Bernstein, Edward L.

Publications and source records attributed to Bernstein, Edward L..

3 records

NASA NTRS1999

Flow Trajectories in Friction Stir Welding

In the Friction Stir Welding (FSW) process, a rotating, shouldered tool with a threaded pin is inserted under pressure along the seam of two pieces of metal which are tightly clamped together, and secured against a rigid anvil underneath. The rotating pin travels along the seam and through a combination of pressure and friction heating produces a zone of plastic deformation around the pin within the workpiece on either side of the seam. As the pin is moved in the direction of welding, the plasticised material moves around the tool and bonds together behind it. The elements of the material flow behavior are a combination of three elements. There is a rotational transport of material being carried around the tool, extrusion of material being forced around the pin on both sides into the cavity created behind it, and a lifting and dropping of material as it is stirred and mixed by the rotating action of the pin. It was assumed that rotational motion of the plastic zone is the primary mechanism for transport of material around the welding tool. A kinematic mathematical model was used to compute trajectories of material movement for various distributions of rotational slip within the plastic zone. These trajectories were then compared with the results of an experiment that produced radiographs of markers embedded in a workpiece that was welded with the FSW process. It was assumed that the copper wire markers retained their original length as the aluminum material flowed around them. The kinematic model included a constraint so that the displacements were such that the total length of the wire markers did not increase after deformation. There was good agreement between the calculated trajectories for the case of localized slip at the outer surface of the plastic deformation zone and the radiographs of the copper wire markers. The trajectories differed markedly from the radiograph traces when a distributed slip zone was assumed. It was concluded that the flow field could be described generally by a rotating plug model with slip occurring on the surface at the outer boundary of the plastic zone.

Bernstein, Edward L.↗

NASA NTRS1996

Modeling aluminum-lithium alloy welding characteristics

The purpose of this project was to develop a finite element model of the heat-affected zone in the vicinity of a weld line on a plate in order to determine an accurate plastic strain history. The resulting plastic strain increments calculated by the finite element program were then to be used to calculate the measure of damage D. It was hoped to determine the effects of varying welding parameters, such as beam power, efficiency, and weld speed, and the effect of different material properties on the occurrence of microfissuring. The results were to be compared first to the previous analysis of Inconel 718, and then extended to aluminum 2195.

Bernstein, Edward L.↗

NASA NTRS1994

Residual stresses in welded plates

The purpose of this project was to develop a simple model which could be used to study residual stress. The mechanism that results in residual stresses in the welding process starts with the deposition of molten weld metal which heats the immediately adjacent material. After solidification of weld material, normal thermal shrinkage is resisted by the adjacent, cooler material. When the thermal strain exceeds the elastic strain corresponding to the yield point stress, the stress level is limited by this value, which decreases with increasing temperature. Cooling then causes elastic unloading which is restrained by the adjoining material. Permanent plastic strain occurs, and tension is caused in the region immediately adjacent to the weld material. Compression arises in the metal farther from the weld in order to maintain overall static equilibrium. Subsequent repair welds may add to the level of residual stresses. The level of residual stress is related to the onset of fracture during welding. Thus, it is of great importance to be able to predict the level of residual stresses remaining after a weld procedure, and to determine the factors, such as weld speed, temperature, direction, and number of passes, which may affect the magnitude of remaining residual stress. It was hoped to use traditional analytical modeling techniques so that it would be easier to comprehend the effect of these variables on the resulting stress. This approach was chosen in place of finite element methods so as to facilitate the understanding of the physical processes. The accuracy of the results was checked with some existing experimental studies giving residual stress levels found from x-ray diffraction measurements.

Bernstein, Edward L.↗