Fundamentals of Scalable Nanoparticle Assembly in Engineering Polymres
Systematically improving the properties of polymer nanocomposites is contingent on effectively controlling nanoparticle (NP) dispersion; further, it is necessary to attain this at scale if these methods are to impact practical applications. While most past work has focused on amorphous polymers, ≈ 70% of all polymers sold annually are semicrystalline. Inspired by this apparent disconnect, our work in the current DOE funded grant and this renewal proposal employs a novel handle, polymer crystallization, to organize NPs into the various amorphous zones of the lamellar semicrystalline morphology (interlamellar, interfibrillar and interspherulitic domains) of stereoregular polymers. We hypothesize that the isothermal crystallization rate of a polymer host, G, and NP diffusivity, are the two relevant control parameters in this context. In the case where the NPs are miscible in the melt, they remain spatially well-dispersed when the polymer is crystallized at a rate that is fast relative to NP diffusion. In contrast, monolayer-thick NP sheets with intersheet spacing of ~10-100nm form in slowly crystallized samples. This sheet stacking is remarkably similar to that seen in natural materials, e.g., Nacre. There is also ordering of the NPs at the larger interfibrillar scale. Importantly, the relative fraction of engulfed, interlamellar and interfibrillar NPs is determined by G. Further, the modulus of these materials can increase by a factor of 2-3 due to the organization state of the NPs, while leaving fracture toughness unaffected. We have established the broad applicability of this approach in two polymers, polyethylene (PE) and polyethyleneoxide (PEO). To achieve this goal we developed a method for grafting long PE chains from NPs with controlled graft density and molecular weight, giving us the ability to tailor their dispersion in the PE melt prior to crystallization. In this renewal proposal, we will develop the fundamental, quantitative understanding that will allow us to independently tailor polymer crystallization rate, NP diffusivity and NP agglomeration state in semicrystalline polymers so as to facilely control NP ordering and hence properties. A program that tightly integrates experiment and theory is proposed, and a key outcome of this research will be a three-dimensional design map for different regimes of NP organization (and hence properties) that can be achieved by polymer crystallization. A second independent outcome is the role of directional solidification and how it competes with the rates of polymer crystallization and NP mobility to affect the organization of the NP.