NASA NTRS1990

Tensile adhesion testing methodology for thermally sprayed coatings

The structure of thermally sprayed coatings consists of lamellae which are oriented parallel to the substrate surface. The lamellae separate and fracture by distinctive mechanisms which are reflected in the failure morphology, and these may be described as adhesive (between the coating and substrate), cohesive (within the coating), or mixed mode. There is a large variability in the failure stress for any nominally identical group of coatings. A lower bound for the fracture toughness of alumina coatings can be calculated as 0.2 MNm exp -3/2. The coating strength values may also be treated as belonging to the statistical distribution of the Weibull function. The Weibull modulus of the coating strength varied from 1.4 to 3.8. This analysis infers that the flaw size within coatings is highly variable and that the flaws are nonuniformly dispersed. The present work focuses on the question of whether tensile adhesion tests are an appropriate testing method for thermally sprayed materials.

Berndt, Christopher C.↗

NASA NTRS1989

Instrumented adhesion tests on plasma sprayed thermal barrier coatings

The failure mechanisms of plasma-sprayed two-layer coatings consisting of an NiCrAlY or NiCrAlZr bond coat with an yttria-stabilized zirconia overlay are presently examined by tensile adhesion tests. It has been found that adhesive failure within the bond coat exhibits greater failure strain than the cohesive failure of the ceramic overlay, supporting the view of the intermediate coatings being highly compliant. The absolute extension exhibited by failures occurring only through the ceramic coating is greater than that of adhesive failure, since the ceramic coating is much thicker than the bond coat.

Berndt, Christopher C.↗

NASA NTRS1985

Examination of coating failure by acoustic emission

Coatings of NiCrAlY bond coat with a zirconia - 12 wt percent yttria overlay were applied to disc-shaped specimens of U-700 alloy. A waveguide of 1 mm diameter platinum was TIG welded to the specimen and allowed it to be suspended in a tubular furnace. The specimen was thermally cycled to 1150 C, and the acoustic emission (AE) monitored. The weight gain per thermal cycle was also measured. A computer system based on the IBM-XT microcomputer was used extensively to acquire the AE data with respect to temperature. This system also controlled the temperature by using a PD software loop. Several different types of AE analyses were performed. A major feature of these tests, not addressed by previous work in this area, was that the coatings covered 100 percent of the specimen and also that the AE was amplified at two different levels. It is believed that this latter feature allows a qualitative appraisal of the relative number of cracks per AE event. The difference in AE counts between the two channels is proportional to the number of cracks per AE event, and this parameter may be thought of as the crack density. The ratio of the AE count difference to the AE count magnitude of one channel is inversely proportional to the crack growth. Both of these parameters allow the crack distribution and crack growth within each specimen to be qualitatively followed during the thermal cycling operation. Recent results which used these principles will be presented.

Berndt, Christopher C.↗

NASA NTRS1984

Behavior of plasma-sprayed coatings

The microstructural development of plasma sprayed oxide coatings is described with particualr reference to aluminum oxide coatings and thermal barrier coatings of yttria stabilized zirconia (YSZ). The microstructural features of these coatings, observed by optical and electron microscopy, are related to their mechanical behavior. The adhesion of the coatings is also investigated using fracture toughness and tensile tests. It is noted that acoustic emission is valuable in formulating possible fracture mechanisms for YSZ coatings.

Berndt, Christopher C.↗