DOE OSTI2024

Green-emitting cubic GaN/In 0.16 Ga 0.84 N/GaN quantum well with 32% internal quantum efficiency at room temperature

Structural and optical properties of a green-emitting cubic (i.e., zinc blende) GaN/In 0.16 Ga 0.84 N/GaN single quantum well structure are reported. The active layer is grown on a phase-pure (i.e., 100%) cubic GaN enabled on a 1 × 1 cm 2 U-grooved silicon (100) through aspect ratio phase trapping. Energy dispersive x-ray spectroscopy combined with room temperature cathodoluminescence reveals 522 nm green light emission at room temperature with only 16.0% ± 1.6% of indium content, which is ~30% less than the amount of indium needed in a traditional green-emitting hexagonal (i.e., wurtzite) well. Temperature-dependent behavior of the green emission, such as activation energy, s-shaped peak energy shift, and linewidth, is reported. Cathodoluminescence at 8 and 300 K reveals an internal quantum efficiency of 32.0% ± 0.6%, which is higher than any reported value for cubic wells. Altogether, phase-pure cubic active layers on phase transition cubic GaN are shown to be promising for green and longer wavelength emitters.

42 ENGINEERING↗

DOE OSTI2023

Low temperature absolute internal quantum efficiency of InGaN-based light-emitting diodes

A method to reveal low temperature absolute internal quantum efficiency of an InGaN-based light-emitting diode (LED) is reported. Structural (via scanning electron and atomic force microscopies, x-ray diffraction, and Raman spectroscopy) and optical (via temperature- and power-dependent photoluminescence) properties of InGaN-based blue LEDs are coupled with a channel-based recombination model, which reveals the low temperature absolute internal quantum efficiency of the LED on traditional sapphire and emerging Si (111) substrates as 27.5% and 71.1%, respectively. High low-temperature absolute internal quantum efficiency of the former is attributed to its lower defect density and less strain. Furthermore, our results show assuming perfect (i.e., 100%) internal quantum efficiency in an InGaN-based LED at low temperatures could be misleading, and using negative thermal quenching properties of defect luminesce bands with a channel-based recombination model can be a method to quantify LED's less than ideal low temperature internal quantum efficiencies.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Structural and optical properties of cubic GaN on U-grooved Si (100)

Cubic GaN epitaxy on large-area U-grooved silicon (100) dies is demonstrated by metalorganic chemical vapor deposition, and its structural and optical properties are reported. Scanning electron, atomic force, and transmission electron microscopy studies reveal that cubic GaN shows no discernible threading dislocations and a low stacking fault density of 3.27 ± 0.18 × 10 4 cm –1 . Temperature-dependent photoluminescence studies reveal as-grown cubic GaN band edge emission internal quantum efficiency as 25.6% ± 0.9%. Selective etching of the low-temperature AlN buffer layer, SiO 2 sidewalls, and hexagonal-phase GaN is demonstrated, which increases the cubic GaN band edge emission internal quantum efficiency to 31.6% ± 0.8%. This increase is attributed to the decrease in the radiative recombination lifetime via the removal of defective hexagonal-phase GaN. Altogether, cubic GaN on U-grooved silicon with high structural and optical quality is reported, promising its suitability for next-generation devices.

36 MATERIALS SCIENCE↗