NASA NTRS1995

Thermal spray processing

Thermal spray processing has been used for a number of years to cost-effecticely apply TBC's for a wide range of heat engine applications. In particular, bond coats are applied by plasma spray and HVOF techniques and partially-stabilized zirconia top coats are applied by plasma spray methods. Thermal spray involves melting and rapid transport of the molten particles to the substrate, where high-rate solidification and coating build-up occur. It is the very nature of this melt processing that leads to the unique layered microstructure, as well as the apparent imperfections, so readily identified with thermal spray. Modeling the process, process-induced residual stresses, and thermal conductivity will be discussed in light of a new understanding of porosity and its anisotropy. Microcracking can be understood using new approaches, allowing a fuller view of the processing-performance connection. Detailed electron microscopic, novel neutron diffraction and fracture analysis of the deposits can lead to a better understanding of how overall microstructure can be controlled to influence critical properties of the deposited TBC system.

Herman, H.↗
NASA NTRS1986

Fracture toughness tests on plasma-sprayed coatings

Fracture toughness measurements have been performed on plasma-sprayed coatings. The intrinsic fracture toughness of plasma-sprayed coatings may be ascertained by means of a double cantilever beam (DCB) test. Emphasis is placed on calibration of the specimen geometry. Representative values for alumina coatings are presented.

Berndt, C. C.↗
NASA NTRS1986

Tensile adhesion test measurements on plasma-sprayed coatings

Adhesion measurements on plasma-sprayed coatings are briefly studied, including a critical analysis of the experimental scatter for duplicate tests. The application of a simple method which presents adhesion strength data in a fracture mechanics perspective is demonstrated. Available data are analyzed in a way which suggests an approach to finding the overall defect contribution to reducing the apparent strength of coatings.

Berndt, C. C.↗
NASA NTRS1984

Mechanical behavior of thermal barrier coatings for gas turbine blades

Plasma-sprayed thermal barrier coatings (TBCs) will enable turbine components to operate at higher temperatures and lower cooling gas flow rates; thereby improving their efficiency. Future developments are limited by precise knowledge of the material properties and failure mechanisms of the coating system. Details of this nature are needed for realistic modeling of the coating system which will, in turn, promote advancements in coating technology. Complementary experiments and analytical modeling which were undertaken in order to define and measure the important failure processes for plasma-sprayed coatings are presented. The experimental portion includes two different tests which were developed to measure coating properties. These are termed tensile adhesion and acoustic emission tests. The analytical modeling section details a finite element method which was used to calculate the stress distribution in the coating system. Some preliminary results are presented.

Berndt, C. C.↗
NASA NTRS1984

Mechanical property measurements of plasma-sprayed thermal-barrier coatings subjected to oxidation

Techniques have been developed for measuring the tensile properties of plasma-sprayed coatings which are used in thermal barrier applications. The measurements have included the average Young's modulus, bond strength and elongation at failure. The oxidation behavior of the bond coat plays an important role in the integrity and adhesion of plasma-sprayed thermal barrier coatings. This work studies the nature of the high temperature degradation on the mechanical properties of the coating. Furnace tests have been carried out on U-700 alloy with bond coats of NiCrAlY or NiCrAlZr and an overlay of ZrO2-8 percent Y2O3. Weight gain measurements on the coatings have been examined with relation to the adhesion strength and failure observations. The results from an initial study are reported in this work.

Berndt, C. C.↗
NASA NTRS1984

Acoustic emission evaluation of plasma-sprayed thermal barrier coatings

Acoustic emission techniques have recently been used in a number of studies to investigate the performance and failure behavior of plasma-sprayed thermal barrier coatings. Failure of the coating is a complex phenomena, especially when the composite nature of the coating is considered in the light of possible failure mechanisms. Thus it can be expected that both the metal and ceramic components (i.e., the bond coat and ceramic overlay) of a composite thermal protection system influence the macroscopic behavior and performance of the coating. The aim of the present work is to summarize the 'state-of-the-art' in terms of this initial work and indicate where future progress may be made.

