NASA NTRS2003

Nondestructive Evaluation of Ceramic Matrix Composite Combustor Components

Combustor liners fabricated from a SiC/SiC composite (silicon carbide fibers in a silicon carbide matrix) were nondestructively interrogated before and after combustion rig testing by x-ray, ultrasonic, and thermographic techniques. In addition, mechanical test results were obtained from witness coupons, representing the as-manufactured liners, and from coupons machined from the components after combustion exposure. Thermography indications correlated with reduced material properties obtained after rig testing. The thermography indications in the SiC/SiC liners were delaminations and damaged fiber tows, as determined through microstructural examinations.

Sun, Jiangang G.↗

NASA NTRS2002

Hoop Tensile Characterization Of SiC/SiC Cylinders Fabricated From 2D Fabric

Tensile stress-strain properties in the hoop direction were obtained for 100-mm diameter SiC/SiC cylinders using ring specimens machined from the cylinder ends. The cylinders were fabricated from 2D balanced fabric with several material variants, including wall thickness (6, 8, and 12 plies), Sic fiber type (Sylramic, Sylramic-iBN, Hi-Nicalon, and Hi-Nicalon S), fiber sizing type, and matrix type (full CVI Sic, and partial CVI plus melt-infiltrated SiC-Si). Fiber ply splices existed in the all the hoops. Tensile hoop measurements were made at room temperature and 1200 C using hydrostatic ring test facilities. The hoop results are compared with in-plane data measured on flat panels using same material variants, but containing no splices.

Verrilli, Michael J.↗

NASA NTRS1988

An Experimental and Analytical Evaluation of a Biaxial Test for Determining Shear Properties of Composite Materials

The results of an experimental and analytical investigation of a biaxial tension/compression test for determining shear properties of composite materials are reported. Using finite element models of isotropic and orthotropic laminates, a specimen geometry was optimized. A kinematic fixture was designed to introduce an equal and opposite pair of forces into a specimen with a one inch square test section. Aluminum and several composite laminates with the optimized geometry and a configuration with large stress gradients were tested in the fixture. The specimens were instrumented with strain gages in the center of the test section for shear stiffness measurements. Pure shear strain was measured. The results from the experiments correlated well with finite element results. Failure of the specimens occurred through the center of the test section and appeared to have initiated at the high stress points. The results lead to the conclusion that the optimized specimen is suitable for determining shear modulus for composite materials. Further revisions to the specimen geometry are necessary if the method is to give shear strength data.

Kennedy, John M.↗