DOE OSTI2016

Summary Report: NMSBA CY 2016 - AEgis Technologies Group Inc. #12458.

AEgis requires large area partial mirror optics consisting of partially reflecting optical coatings on large dimension substrates for high energy laser (HEL) applications. The partial mirrors should transmit nearly the same small fraction of HEL radiation incident from a wide range of angles of incidence (AOIs), and the laser-induced damage threshold (LIDT) of the coatings should be high enough for them to be able to withstand direct exposure to near infrared CW HEL radiation at multi-kilowatt/cm2 power levels. The transmitted fraction of incident HEL radiation should reach an array of detectors at power levels high enough for reliable detection but low enough to not damage the detectors. The reflected fraction of incident HEL radiation should scatter into a divergent pattern so as to be eye safe at a distance of ~ 200 m from the mirror in the case of 100 kilowatt incident laser power. The detector array together with the partial mirror optic and possible additional optics that provide divergent scattering of reflected HEL radiation constitute what AEgis refers to as a target board. The target board use environment may vary from benign, indoor laboratory conditions to harsh, outdoor conditions in tests on the ground as well as in air. Under this NMSBA project, Sandia agreed to apply its extensive expertise and capability in the design and production of high LIDT coatings on large dimension optics for high power pulsed laser radiation to advise and assist AEgis in the design and development of high LIDT coatings for the partial mirror optic. Sandia and AEgis met several times to discuss the partial mirror and target board requirements, and Sandia was guided in its work by these discussions as well as by the partial mirror and target board requirement summaries of Tables 1 and 2, respectively, that were provided by AEgis.

47 OTHER INSTRUMENTATION↗
DOE OSTI2016

Design and laser damage properties of a dichroic beam combiner coating for 22.5-deg incidence and S polarization with high transmission at 527 nm and high reflection at 1054 nm

We designed a dichroic beam combiner coating with 11 HfO 2 /SiO 2 layer pairs and deposited it on a large substrate. It provides high transmission (HT) at 527 nm and high reflection (HR) at 1054 nm for a 22.5-deg angle of incidence (AOI), S polarization (Spol), and uses near half-wave layer thicknesses for HT at 527 nm, modified for HR at 1054 nm. The two options for the beam combiner each require that a high intensity beam be incident on the coating from within the substrate (from glass). We analyze the laser-induced damage threshold (LIDT) differences between the two options in terms of the 527- and 1054-nm E-field behaviors for air → coating and glass → coating incidences. This indicates that LIDTs should be higher for air → coating than for glass → coating incidence. LIDT tests at the use AOI, Spol with ns pulses at 532 and 1064 nm confirm this, with glass → coating LIDTs about half that of air → coating LIDTs. Lastly, these results clearly indicate that the best beam combiner option is for the high intensity 527 and 1054 nm beams to be incident on the coating from air and glass, respectively.

36 MATERIALS SCIENCE↗
DOE OSTI2016

Laser damage comparisons of broad-bandwidth, high-reflection optical coatings containing TiO 2 , Nb 2 O 5 , or Ta 2 O 5 high-index layers

Broad bandwidth coatings allow angle of incidence flexibility and accommodate spectral shifts due to aging and water absorption. Higher refractive index materials in optical coatings, such as TiO 2 , Nb 2 O 5 , and Ta 2 O 5 , can be used to achieve broader bandwidths compared to coatings that contain HfO 2 high index layers. We have identified the deposition settings that lead to the highest index, lowest absorption layers of TiO 2 , Nb 2 O 5 , and Ta 2 O 5 , via e-beam evaporation using ion-assisted deposition. We paired these high index materials with SiO 2 as the low index material to create broad bandwidth high reflection coatings centered at 1054 nm for 45 deg angle of incidence and P polarization. Furthermore, high reflection bandwidths as large as 231 nm were realized. Laser damage tests of these coatings using the ISO 11254 and NIF-MEL protocols are presented, which revealed that the Ta 2 O 5 /SiO 2 coating exhibits the highest resistance to laser damage, at the expense of lower bandwidth compared to the TiO 2 /SiO 2 and Nb 2 O 5 /SiO 2 coatings.