Berndt, C. C.↗
NASA NTRS1984

Performance of thermal barrier coatings in high heat flux environments

Thermal barrier coatings were exposed to the high temperature and high heat flux produced by a 30 kW plasma torch. Analysis of the specimen heating rates indicates that the temperature drop across the thickness of the 0.038 cm ceramic layer was about 1100 C after 0.5 sec in the flame. An as-sprayed ZrO2-8%Y2O3 specimens survived 3000 of the 0.5 sec cycles with failing. Surface spalling was observed when 2.5 sec cycles were employed but this was attributed to uneven heating caused by surface roughness. This surface spalling was prevented by smoothing the surface with silicon carbide paper or by laser glazing. A coated specimen with no surface modification but which was heat treated in argon also did not surface spall. Heat treatment in air led to spalling in as early as 2 cycle from heating stresses. Failures at edges were investigated and shown to be a minor source of concern. Ceramic coatings formed from ZrO2-12%Y2O3 or ZrO2-20%Y2O3 were shown to be unsuited for use under the high heat flux conditions of this study.

Miller, R. A.↗
NASA NTRS1984

Failure analysis of plasma-sprayed thermal barrier coatings

Thermally induced failure processes of plasma-sprayed thermal barrier coatings are examined. Cracking processes give rise to noise which was monitored by acoustic emission (AE) techniques. The sequential failure of coatings was examined from samples which were thermally cycled. Coatings of yttria-stabilized zirconia with and without a NiCrAlZr bond coat were plasma-sprayed onto U700 alloy rod. In some cases the substrate was intentionally overheated during deposition of the thermal protection system to check how this process variable influenced the AE response of the specimen. In this way a qualitative appraisal of how process variables affect coating integrity could be discerned in terms of cracking behavior. Results from up to seven consecutive thermal cycles are reported here. Coating failure was observed in all cases. Failure of the thermal protection system is progressive, since cracking and crack growth were observed prior to ultimate failure. Thus castastrophic failure occurs at some stage when there is a transformation from the microcrack to a macrocrack network.

Berndt, C. C.↗
NASA NTRS1984

Performance of thermal barrier coatings in high heat flux environments

Thermal barrier coatings were exposed to the high temperature and high heat flux produced by a 30 kW plasma torch. Analysis of the specimen heating rates indicates that the temperature drop across the thickness of the 0.038 cm ceramic layer was about 1100 C after 0.5 sec in the flame. An as-sprayed ZrO2-8 percent Y2O3 specimens survived 3000 of the 0.5 sec cycles with falling. Surface spalling was observed when 2.5 sec cycles were employed but this was attributed to uneven heating caused by surface roughness. This surface spalling was prevented by smoothing the surface with silicon carbide paper or by laser glazing. A coated specimen with no surface modification but which was heat treated in argon also did not surface spall. Heat treatment in air led to spalling in as early as 1 cycle from heating stresses. Failures at edges were investigated and shown to be a minor source of concern. Ceramic coatings formed from ZrO2-12 percent Y2O3 or ZrO2-2O percent Y2O3 were shown to be unsuited for use under the high heat flux conditions of this study.

Miller, R. A.↗
NASA NTRS1984

Neutron and X-ray diffraction of plasma-sprayed zirconia-yttria thermal barrier coatings

ZrO2-7.8mol. pct. YO1.5, a fused powder, and ZrO2-8.7mol. pct. YO1.5, a prereacted powder, were plasma-sprayed onto steel substrates. Neutron diffraction and X-ray diffraction of the as-received powder, the powder plasma sprayed into water, as-sprayed coatings, and coatings heat-treated for 10 and 100 h were carried out to study phase transformations and ordering of the oxygen ions on the oxygen sublattice. The as-received fused powder has a much lower monoclinic percentage than does the pre-reacted powder, this resulting in a much lower monoclinic percentage in the coating. Heat treatment increases the percentages of the cubic and monoclinic phases, while decreasing the tetragonal content. An ordered tetragonal phase is detected by the presence of extra neutron diffraction peaks. These phase transformations and ordering will result in volume changes. The implications of these transformations on the performance of partially stabilized zirconia thermal barrier coatings is discussed.

