NASA NTRS1994

Comparison of the magnetic properties and Mossbauer analysis of glass from the Cretaceous-Tertiary boundary, Beloc, Haiti, with tektites

The magnetic properties of black Beloc glass have been measured. The Curie constant, the magnetization, and the magnetic susceptibility of the Beloc glass fall within the known ranges observed for tektites. However, the temperature-independent component of the magnetic susceptibility is slightly higher than that found for tektites. Moreover, it is not possible to match the experimental magnetic data for the Beloc glass with the calculated values using the previously reported Fe(3+)/Fe(2+) ratio of 0.7. The oxidation state of Fe was therefore redetermined by Mossbauer measurements, and the Fe(3+)/Fe(2+) ratio was found to be 0.024 plus or minus 0.015. Using the redetermined value of the ratio, the magnetic parameters were again calculated using formulas that are applicable to tektites, and good agreement was found between the calculated and experimental values. The experimental magnetic measurements and the redetermined Fe(3+)/Fe(2+) ratio of the Beloc glass specimens are essentially the same as those found for tektite glass.

Thorpe, A. N.↗

NASA NTRS1993

Magnetic properties and Moessbauer analyses of glass from the K-T boundary, Beloc, Haiti

The experimental magnetic susceptibility, the temperature-independent component of the magnetic susceptibility, the magnetization, and the Curie constant have been measured for a number of specimens of glass from the K-T boundary found at Beloc, Haiti, and the results are compared with those of similar measurements of tektites. Because the Fe(3+)/Fe(2+) ratio is needed to calculate the magnetic parameters, Moessbauer spectroscopic measurements were also made. The data were consistent with the classification of the Beloc glasses as tektites.

Senftle, F. E.↗

NASA NTRS1992

Bulk YBa2Cu3O(x) superconductors through pressurized partial melt growth processing

A novel pressurized partial melt growth process has been developed for producing large pieces of bulk Y-Ba-Cu-O superconductors. During long-time partial melt growth stage, an additional driving force for solidification is obtained by using pressurized oxygen gas. The microstructure and superconducting properties of the resulting samples were investigated. It was found that this new technique can eliminate porosity and inhomogeneity, promote large-scale grain-texturing, and improve interdomain coupling as well.

Hu, S.↗

NASA NTRS1990

Microstructure and magnetization of doped Y-Ba-Ca-O materials prepared by melt quench and post annealing method

Y-Ba-Cu-O bulk materials prepared using the melt quench and post annealing method were shown to have very high maximum as well as remanent magnetization. Studies were carried out on materials prepared using this method which deviate from the Y:Ba:Cu = 1:2:3 stoichiometry. In one series of materials, only the stoichiometry was changed, in particular by introducing an excess of yttrium. In other cases, dopants including several rare earths were introduced. Effects of variations in composition on microstructure and phase evolution are discussed, as well as effects on the magnetic susceptibility and on the magnetization. The results show that doped materials can exhibit improvements in magnetic properties. Furthermore, the use of dopants sheds light on the role of defect sites in flux pinning.

Hojaji, H.↗

NASA NTRS1989

The low magnetic field properties of superconducting bulk yttrium barium copper oxide - Sintered versus partially melted material

A comparison of the low magnetic field properties of sintered (990 C) and partially melted samples (1050 C) has been performed. Changes in the microstructure produced by recrystallization from the melt result in a significant increase in flux pinning at 77 K. Low-frequency (10-100 Hz), low-ac magnetic-field (0.01-9.0 Oe) ac susceptibility data show that gross changes in the loss component accompany the observed changes in microstructure. The effects of applied dc magnetic fields (10-220 Oe) on the ac responses of these microstructures have also been probed.

Hein, R. A.↗

NASA NTRS1984

The chemical durability of tektites - A laboratory study and correlation with long-term corrosion behavior

Leach tests carried out on tektite specimens (indochinites and australites) under high-dilution conditions show a common behavior characterized by low leach rates (0.00018 g/sq m per d, or 7.2 x 10 to the -12th m/d at 23 C) and an activation energy of (79,600 + or - 700 J/mol). The extent of selective leaching is very small, of the order of 10 to the -8th m. Extrapolation of test results over the lifetime of the tektites gives an excellent agreement with field observations on the extent of corrosion, and this is an important step in establishing the validity of laboratory tests as a basis for the development of models and predictions concerning long-term durabilities at least in the limiting case of high dilution or rapid flow. The results are also shown to be in agreement with various previous observations on the corrosion resistance of tektites. The chemical durability of tektites is observed to be consistent with their composition, highlighting requirements of high corrosion resistance in glasses; these requirements include a silica content in excess of 67 mol percent, an extremely low water content, and an alkali content which is low both absolutely and relative to the di- and poly-valent metal oxide levels. It is shown that artificial glasses which fulfil these criteria are no less corrosion-resistant than the corresponding natural glasses. These conclusions have bearing on the development, as well as on the evaluation, of glasses intended for very long service, such as radioactive waste vitrification media.

Barkatt, A.↗