Publications and source records attributed to Barr, Christopher.

9 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2021

Evidence for a High Temperature Whisker Growth Mechanism Active in Tungsten during In Situ Nanopillar Compression

A series of nanopillar compression tests were performed on tungsten as a function of temperature using in situ transmission electron microscopy with localized laser heating. Surface oxidation was observed to form on the pillars and grow in thickness with increasing temperature. Deformation between 850 °C and 1120 °C is facilitated by long-range diffusional transport from the tungsten pillar onto adjacent regions of the Y2O3-stabilized ZrO2 indenter. The constraint imposed by the surface oxidation is hypothesized to underly this mechanism for localized plasticity, which is generally the so-called whisker growth mechanism. The results are discussed in context of the tungsten fuzz growth mechanism in He plasma-facing environments. The two processes exhibit similar morphological features and the conditions under which fuzz evolves appear to satisfy the conditions necessary to induce whisker growth.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Grain growth of nanocrystalline aluminum under tensile deformation: A combined in situ TEM and atomistic study

Nanocrystalline Al thin films have been strained in situ in a transmission electron microscope using two separate nanomechanical techniques involving a push-to-pull device and a microelectromechanical system (MEMS) device. Deformation-induced grain growth was observed to occur via stress-assisted grain boundary migration with extensive grain growth occurring in the necked region, indicating that the increase in local stress drives the boundary migration. Under applied tensile stresses close to the ultimate tensile strength of 450 MPa for a nanocrystalline Al specimen, measured boundary migration speeds are 0.2 – 0.7 nm s -1 for grains outside necked region and increases to 2.5 nm s -1 for grains within the necked region where the local estimated tensile stresses are elevated to around 630 MPa. By tracking grain boundary motion over time, molecular dynamics simulations showed qualitative agreement in terms of pronounced grain boundary migration with the experimental observations. The combined in situ observation and molecular dynamics simulation results underscore the important role of stress-driven grain growth in plastically deforming nanocrystalline metals, leading to intergranular fracture through predominant grain boundary sliding in regions with large localized deformation.

36 MATERIALS SCIENCE↗