, Pt 1 Zn 1 exhibited much higher reactivity and stability than Pt 3 Zn 1 and Pt in both the direct dehydrogenation and oxidative dehydrogenation of ethane to ethylene reactions.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

NASA NTRS2014

Thermophysical Property Measurements of Silicon-Transition Metal Alloys

Metals and metallic alloys often have high melting temperatures and highly reactive liquids. Processing reactive liquids in containers can result in significant contamination and limited undercooling. This is particularly true for molten silicon and it alloys. Silicon is commonly termed "the universal solvent". The viscosity, surface tension, and density of several silicon‐transition metal alloys were determined using the Electrostatic Levitator system at the Marshall Space Flight Center. The temperature dependence of the viscosity followed an Arrhenius dependence, and the surface tension followed a linear temperature dependence. The density of the melts, including the undercooled region, showed a linear behavior as well. Viscosity and surface tension values were obtain for several of the alloys in the undercooled region.

Banish, R. Michael↗

NASA NTRS2003

Thermophysical Properties of Te-based II-VI Semiconductors: Reduced Algorithms for Thermal Diffusivity Determination

This paper presents methodologies for measuring the thermal diffusivity using the difference between temperatures measured at two, essentially independent, locations. A heat pulse is applied for an arbitrary time to one region of the sample; either the inner core or the outer wall. Temperature changes are then monitored versus time. The thermal diffusivity is calculated from the temperature difference versus time. No initial conditions are used directly in the final results.

Banish, R. Michael↗

NASA NTRS2003

Convective Effects During Diffusivity Measurements in Liquids with An Applied Magnetic Field

Convective contamination of self-diffusion experiments with an applied magnetic field is considered using a two-dimensional axisymmetric model. Constant, uniform, and an additional non-uniform heat fluxes are imposed along the sidewall of the cylinder while constant heat loss occurs through the top and bottom. In this model, due to a very small thermal Peclet number, convective heat transfer is neglected, and the flow is steady and inertialess. Time-dependent concentration is solved for various values of the mass Peclet number, Pe(sub m), (the ratio between the convective transport rate and the diffusive transport rate) and different magnetic field strengths represented by the Hartmann number Ha. Normalized values of these diffusivities vs. effective Pe(sub m) are presented for different imposed temperature profiles. In all cases, the diffusivity value obtained through the simulated measurement increases as the effective Pe(sub m) increases. The numerical results suggest that an additional periodic flux, or hot and cold spots, can significantly decrease the convective contamination in our geometry.

Khine, Yu Yu↗

NASA NTRS1998

Temperature Dependence of Diffusivities in Liquid Elements (LMD)

This research was to advance the understanding of diffusion mechanisms in liquid metals and alloys through accurate diffusivity measurements over a wide range of temperatures, including the proximity of the materials melting points. Specifically, it was driven towards developing a methodology (and subsequent flight hardware) to enable several diffusion coefficient measurements (i.e., at several different temperatures) to be performed using a single sample. The Liquid Metal Diffusion (LMD) was funded as a Flight Definition Project in February 1993 in response to NRA 91-OSSA-20 (Microgravity Science and Applications Division). The Science Concept Review for LAID was held during April 1994. In January 1995 we were informed that we had failed this review and the project was change to ground-based activities only. A new proposal was submitted for the next NRA addressing the panels concerns. As part of NASA's Risk Mitigation program, a scaled-down version of the hardware was funded in July of 1995 for a flight opportunity utilizing experiment on the Microgravity Isolation Mount. This experiment was to determine the self-diffusivity of indium at 185 C. The LMD was transferred to the Mir Space Station in STS-81 and returned on STS-84 (January - May 1997). Three, out of five, self-diffusion data sets were returned. A description of this experiment/hardware is included below. This summary is only intended to give the reader an overview of the results obtained for the tasks outlined in the original proposal. Research that was not published is explained in more detail. At the end of this report is a list of refereed publications and invited talks that were given as a result of this work. The reader is directed to these for further details. Attachment: Real-time diffusivity measurements in liquids at several temperatures with one sample, On the insensitivity of liquid diffusivity measurements to deviations from 1D transport, and Numerical simulations of the convective contamination of diffusivity measurements in liquids.

Banish, R. Michael↗

NASA NTRS1993

Temperature dependence of diffusivities, preliminary definition phase

During the six months definition phase of the instrument development program, research personnel at the Center for Microgravity and Materials Research of the University of Alabama in Huntsville (UAH) were to furnish all of the necessary labor, services, materials, and facilities necessary to provide science requirement definition, initiate hardware development activities, requirements and timetable for integration and experimental accommodation of the GAS payload into the Shuttle cargo bay and an updated ground-based research flight program proposal consistent with the NRA selection letter. These activities were to be accomplished in parallel and consistent with the necessary research and development work toward the accomplishment of the overall objectives of the selected proposal.

Rosenberger, Franz↗

NASA NTRS1988

Vapor concentration measurement with photothermal deflectometry

Theoretical and experimental results for using the photothermal deflection technique to measure vapor species concentration, while minimizing the disturbance of the transport (material) parameters due to vapor heating, are developed and described. In contrast to common practice, the above constraints require using a pump-beam duty cycle of less than 50 percent. The theoretical description of the shortened heating time is based on a step-function formulation of the pumping cycle. The results are obtained as closed-form solutions of the energy equation for many chopping cycles until steady state is reached, by use of a Green's-function method. The Euler formulation of the Fermat principle is used to calculate the deflection angle. The equations are expanded to include the effects of vapor velocity on both the temperature and temperature gradient profiles. The effects of finite (unfocused) pump and probe beams and thermal (Soret) diffusion are also accounted for. Excellent agreement between theory and experiment is obtained.

Banish, R. Michael↗