36 MATERIALS SCIENCE↗
DOE OSTI2016

Analysis of laser damage tests on coatings designed for broad bandwidth high reflection of femtosecond pulses

We designed an optical coating based on TiO 2 /SiO 2 layer pairs for broad bandwidth high reflection (BBHR) at 45-deg angle of incidence (AOI), P polarization of femtosecond (fs) laser pulses of 900-nm center wavelength, and produced the coatings in Sandia’s large optics coater by reactive, ion-assisted e-beam evaporation. This paper reports on laser-induced damage threshold (LIDT) tests of these coatings. The broad HR bands of BBHR coatings pose challenges to LIDT tests. An ideal test would be in a vacuum environment appropriate to a high energy, fs-pulse, petawatt-class laser, with pulses identical to its fs pulses. Short of this would be tests over portions of the HR band using nanosecond or sub-picosecond pulses produced by tunable lasers. Such tests could, e.g., sample 10-nm-wide wavelength intervals with center wavelengths tunable over the broad HR band. Alternatively, the coating’s HR band could be adjusted by means of wavelength shifts due to changing the AOI of the LIDT tests or due to the coating absorbing moisture under ambient conditions. In conclusion, we had LIDT tests performed on the BBHR coatings at selected AOIs to gain insight into their laser damage properties and analyze how the results of the different LIDT tests compare.

36 MATERIALS SCIENCE↗
DOE OSTI2016

Repair of a mirror coating on a large optic for high laser damage applications using ion milling and over-coating methods

Here, when an optical coating is damaged, deposited incorrectly, or is otherwise unsuitable, the conventional method to restore the optic often entails repolishing the optic surface, which can incur a large cost and long lead time. We propose three alternative options to repolishing, including (i) burying the unsuitable coating under another optical coating, (ii) using ion milling to etch the unsuitable coating completely from the optic surface and then recoating the optic, and (iii) using ion milling to etch through a number of unsuitable layers, leaving the rest of the coating intact, and then recoating the layers that were etched. Repairs were made on test optics with dielectric mirror coatings according to the above three options. The mirror coatings to be repaired were quarter wave stacks of HfO 2 and SiO 2 layers for high reflection at 1054 nm at 45 deg incidence in P-polarization. One of the coating layers was purposely deposited incorrectly as Hf metal instead of HfO2 to evaluate the ability of each repair method to restore the coating’s high laser-induced damage threshold (LIDT) of 64.0 J/cm 2 . The repaired coating with the highest resistance to laser-induced damage was achieved using repair method (ii) with an LIDT of 49.0 to 61.0 J/cm 2 .

36 MATERIALS SCIENCE↗
DOE OSTI2016

Repair of a Mirror Coating on a Large Optic for High Laser Damage Applications using Ion Milling and Over-Coating Methods.

When an optical coating is damaged, deposited incorrectly, or is otherwise unsuitable, the conventional method to restore the optic often entails repolishing the optic surface, which can incur a large cost and long lead time. We propose three alternative options to repolishing, including (i) burying the unsuitable coating under another optical coating, (ii) using ion milling to etch the unsuitable coating completely from the optic surface, and then recoating the optic, and (iii) using ion milling to etch through a number of unsuitable layers, leaving the rest of the coating intact, and then recoating the layers that were etched. Repairs were made on test optics with dielectric mirror coatings according to the above three options. The mirror coatings to be repaired were quarter wave stacks of HfO 2 and SiO 2 layers for high reflection at 1054 nm at 45° incidence in P-polarization. One of the coating layers was purposely deposited incorrectly as Hf metal instead of HfO 2 to evaluate the ability of each repair method to restore the coating’s high laser-induced damage threshold (LIDT) of 64.0 J/cm 2 . Finally, the repaired coating with the highest resistance to laser-induced damage was achieved using repair method (ii) with an LIDT of 49.0 – 61.0 J/cm 2 .

42 ENGINEERING↗
DOE OSTI2016

How reduced vacuum pumping capability in a coating chamber affects the laser damage resistance of HfO 2 /SiO 2 antireflection and high reflection coatings.

Optical coatings with the highest laser damage thresholds rely on clean conditions in the vacuum chamber during the coating deposition process. A low base pressure in the coating chamber, as well as the ability of the vacuum system to maintain the required pressure during deposition, are important aspects of limiting the amount of defects in an optical coating that could induce laser damage. Our large optics coating chamber at Sandia National Laboratories normally relies on three cryo pumps to maintain low pressures for e-beam coating processes. However, on occasion, one or more of the cryo pumps have been out of commission. In light of this circumstance, we explored how deposition under compromised vacuum conditions resulting from the use of only one or two cryo pumps affects the laser-induced damage thresholds of optical coatings. Finally, the coatings of this study consist of HfO 2 and SiO 2 layer materials and include antireflection coatings for 527 nm at normal incidence, and high reflection coatings for 527 nm, 45⁰ angle of incidence (AOI), in P-polarization (P-pol).

Field, Ella Suzanne↗