Engineering topics
Bieler, T. R.
Publications and source records attributed to Bieler, T. R..
The Influence of Strain Path and Heat Treatment Variations on Recrystallization in Cold-Rolled High-Purity Niobium Polycrystals
With the standard material and cavity production guidelines, the properties and performance of industrially produced high-purity niobium superconducting radiofrequency (SRF) cavities are unpredictably variable. Currently, assembled niobium SRF cavities undergo post-purification vacuum heat treatment at 800 °C for three hours to remove hydrogen and increase performance; however, recent work has shown significant improvements in cavity performance when annealed between 900–1000 °C, causing recrystallization (Rx). Increasing the annealing temperature and/or the heating rate should facilitate the onset of Rx, resulting in a greater reduction in the density of geometrically necessary dislocations (GNDs) that are strongly associated with the degradation of cavity performance via trapped magnetic flux. Improving the SRF community's understanding of the influence of both heat treatment and deformation history on the resulting microstructure and Rx behavior in high-purity niobium is needed. This fundamental metallurgy is critical for identifying improved specifications for the consistent production of high-performing niobium SRF cavities. This research investigates variations in deformation paths, heating rates, and annealing temperatures on Rx of deformed samples of polycrystalline high-purity niobium. To assess the effects of strain path, samples were cold-rolled to ~30% reduction prior to annealing, with half of the sample set rolled parallel to the as-received niobium sheet and the other half in the transverse direction.
On the correlation between plastic strain and misorientation in polycrystalline body-centered-cubic microstructures with an emphasis on the grain size, loading history, and crystallographic orientation
In this work, the correlation between plastic strain and crystallographic misorientation, grain size, grain orientation, distance from grain boundary, and loading history were investigated experimentally and numerically for body-centered-cubic (BCC) polycrystalline microstructures based on a misorientation deviation (MD) approach. Nine monotonic tensile experiments were performed on two BCC titanium alloys inside a scanning electron microscope (SEM). The influence of reference orientation was explored both at the grain scale and at the mesoscale using electron backscattered diffraction (EBSD). The correlation between global plastic strain and the MD was quantified. The tendency for orientation change was quantified as a function of plastic strain and grain orientation for three crystallographic orientations (i.e., [100], [110], and [111]) with respect to tensile direction. The subpopulation of small grains exhibited a lower level of misorientation dispersion compared with larger grains, and this discrepancy became more pronounced at higher strains. An empirical equation was proposed to estimate the level of misorientation dispersion for individual grains as a function of grain size and global plastic strain level. Two interrupted in-situ SEM experiments were performed, and this resulted in a significantly increased misorientation compared with uninterrupted tests performed to similar plastic strain levels.
Effect of strain rate on tensile mechanical properties of high-purity niobium single crystals for SRF applications
Not Available
Possible role of grain-boundary and dislocation structure for the magnetic-flux trapping behavior of niobium: A first-principles study
In this work, first-principles methods were used to understand magnetic flux trapping at vacancies, dislocations, and grain boundaries in high-purity superconducting niobium. Full-potential linear augmented plane-wave methods were applied in progressively greater complexity, starting at simple vacancies and extending to screw dislocations and tilt grain boundaries to analyze the effects of magnetic field on the superconducting state surrounding these defects. Density-functional theory calculations identified changes in electronic structure at the dislocation core and different types of symmetric tilt grain boundaries relative to bulk niobium. Electron redistribution enhanced nonparamagnetic effects and thus perturb superconductivity, resulting in local conditions suitable for premature flux penetration and subsequently flux pinning. Since the coherence length of superconducting niobium at 0 K is significantly larger than the lattice parameter, the effects of line and planar defects in niobium are predicted to be stronger for defect clusters than single defects in isolation, which is consistent with recent experimental observations. Controlling accumulation or depletion of charge at the defects, e.g., by segregation of an impurity atom, can mitigate these tendencies thus increasing the quality of superconducting niobium.