DOE OSTI2024

Robust Solar Receivers Using MAX Phase Materials

This work was supported by the U.S. Department of Energy’s Office of Energy Efficiency and Renewable Energy under the Solar Energy Technologies Office Award Number 35928. The objective of the proposed effort was to develop and optimize additive manufacturing technologies for low-cost fabrication of high-temperature receivers using MAX phase-based materials (Ti 3 SiC 2 and Ti 3 AlC 2 ). MAX phase materials are a group of ternary metal carbides and nitrides where M stands for an early transition metal element, A is a group 13–16 element, and X is C and/or N. In Phase 1, the binder jetting additive manufacturing process was used to synthesize and characterize the Ti 3 SiC 2 MAX phase material. The typical process involved first producing a TiC preform using binder jetting followed by infiltration of the preform with silicon melt to form Ti 3 SiC 2 in situ. The reaction-infiltrated samples showed formation of MAX phase in the sample core; however, the surface showed cracking. Various process conditions—cooling rates, hold times, Si proportion, etc.—were varied to minimize the surface cracking. The fabricated MAX phase core was characterized by microstructure analysis and evaluations of mechanical properties such as hardness and thermal shock. In Phase 2, the focus included fabrication of Ti 3 SiC 2 MAX phase materials by spark plasma sintering (SPS) and synthesis of Ti 3 AlC 2 MAX phase materials by the Al melt infiltration process. It is expected that Al infiltration will not cause sample cracking, since Al does not expand during solidification. In addition, other processing approaches were investigated to fabricate the MAX phase materials, such as SPS with a graphite bedding approach for producing short-length Ti 3 AlC 2 MAX phase tubes for demonstration of prototypical Concentrating Solar Power receiver tubes. Fabricated samples underwent thermo-mechanical testing to validate the materials for the solar receiver application at temperatures >1000°C. In Phase 3, the effort focused on the development and optimization of the Ti-Al-C MAX phase composite material using the Al melt infiltration approach. We started with optimization of precursor powders and making preform structures by either pressing them in a die or using the binder jetting additive manufacturing process followed by Al melt infiltration. In addition, we investigated the formation of preform structures by cold isostatic pressing followed by Al melt infiltration for making Ti-Al-C MAX phase composite. Thermo-mechanical characterizations, such as creep, strength, and thermal shock, were conducted to establish the structures’ performance.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Development of a high-temperature Inconel 625 heat exchanger by model design and binder jetting additive manufacturing

A nickel-based Inconel 625 superalloy heat exchanger for high-temperature applications was developed via binder jetting additive manufacturing. The material properties were characterized first on printed and sintered parts. Two sintering temperatures were used to investigate the effects of the temperature on densification and microstructure. For channel geometry design, the heat transfer capabilities of the heat exchanger were optimized for the cross-section geometry of fluid flow channels in a counterflow configuration, and a stress analysis was conducted to investigate the effects of channel geometry. After headers were incorporated into the heat exchanger as a one-piece component, a prototype was printed. A complete depowdering was achieved via compressed air blowing, and sintering was performed with the developed profile. Ultimately, a one-piece heat exchanger with a nearly full density was obtained. Heat transfer tests were performed on this unit, and the results were compared with those from the simulations. In this study, systematic processes were developed for an additively manufactured Inconel-based heat exchanger for high-pressure, high-temperature heat transfer applications.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Development of Ti 3 SiC 2 MAX phase tubular structures for solar receiver applications

