DOE OSTI2024

Concurrent Amorphization and Nanocatalyst Formation in Cu‐Substituted Perovskite Oxide Surface: Effects on Oxygen Reduction Reaction at Elevated Temperatures

Abstract The activity and durability of chemical/electrochemical catalysts are significantly influenced by their surface environments, highlighting the importance of thoroughly examining the catalyst surface. Here, Cu‐substituted La 0.6 Sr 0.4 Co 0.2 Fe 0.8 O 3‐δ is selected, a state‐of‐the‐art material for oxygen reduction reaction (ORR), to explore the real‐time evolution of surface morphology and chemistry under a reducing atmosphere at elevated temperatures. Remarkably, in a pioneering observation, it is discovered that the perovskite surface starts to amorphize at an unusually low temperature of approximately 100 °C and multicomponent metal nanocatalysts additionally form on the amorphous surface as the temperature raises to 400 °C. Moreover, this investigation into the stability of the resulting amorphous layer under oxidizing conditions reveals that the amorphous structure can withstand a high‐temperature oxidizing atmosphere (≥650 °C) only when it has undergone sufficient reduction for an extended period. Therefore, the coexistence of the active nanocatalysts and defective amorphous surface leads to a nearly 100% enhancement in the electrode resistance for the ORR over 200 h without significant degradation. These observations provide a new catalytic design strategy for using redox‐dynamic perovskite oxide host materials.

Jeon, SungHyun↗

DOE OSTI2023

Cobalt-substituted perovskite compounds for solid oxide electrochemical cells

Oxygen electrodes are provided, comprising a perovskite compound having Formula (I), Sr(Ti 1-x Fe x-y Co y )O 3-δ wherein 0.90 ≥ x ≥ 0.40 and 0.02 ≥ y ≥ 0.30. Electrochemical devices comprising such oxygen electrodes are also provided, comprising a counter electrode in electrical communication with the oxygen electrode, and a solid oxide electrolyte between the oxygen electrode and the counter electrode. Methods of using such electrochemical devices are also provided, comprising exposing the oxygen electrode to a fluid comprising O 2 under conditions to induce the reaction O 2 +4e − →2O 2− , or to a fluid comprising O 2− under conditions to induce the reaction 2O 2− →O 2 +4e − .

Zhang, Shan-Lin↗

DOE OSTI2023

Roadmap on exsolution for energy applications

Over the last decade, exsolution has emerged as a powerful new method for decorating oxide supports with uniformly dispersed nanoparticles for energy and catalytic applications. Due to their exceptional anchorage, resilience to various degradation mechanisms, as well as numerous ways in which they can be produced, transformed and applied, exsolved nanoparticles have set new standards for nanoparticles in terms of activity, durability and functionality. In conjunction with multifunctional supports such as perovskite oxides, exsolution becomes a powerful platform for the design of advanced energy materials. In the following sections, we review the current status of the exsolution approach, seeking to facilitate transfer of ideas between different fields of application. We also explore future directions of research, particularly noting the multi-scale development required to take the concept forward, from fundamentals through operando studies to pilot scale demonstrations.

25 ENERGY STORAGE↗

DOE OSTI2023

Beneficial Effects of La 0.5 Sr 0.5 CoO 3 Coatings on Thin‐Film LiMn 2 O 4 Cathodes for Lithium Ion Batteries

Abstract The severe capacity loss of spinel LiMn 2 O 4 (LMO) limits the utility of this otherwise promising lithium ion battery cathode material. One of the strategies to mitigate capacity fade is applying a coating on LMO particle surfaces. While this approach yields promising results, there is limited understanding of mechanisms whereby coatings improve LMO capacity retention. Herein, the effects of a new protective coating material, La 0.5 Sr 0.5 CoO 3 (LSCO), in a thin‐film battery geometry that is amenable to fundamental studies of electrode processes, are reported. RF sputtering deposition is used to produce high quality 25–100 nm LMO cathodes on Al 2 O 3 substrates with an intervening Pt/Ti back‐side contact layer. Cycling of the un‐coated cathodes results in capacity loss of 18% over 300 cycles. Adding a 2 nm LSCO layer reduces the capacity loss to 3%. While this may be due in part to reduced Mn dissolution, scanning transmission electron microscopy results indicate that the coating helps to preserve crystallinity and reduce lattice structure distortion due to inhibited formation of defect tetragonal spinel. Three‐electrode electrochemical impedance spectroscopy results reveal that the LSCO coating increases charge transfer and ohmic resistances, but the increases are generally too small to significantly impact cell performance even at high C‐rates.

25 ENERGY STORAGE↗