Engineering topics

Bhatt, R. T.

Publications and source records attributed to Bhatt, R. T..

At least 37 records · Page 2

NASA NTRS1995

Heat Treatment Effects on the Tensile Properties and Microstructures of a SiC/RBSN Composite in Nitrogen

The room-temperature tensile properties and constituent microstructures of a unidirectionally reinforced SiC/reaction bonded silicon nitride (RBSN) composite have been investigated after heat treatments at 1400, 1600, or 1800 C in nitrogen for up to 100 hr. The composite consisted of approximately 24 vol% of aligned 140 micron diameter, continuous length, chemically vapor deposited SiC fibers in an approximately 40% porous silicon nitride matrix. The composites heat treated at 1400 C for up to 100 hr showed elastic modulus, first matrix cracking strength, and ultimate tensile strength values similar to those of the as-fabricated composites, but those heat treated for 1 hr beyond this temperature displayed losses in all three properties. Recrystallization of the SiC fibers, reaction between the carbon-rich interface coating on the fibers and the RBSN matrix, and dissociation of the RBSN matrix are the reasons for the loss of mechanical properties.

Bhatt, R. T.↗

NASA NTRS1995

Thermal Stability of Hi-Nicalon SiC Fiber in Nitrogen and Silicon Environments

The room temperature tensile strength of uncoated and two types of pyrolytic boron nitride coated (PBN and Si-rich PBN) Hi-Nicalon SiC fibers was determined after 1 to 400 hr heat treatments to 1800 C under N2 pressures of 0.1, 2, and 4 MPa, and under 0.1 Mpa argon and vacuum environments. In addition, strength stability of both uncoated and coated fibers embedded in silicon powder and exposed to 0.1 MPa N2 for 24 hrs at temperatures to 1400 C was investigated. The uncoated and both types of BN coated fibers exposed to N2 for 1 hr showed noticeable strength degradation above 1400 C and 1600 C, respectively. The strength degradation appeared independent of nitrogen pressure, time of heat treatment, and surface coatings. TEM microstructural analysis suggests that flaws created due to SiC grain growth are responsible for the strength degradation. In contact with silicon powder, the uncoated and both types of PBN coated fibers degrade rapidly above 1350 C.

Bhatt, R. T.↗

NASA NTRS1994

Effects of Thermal Cycling on Thermal Expansion and Mechanical Properties of Sic Fiber-reinforced Reaction-bonded Si3n4 Composites

Thermal expansion curves for SiC fiber-reinforced reaction-bonded Si3N4 matrix composites (SiC/RBSN) and unreinforced RBSN were measured from 25 to 1400 C in nitrogen and in oxygen. The effects of fiber/matrix bonding and cycling on the thermal expansion curves and room-temperature tensile properties of unidirectional composites were determined. The measured thermal expansion curves were compared with those predicted from composite theory. Predicted thermal expansion curves parallel to the fiber direction for both bonding cases were similar to that of the weakly bonded composites, but those normal to the fiber direction for both bonding cases resulted in no net dimensional changes at room temperature, and no loss in tensile properties from the as-fabricated condition. In contrast, thermal cycling in oxygen for both composites caused volume expansion primarily due to internal oxidation of RBSN. Cyclic oxidation affected the mechanical properties of the weakly bonded SiC/RBSN composites the most, resulting in loss of strain capability beyond matrix fracture and catastrophic, brittle fracture. Increased bonding between the SiC fiber and RBSN matrix due to oxidation of the carbon-rich fiber surface coating and an altered residual stress pattern in the composite due to internal oxidation of the matrix are the main reasons for the poor mechanical performance of these composites.

Bhatt, R. T.↗

NASA NTRS1992

Effect of HIPing on the effective thermal conductivity/diffusivity and the interfacial thermal conductance of uniaxial SiC fibre-reinforced RBSN

Hot isostatic pressing (HIPing) was found to increase the thermal diffusivity/conductivity of uniaxial silicon carbide fiber-reinforced reaction-bonded silicon nitride (RBSN) matrix composites, as the result of the densification of the matrix, the increase in the grain size of the silicon carbide and the improved thermal contact between the fibers and the matrix. Transverse to the fiber direction the thermal diffusivity/conductivity was found to be a function of the surrounding gaseous atmosphere due to the access of the gas phase to the fiber-matrix interface, which was facilitated by the existence of an interfacial gap due to the thermal expansion mismatch between the fibers and the matrix. The interfacial conductance was found to exhibit a strong positive temperature dependence as the result of the closure of the interfacial gap with increasing temperature.