Solar receiver tubes are key components of concentrating solar-thermal power (CSP) systems that harvest solar energy. For better efficiency, the Gen3 CSP receivers, which collect heat into a heat transfer fluid, require a temperature exceeding 700 °C during operation and need to perform under extreme conditions of high temperature and high thermal stress. Operators are seeking CSP designs using new high-temperature structural materials with high thermal conductivity and high creep resistance to achieve a design life of 30 years and thus help recover the plant capital cost sooner. MAX phase materials, which consist of an early transition metal element, an A-group element, and carbon or nitrogen, are expected to exhibit high creep resistance as well as high fracture toughness. Here, in this paper, we describe fabricating both (1) dense Ti 3 SiC 2 MAX phase disks and (2) short-length tubes using field-assisted sintering technology (FAST). First, the disk samples that we fabricated are fully dense and contain ≈90 % Ti 3 SiC 2 MAX phase materials and ≈10 % TiC phase materials. We determined a flexure strength of 519 ± 32 MPa by conducting a four-point bending test at room temperature with rectangular bar samples of ≈100 % density. The thermal conductivity of the Ti 3 SiC 2 MAX phase samples, measured by light flashing analysis, decreases linearly from a value of 41 W . m -1 . K -1 at room temperature to a value of 36 W . m -1 . K -1 at 650 °C. A solar reflectance measurement of the Ti 3 SiC 2 MAX phase revealed that, temperature increases from 400 to 1400 °C, thermal emittance increases from 0.39 to 0.49, while selectivity decreases from 1.8 to 1.4, respectively. Whereas the surface oxidized MAX phase samples after 100 h exposure to air at 1000 °C exhibit that of SiC. Next, we discuss fabrication of the crack-free Ti 3 SiC 2 MAX phase tubular structures accomplished by using FAST processing in graphite bedding. A Ti 3 SiC 2 MAX phase content of > 95 % with traceable ≈3% remaining TiC phase and ≈15 % porosity were demonstrated after high-temperature annealing. An average fracture strength of ≈250 MPa was determined with Ti 3 SiC 2 MAX phase tubes of ≈85 % density by diametral compression testing at room temperature. Our work demonstrated that using FAST processing to produce Ti 3 SiC 2 MAX phase tubular structures for CSP receiver applications is a viable approach.

14 SOLAR ENERGY↗

DOE OSTI2024

ASME Section III, Division 5, Class A 100,000-hour design data for Alloy 709

This report documents the 100,000 hour, Class A ASME design material data for Alloy 709 based on the extensive Department of Energy, Office of Nuclear Energy, Advanced Reactor Technologies qualification test campaign. This report includes design tensile properties, creep rupture data, allowable stresses, isochronous stress-strain curves, buckling charts, and a few additional miscellaneous pieces of design data. Companion work at Oak Ridge National Laboratory and Argonne National Laboratory provide design cyclic data --- fatigue charts and creep-fatigue diagrams --- and an inelastic constitutive model. This work substantially completes the ASME data package for the Alloy 709 Code Case, though the design data will continue to updated as the final tests finish. This report also compares the design performance of Alloy 709 against that of 316H stainless steel to provide a reference for the improved high temperature strength of 709 compared to a reference material for sodium fast reactor construction.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Acceptance criteria for in situ surveillance of MSR materials based on thermally-loaded mechanical test articles

This report describes practices and acceptance test procedures for designing, running, and maintaining a material surveillance program in a future operating molten salt reactor. The programs described here rely on test data from passively actuated mechanical test articles inserted into critical regions of the reactor and periodically removed for out-of-reactor testing. The report defines definite acceptance procedures, based on the results of these tests, to determine whether a component can continue to operate accounting for the accumulation of environmentally-assisted mechanical damage in the component materials to date, and extrapolated out through the next inspection period. Additionally, the report describes work on a software tool implementing many of the surveillance methods and procedures described here and progress on simplified methods for inferring damage accumulation in the test articles, based on out-of-reactor thermal cycling, that do not rely on sophisticated numerical analysis.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Design Methods, Tools, and Data for Ceramic Solar Receivers

This report presents the development of tools and methods for evaluating the reliability and performance of ceramic materials in high temperature solar receivers. As Concentrating Solar Power (CSP) technologies aim for higher operating temperatures to enhance efficiency and meet industrial process heat requirements, current high temperature metallic materials face challenges in maintaining structural integrity. This report explores advanced ceramics as a promising alternative, given their superior high temperature strength and lower thermal expansion, compared to metals. To address the need for effective ceramic receiver design tools, this report integrates statistical failure models of ceramics into the existing srlife tool: an open-source software package designed to estimate the life of high temperature CSP components. These failure models account for the inherent variability and flaw distribution in ceramics, as well as the impact of subcritical crack growth under high temperature cyclic loads. The report also presents experimental data collected for a commercially available ceramic material, SiC, and details the process of estimating reliability model parameters from these data. A comparative design analysis is then performed between ceramic (SiC) and metallic (current nickel-based superalloys A740H and A282) receiver. This comparison demonstrates that SiC receivers can achieve service life exceeding 30 years under high incident heat flux conditions, compared to just a few years for metallic receivers.

14 SOLAR ENERGY↗