Ammonia-fed reversible protonic ceramic fuel cells with Ru-based catalyst

Abstract The intermediate operating temperatures (~400–600 °C) of reversible protonic ceramic fuel cells (RePCFC) permit the potential use of ammonia as a carbon-neutral high energy density fuel and energy storage medium. Here we show fabrication of anode-supported RePCFC with an ultra-dense (~100%) and thin (4 μm) protonic ceramic electrolyte layer. When coupled to a novel Ru-(BaO) 2 (CaO)(Al 2 O 3 ) (Ru-B2CA) reversible ammonia catalyst, maximum fuel-cell power generation reaches 877 mW cm −2 at 650 °C under ammonia fuel. We report relatively stable operation at 600 °C for up to 1250 h under ammonia fuel. In fuel production mode, ammonia rates exceed 1.2 × 10 −8 NH 3 mol cm −2 s −1 at ambient pressure with H 2 from electrolysis only, and 2.1 × 10 −6 mol NH 3 cm −2 s −1 at 12.5 bar with H 2 from both electrolysis and simulated recycling gas.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2020

An all-oxide electrolysis cells for syngas production with tunable H 2 /CO yield via co-electrolysis of H 2 O and CO 2

High-rate production of syngas with tunable H 2 /CO and coke-free operation is achieved in a solid-oxide electrolysis cell (SOEC). Prior to operation, controlled pre-reduction of La 0.7 Sr 0.3 Fe 0.9 Ni 0.1 O 3-δ (LSFNi) cathode is used to trigger the in-situ exsolution of Ni-Fe alloy nanoparticles with an average size of ~45 nm uniformly distributed and socketed on LSFNi backbone, enabling efficient co-electrolysis of H 2 O and CO 2 to H 2 and CO. At 1.5 V, the current density reaches ~1.0 A cm-2 at 750 °C and ~2.4 A cm -2 at 850 °C with near 100% Faradaic Efficiency. We demonstrate the feasibility of tuning the output H 2 /CO ratio by nearly two orders of magnitude (from ~0.1 to ~7) by manipulating H 2 O/CO 2 ratio of feed gas, operating temperature, and current density. Finally, stable operation for >100 h is obtained without evidence of carbon deposition, although high current density operation leads to observable deterioration of anode/electrolyte interface due to the rapid oxygen evolution.

25 ENERGY STORAGE↗