Structural, magnetic, and electronic evolution of the spin-ladder system BaFe 2 S 3-x Se x with isoelectronic substitution
We reWe report experimental studies of a series of BaF e 2 S 3 - x Se x ( 0 ≤ $x$ ≤ 3 ) single crystals and powder specimens using x-ray diffraction, neutron-diffraction, muon-spin-relaxation, and electrical transport measurements. A structural transformation from $C$ $mcm$ ( BaFe 2 Se 3 ) to $P$ $nma$ ( BaFe 2 Se 3 ) was identified around $x$ = 0.7 - 1 . Neutron-diffraction measurements on the samples with $x$ = 0.2, 0.4, and 0.7 reveal that the Néel temperature of the stripe antiferromagnetic order is gradually suppressed from ~120 to 85 K, while the magnitude of the ordered Fe 2+ moments shows very little variation. Similarly, the block antiferromagnetic order in BaFe 2 Se 3 remains robust for 1.5 ≤ $x$ ≤ 3 with negligible variation in the ordered moment and a slight decrease of the Néel temperature from 250 K ( $x$ = 3 ) to 225 K ( $x$ = 1.5 ). The sample with $x$ = 1 near the $C$ $mcm$ and $P$ $nma$ border shows coexisting, two-dimensional, short-range stripe- and block-type antiferromagnetic correlations. The system remains insulating for all $x$ , but the thermal activation gap shows an abrupt increase when traversing the boundary from the $C$ $mcm$ stripe phase to the $P$ $nma$ block phase. The results demonstrate that the crystal structure, magnetic order, and electronic properties are strongly coupled in the BaFe 2 S 3-x Se x system.