Shankar, N. R.↗
NASA NTRS1984

Failure analysis of plasma-sprayed thermal barrier coatings

Thermally induced failure processes of plasma-sprayed thermal barrier coatings are examined. Cracking processes give rise to noise which was monitored by acoustic emission (AE) techniques. The sequential failure of coatings was examined from samples which were thermally cycled. Coatings of yttria-stabilized zirconia with and without a NiCrAlZr bond coat were plasma-sprayed onto U700 alloy rod. In some cases the substrate was intentionally overheated during deposition of the thermal protection system to check how this process variable influenced the AE response of the specimen. In this way a qualitative appraisal of how process variables affect coating integrity could be discerned in terms of cracking behavior. Results from up to seven consecutive thermal cycles are reported here. Coating failure was observed in all cases. Failure of the thermal protection system is progressive, since cracking and crack growth were observed prior to ultimate failure. Thus castastrophic failure occurs at some stage when there is a transformation from the microcrack to a macrocrack network.

Berndt, C. C.↗
NASA NTRS1984

Performance of thermal barrier coatings in high heat flux environments

Thermal barrier coatings were exposed to the high temperature and high heat flux produced by a 30 kW plasma torch. Analysis of the specimen heating rates indicates that the temperature drop across the thickness of the 0.038 cm ceramic layer was about 1100 C after 0.5 sec in the flame. An as-sprayed ZrO2-8 percent Y203 specimens survived 3000 of the 0.5 sec cycles with failing. Surface spalling was observed when 2.5 sec cycles were employed but this was attributed to uneven heating caused by surface roughness. This surface spalling was prevented by smoothing the surface with silicon carbide paper or by laser glazing. A coated specimen with no surface modification but which was heat treated in argon also did not surface spall. Heat treatment in air led to spalling in as early as 2 cycle from heating stresses. Failures at edges were investigated and shown to be a minor source of concern. Ceramic coatings formed from ZrO2-12 percent Y2O3 or ZrO2-20 percent Y2O3 were shown to be unsuited for use under the high heat flux conditions of this study.

Miller, R. A.↗
NASA NTRS1983

Phase analysis of plasma-sprayed zirconia-yttria coatings

Phase analysis of plasma-sprayed 8 wt pct-yttria-stabilized zirconia (YSZ) thermal barrier coatings and powders was carried out by X-ray diffraction. Step scanning was used for increased peak resolution. Plasma spraying of the YSZ powder into water or onto a steel substrate to form a coating reduced the cubic and monoclinic phases with a simultaneous increase in the tetragonal phase. Heat treatment of the coating at 1150 C for 10 h in an Ar atmosphere increased the amount of cubic and monoclinic phases. The implications of these transformations on coating performance and integrity are discussed.

Shankar, N. R.↗
NASA NTRS1983

Anisotropic thermal expansion effects in plasma-sprayed ZrO2-8 percent Y2O3 coatings

The thermal expansion properties of plasma-sprayed ZrO2-8-wt pct Y2O3 coatings, detached from the substrate, have been examined. Coatings were heat-treated in air or in argon. Anisotropic effects in the longitudinal (planar to the substrate surface) and transverse (perpendicular to the substrate surface) directions were measured and related to the coating structure. The thermal expansion coefficient of the coating is discussed in terms of the material's properties, such as the crack network and interlamellar boundary distribution. A precise model for the expansion behavior of coatings still needs attention, since no description of all of the contributing variables exists. A quantitative analysis of thermal properties of coatings will aid in future design and modeling of coating systems.

Berndt, C. C.↗
NASA NTRS1983

Failure during thermal cycling of plasma-sprayed thermal barrier coatings

The thermal cycling behavior of plasma-sprayed ZrO2-12 wt pct Y2O3 coatings was studied. Coatings were produced with and without bond coats of Ni-Cr-Al-Zr and in some cases the substrates were heated to above the optimum temperature prior to spraying. The coatings (attached to the substrate) were thermal cycled to 1200 C and their cracking behavior was followed by acoustic emission (AE) techniques. It was possible to examine the failure mechanisms by statistical analysis of the AE data and to evaluate the influence of preheating and bond coating. It is shown that the AE spectrum changes when a bond coat is used because of the presence of microcracks which, in turn, dissipate energy and improve the coating integrity. The preheating effect is reflected by a decrease in the peak count rate and an increase in the temperature at which AE activity is initiated.

Berndt, C. C.↗