Bhatt, H.↗

NASA NTRS1992

Role of interfacial thermal barrier in the transverse thermal conductivity of uniaxial SiC fiber-reinforced reaction bonded silicon nitride

The transverse thermal conductivity of reaction-bonded Si3N4 is significantly affected by an interfacial barrier at the interface formed with SiC reinforcing fibers. A comparative study of composites with and without reinforcing-fiber carbon coatings found the coating to reduce effective thermal conductivity by a factor of about 2; this, however, is partially due to a thermal expansion-mismatch gap between fiber and matrix. HIPing of composites with coated fibers led to an enhancement of thermal conductivity via improved interfacial thermal contact and greater grain size and crystallinity of the fibers.

Bhatt, H.↗

NASA NTRS1992

Effect of high temperature annealing on the microstructure of SCS-6 SiC fibers

The effect of annealing the SCS-6 SiC fiber for one hour at 2000 C in an argon atmosphere is reported. The SiC grains in the fiber coarsen appreciably and the intergranular carbon films segregate to the grain junctions. It would appear that grain growth in the outer part of the fiber is primarily responsible for the loss in fiber strength and improvement in fiber creep resistance.

Ning, X. J.↗

NASA NTRS1991

Ultrasonic velocity technique for monitoring property changes in fiber-reinforced ceramic matrix composites

A technique for measuring ultrasonic velocity was used to monitor changes that occur during processing and heat treatment of a SiC/RBSM composite. Results indicated that correlations exist between the ultrasonic velocity data and elastic modulus and interfacial shear strength data determined from mechanical tests. The ultrasonic velocity data can differentiate strength. The advantages and potential of this nondestructive evaluation method for fiber reinfoced ceramic matrix composite applications are discussed.

Kautz, H. E.↗

NASA NTRS1991

Investigation of interfacial shear strength in SiC/Si3N4 composites

A fiber push-out technique was used to determine fiber/matrix interfacial shear strength (ISS) for silicon carbide fiber reinforced reaction-bonded silicon nitride (SiC/RBSN) composites in the as-fabricated condition and after consolidation by hot isostatic pressing (HIPing). In situ video microscopy and acoustic emission detection greatly aided the interpretation of push-out load/displacement curves.

Eldridge, J. I.↗

NASA NTRS1991

Investigation of interfacial shear strength in SiC/Si3N4 composites

Eldridge, J. I.↗

NASA NTRS1990

Mechanical Properties Of SiC/Si3N4 Laminates

Two reports describe tests to determine mechanical properties of laminates made of reaction-bonded silicon nitride matrices reinforced with 30 volume percent of aligned silicon carbide fibers. Emphasizes different aspects of topic. One focuses on behavior related to strength at ambient temperature; other focuses on strength after exposure to high temperatures. Overall, results indicate that composites are candidates for use at high temperatures; for example, as components of heat engines.

Bhatt, R. T.↗

NASA NTRS1990

Thermal effects on the mechanical properties of SiC fibre reinforced reaction-bonded silicon nitride matrix composites

The elevated temperature four-point flexural strength and the room temperature tensile and flexural strength properties after thermal shock were measured for ceramic composites consisting of 30 vol pct uniaxially aligned 142 micron diameter SiC fibers in a reaction bonded Si3N4 matrix. The elevated temperature strengths were measured after 15 min of exposure in air at temperatures to 1400 C. Thermal shock treatment was accomplished by heating the composite in air for 15 min at temperatures to 1200 C and then quenching in water at 25 C. The results indicate no significant loss in strength properties either at temperature or after thermal shock when compared with the strength data for composites in the as-fabricated condition.

Bhatt, R. T.↗

NASA NTRS1990

Role of the interfacial thermal barrier in the effective thermal diffusivity/conductivity of SiC-fiber-reinforced reaction-bonded silicon nitride

Experimental thermal diffusivity data transverse to the fiber direction for composites composed of a reaction bonded silicon nitride matrix reinforced with uniaxially aligned carbon-coated silicon carbide fibers indicate the existence of a significant thermal barrier at the matrix-fiber interface. Calculations of the interfacial thermal conductances indicate that at 300 C and 1-atm N2, more than 90 percent of the heat conduction across the interface occurs by gaseous conduction. Good agreement is obtained between thermal conductance values for the oxidized composite at 1 atm calculated from the thermal conductivity of the N2 gas and those inferred from the data for the effective composite thermal conductivity.

