DOE OSTI2024

Phase Transition of Heptane under Pressure

A solid-to-solid phase transition was discovered in n-heptane with an onset at a pressure of 1.7 ± 0.1 GPa, evidenced by a discontinuity in the pressure–volume equation of state obtained from synchrotron X-ray diffraction experiments conducted at room temperature. The phase transition also resulted in discontinuous shifts of vibrational peaks in the infrared spectra. No additional phase transitions were detected up to 10 GPa, contradicting an earlier claim of a phase transition at 3 GPa. Furthermore, the hydrostatic limit of heptane in a diamond anvil cell was estimated to be 3.5 GPa. Above that pressure, the stress state is not well-defined, which may explain prior reports of a phase transition at 7.5 GPa.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2023

Photoluminescence of Cr 3+ in β-Ga 2 O 3 and (Al 0.1 Ga 0.9 ) 2 O 3 under pressure

The effects of pressure on single crystals of Cr-doped gallium oxide (β-Ga 2 O 3 :Cr 3+ ) and aluminum gallium oxide [(Al 0.1 Ga 0.9 ) 2 O 3 ] were examined by measuring the wavelength shift in the spectral R lines. Photoluminescence (PL) spectra of these materials were collected from samples in diamond anvil cells at pressures up to 9 GPa. The β-Ga 2 O 3 :Cr 3+ R lines were found to shift linearly under hydrostatic pressure. The (Al 0.1 Ga 0.9 ) 2 O 3 R lines also show a linear shift but the R 1 line shifted less than for β-Ga 2 O 3 :Cr 3+ . The ratio of R 2 to R 1 peak areas vs pressure is dominated by nonradiative recombination. X-ray diffraction measurements of (Al 0.1 Ga 0.9 ) 2 O 3 indicate that its equation of state is similar to that of β-Ga 2 O 3 . β-Ga 2 O 3 :Cr 3+ was examined under non-hydrostatic conditions by using mineral oil as a pressure transmitting medium. Similar to the case in ruby, the R 1 line is much more sensitive to non-hydrostatic stress than R 2 . Spatially resolved PL of a sample at 8 GPa in mineral oil showed significant variations in the R 1 emission wavelength. Furthermore, these results suggest that the R 1 line can serve as a sensitive probe of alloy composition and non-hydrostatic stress, while the R 2 line is insensitive to these perturbations.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Photoluminescence spectroscopy of Cr 3+ in β-Ga 2 O 3 and (Al 0.1 Ga 0.9 ) 2 O 3

Alloying β-Ga 2 O 3 with Al 2 O 3 to create (Al x Ga 1–x ) 2 O 3 enables ultra-wide bandgap materials suitable for applications deep into ultraviolet. In this work, photoluminescence (PL) spectra of Cr 3+ were investigated in monoclinic single crystal β-Ga 2 O 3 , and 10 = mol. % Al 2 O 3 alloyed with β-Ga 2 O 3 , denoted β-(Al 0.1 Ga 0.9 ) 2 O 3 or AGO. Temperature-dependent PL properties were studied for Cr 3+ in AGO and β-Ga 2 O 3 from 295 to 16 K. For both materials at room temperature, the red-line emission doublet R 1 and R 2 occurs at 696 nm (1.78 eV) and 690 nm (1.80 eV), respectively, along with a broad emission band at 709 nm (1.75 eV). Here, the linewidths for AGO are larger for all temperatures due to alloy broadening. For both materials, the R-lines blue-shift with decreasing temperature. The (lowest energy) R 1 line is dominant at low temperatures due to the thermal population of the levels. For temperatures above ~50 K, however, the ratio of R 2 to R 1 peak areas is dominated by nonradiative combination.

36 MATERIALS SCIENCE↗