Bhatt, Hemanshu↗

NASA NTRS1988

Thermal effects on the mechanical properties of SiC fiber reinforced reaction bonded silicon nitride matrix (SiC/RBSN) composites

Bhatt, R. T.↗

NASA NTRS1987

Making a Silicon-Nitride/Silicon-Carbide Composite

Hot pressing and nitriding produce strong fiber/matrix material. Fabrication method developed for processing strong and tough silicon-based ceramic composite material, SiC/RBSN, which consists of reaction-bonded Si3N4 (RBSN) reinforced by continuous-length, high-modulus, high strength silicon carbide (SiC) fibers prepared by chemical-vapor deposition method. Increased toughness and ultimate strength of SiC/RBSN composite makes it potential structural material for advanced heat engines.

Bhatt, R. T.↗

NASA NTRS1985

Environmental effects on the tensile strength of chemically vapor deposited silicon carbide fibers

The room temperature and elevated temperature tensile strengths of commercially available chemically vapor-deposited (CVD) silicon carbide fibers were measured after 15 min heat treatment to 1600 C in various environments. These environments included oxygen, air, argon and nitrogen at one atmosphere and vacuum at 10/9 atmosphere. Two types of fibers were examined which differed in the SiC content of their carbon-rich coatings. Threshold temperature for fiber strength degradation was observed to be dependent on the as-received fiber-flaw structure, on the environment and on the coating. Fractographic analyses and flexural strength measurements indicate that tensile strength losses were caused by surface degradation. Oxidation of the surface coating is suggested as one possible degradation mechanism. The SiC fibers containing the higher percentage of SiC near the surface of the carbon-rich coating show better strength retention and higher elevated temperature strength.

Bhatt, R. T.↗

NASA NTRS1985

Mechanical properties of SiC fiber-reinforced reaction-bonded Si3N4 composites

The room temperature mechanical and physical properties of silicon carbide fiber reinforced reaction-bonded silicon nitride composites (SiC/RBSN) have been evaluated. The composites contained 23 and 40 volume fraction of aligned 140 micro m diameter chemically vapor deposited SiC fibers. Preliminary results for composite tensile and bend strengths and fracture strain indicate that the composites displayed excellent properties when compared with unreinforced RBSN of comparable porosity. Fiber volume fraction showed little influence on matrix first cracking strain but did influence the stressed required for matrix first cracking and for ultimate composite fracture strength. It is suggested that by reducing matrix porosity and by increasing the volume fraction of the large diameter SiC fiber, it should be possible to further improve the composite stress at which the matrix first cracks.

Bhatt, R. T.↗

NASA NTRS1982

Fatigue behavior of SiC reinforced Ti/6Al-4V/ at 650 C

Axial, low cycle fatigue properties of 25 and 44 fiber vol pct SiC/Ti(6Al-4V) composites, measured at 650 C, were compared with the fatigue properties of unreinforced Ti(6Al-4V) at the same temperature. A prior study of the fatigue behavior of this composite system at room temperature indicated that the SiC fiber reinforcement did not provide the anticipated improvement of fatigue resistance of this alloy. At 650 C, the composite fatigue properties degraded somewhat from those at room temperature. However, these properties degraded more for the unreinforced matrix at 650 C with the result that the composite fatigue strength was two to three times the fatigue strength of the matrix alloy. The reasons for this reversal are discussed in terms of crack initiation at broken fibers and residual matrix stresses.

Bhatt, R. T.↗

NASA NTRS1982

Thermal degradation of the tensile properties of undirectionally reinforced FP-AI203/EZ 33 magnesium composites

The effects of isothermal and cyclic exposure on the room temperature axial and transverse tensile strength and dynamic flexural modulus of 35 volume percent and 55 volume percent FP-Al2O3/EZ 33 magnesium composites were studied. The composite specimens were continuously heated in a sand bath maintained at 350 C for up to 150 hours or thermally cycled between 50 and 250 C or 50 and 350 C for up to 3000 cycles. Each thermal cycle lasted for a total of six minutes with a hold time of two minutes at the maximum temperature. Results indicate to significant loss in the room temperature axial tensile strength and dynamic flexural modulus of composites thermally cycled between 50 and 250 C or of composites isothermally heated at 350 C for up to 150 hours from the strength and modulus data for the untreated, as fabricated composites. In contrast, thermal cycling between 50 and 350 C caused considerable loss in both room temperature strength and modulus. Fractographic analysis and measurement of composite transverse strength and matrix hardness of thermally cycled and isothermally heated composites indicated matrix softening and fiber/matrix debonding due to void growth at the interface and matrix cracking as the likely causes of the strength and modulus loss behavior.

Bhatt, R. T.↗